During lithium-ion battery packing, joining between battery cases and tabs is challenging for manufacturers due to dissimilar materials of the battery case and the tab, as well as their thicknesses. Laser welding, which has proven to produce a good weld with high productivity and low electrical resistance, is introduced to weld these materials. The weld was conducted with nanosecond-pulsed fiber laser and the effect of laser powers on mechanical and electrical properties as well as microstructure of the joint is investigated. The weld bead at the low laser power exhibited several blowholes on the surface, while the formation of voids including centerline and root cavities was observed through the cross-section. Moreover, the phenomenon of upward penetration (UP) was observed in all laser powers and recoil pressure which was generated by metal evaporation was supposed to cause the formation of an upward flow of the lower material. A hardness test was performed on both horizontal and vertical directions through the fusion zone. Additionally, the increase of upward penetration (UP) resulted in higher strength and lower electrical resistance of the weld.

Extensive experimental and computational studies have demonstrated outstanding physical and chemical properties of the novel materials of compositionally complex carbides (CCCs), enabling their promising applications in advanced fission and fusion energy systems. This perspective provides a comprehensive overview of radiation damage behavior reported in the literature to understand the fundamental mechanisms related to the impact of multi-principal metal components on phase stability, irradiation-induced defect clusters, irradiation hardening, and thermal conductivity of compositionally complex carbides. Several future research directions are recommended to critically evaluate the feasibility of designing and developing new ceramic materials for extreme environments using the transformative “multi-principal component” concept. Compared to the existing materials for nuclear applications including stainless steels, nickel alloys, ZrC, SiC, and potentially high-entropy alloys, as well as certain other compositionally complex ceramic families. CCCs appear to be more resistant to amorphization, growth of irradiation defect clusters, and void swelling.

Two advanced manufacturing processes, spark plasma sintering (SPS) and selective laser sintering (SLS), have been developed for synthesis of (Zr,Nb,Ta,Ti,W)C compositionally complex carbide (CCC) via reactive sintering of a powder mixture of constitute monocarbides. X‐ray diffraction analysis confirmed that the single‐phase CCC can be formed by both SPS and SLS. While a homogenous microstructure with uniform metal element distributions was developed during SPS, three‐layer microstructures with a thin TiC‐rich layer and two TaC‐rich layers along with a TiO ₂ ‐rich surface layer containing W nanoparticles were formed during SLS. In addition, cellular structures with W, Zr, and Ti element segregation and dislocations on cell boundaries were observed in the SLS‐CCC sample, indicating the effect of nonequilibrium conditions on microstructure formation during laser melting followed by rapid cooling and solidification process. Compared to the SPS‐CCC sample, the SLS‐CCC showed enhanced hardness and reduced thermal conductivity, which may be related to their unique cellular structures.

Given the drawbacks of the conventional welding methods in joining the battery case and tab in the lithium-ion battery, the laser welding technique using the metal tube has been introduced for the weld. The metal tube is supposed to contribute a positive effect including protection to the outside structure by blocking the injection of the spatters, and minimization of the contact gap between the battery case and table. However, the use of the metal tube is believed to cause the plume trapped inside and affect the intensity distribution of the laser gaussian beam. Through the observation and analysis in this study, both advantages and disadvantages of the application of the metal tube on the weld have been analyzed. The use of the metal tube prevents the ejection of the spatter to the outside of the welding zone, as well as minimize the air gap between the battery case and tab in the lap joint weld is also minimized. On the other hand, the trapped plume inside the metal tube and the reduction of the energy of the laser beam have been considered to cause significant changes in the morphology, mechanical, and electrical properties of the weld.

The nature of structural changes of nanosecond laser modification inside silicon is investigated. Raman spectroscopy and transmission electron microscopy measurements of cross sections of the modified channels reveal highly localized crystal deformation. Raman spectroscopy measurements prove the existence of amorphous silicon inside nanosecond laser induced modifications, and the percentage of amorphous silicon is calculated based on the Raman spectrum. For the first time, the high-resolution transmission electron microscopy images directly show the appearance of amorphous silicon inside nanosecond laser induced modifications, which corroborates the indirect measurements from Raman spectroscopy. The laser modified channel consists of a small amount of amorphous silicon embedded in a disturbed crystal structure accompanied by strain. This finding may explain the origin of the positive refractive index change associated with the written channels that may serve as optical waveguides.