First-principles density functional theory (DFT) is employed to study the electronic structure of oxygen and gallium vacancies in monoclinic bulk β-Ga₂O₃ crystals. Hybrid exchange–correlation functional B3LYP within the density functional theory and supercell approach were successfully used to simulate isolated point defects in β-Ga₂O₃. Based on the results of our calculations, we predict that an oxygen vacancy in β-Ga₂O₃ is a deep donor defect which cannot be an effective source of electrons and, thus, is not responsible for n-type conductivity in β-Ga₂O₃. On the other hand, all types of charge states of gallium vacancies are sufficiently deep acceptors with transition levels more than 1.5 eV above the valence band of the crystal. Due to high formation energy of above 10 eV, they cannot be considered as a source of p-type conductivity in β-Ga₂O₃.

Zinc gallate (ZnGa₂O₄) spinel ceramics doped with Mn²⁺ ions was prepared by a solid-state reaction at 1200 °C in air. Manganese concentration was equal to 0.05 mol.% of MnO with respect to ZnO. Ceramics produced in this way show an efficient green emission at about 505 nm under UV or X-ray excitations, which is caused by Mn²⁺ ions. This green emission is observed also as a relatively long afterglow (visible to the naked eye in the dark for about one hour) after switching-off the X-ray excitation. Time profiles of the beginning of glow and afterglow have been studied together with thermally stimulated (TSL) and optically stimulated (OSL) luminescence. Experimental results demonstrate a presence of few types of shallow and deep traps responsible for the observed afterglow and TSL/OSL emission of the material. The possibility of pulsed optical stimulation and time-resolved OSL characteristics of ZnGa₂O₄: Mn²⁺ has been reported for the first time. The presented results suggest the ZnGa₂O₄: Mn²⁺ spinel as a promising material for further fundamental research and possibility of application as a green long-lasting phosphor or storage phosphor for TSL/OSL radiation dosimetry.