This study investigates the detoxification properties of guanidinylated chitosan against chemical warfare agents and its application to the preparation of military protective clothing. Guanidinylated chitosan was synthesized by chitosan guanidinylation with cyanamide. The detoxification properties of the guanidinylated chitosan were then evaluated using a chemical warfare agent simulant, called diisopropylfluorophosphate (DFP). Cotton fabric was treated with 1 wt.% of guanidinylated chitosan in acetic acid and water solution using the simple and conventional textile treatment method of pad–dry–cure. The detoxification properties of the guanidinylated chitosan-treated cotton fabric were evaluated to investigate the application of guanidinylated chitosan to the preparation of military protective clothing. Subsequently, 71.3% of DFP was hydrolyzed to non-hazardous diisopropylhydrogenphosphate (DHP) in 2 h because of the base organocatalytic activity of 0.02 g guanidinylated chitosan itself. Moreover, 60.1% of DFP was hydrolyzed by the catalytic activity of the guanidinylated chitosan-treated cotton fabric, which contained only 0.0002 g of guanidinylated chitosan. This result shows that the guanidinylated chitosan itself has detoxification properties for hydrolyzing DFP to DHP, and its detoxification properties can be more efficient when applied to cotton fabric because it showed 84.3% of the detoxification properties with only 1 wt.% of guanidinylated chitosan. For the first time, this study shows that guanidinylated chitosan has considerable detoxification properties and can be used as an agent to prepare protective clothing.

This study aimed to investigate the effect of impregnation pressure on the decrease in porosity of impregnated bulk graphite. The correlation between pitch impregnation behavior and the pore sizes of the bulk graphite block was studied to determine the optimal impregnation pressure. The densities and porosities of the bulk graphite before and after pitch impregnation under various pressures between 10 and 50 bar were evaluated based on the Archimedes method and a mercury porosimeter. The density increased rates increased by 1.93–2.44%, whereas the impregnation rate calculated from the rate of open porosity decreased by 15.15–24.48%. The density increase rate and impregnation rate were significantly high when the impregnation pressures were 40 and 50 bar. Compared with impregnation pressures of 10, 20, and 30 bar, the minimum impregnatable pore sizes with impregnation pressures of 40 and 50 bar were 30–39 and 24–31 nm, respectively. The mercury intrusion porosimeter analysis results demonstrated that the pressure-sensitive pore sizes of the graphite blocks were in the range of 100–4500 nm. Furthermore, the ink-bottle-type pores in this range contributed predominantly to the effect of impregnation under pressure, given that the pitch-impregnated-into-ink-bottle-type pores were difficult to elute during carbonization.

This study investigated the toughening effect of in situ polytriazoleketone (PTK) and polytriazolesulfone (PTS) toughening agent when applied to various epoxy resins, such as diglycidyl ether of bisphenol A (DGEBA), diglycidyl ether of bisphenol F (DGEBF), and triglycidyl p-aminophenol (TGAP) with 3,3′-diaminodiphenylsulfone as a curing agent. The fracture toughness, tensile properties, and thermal properties of the prepared epoxy samples were evaluated and compared. When PTK was mixed with DGEBF, the fracture toughness was improved by 27% with 8.6% increased tensile strength compared to the untoughened DGEBF. When PTS was mixed with TGAP, the fracture toughness was improved by 51% without decreasing tensile properties compared to the untoughened TGAP. However, when PTK or PTS was mixed with other epoxy resins, the fracture toughness decreased or improved with decreasing tensile properties. This is attributed to the poor miscibility between the solid-state monomer of PTK (4,4′-bis(propynyloxy)benzophenone (PBP)) or PTS (4,4′-sulfonylbis(propynyloxy)benzene (SPB)) and the epoxy resin, resulting in the polymerization of low molecular weight PTK or PTS in epoxy resin. Therefore, the toughening effect of PTK or PTS can be maximized by the appropriate selection of epoxy resin based on the miscibility between PBP or SPB and the resin.

Generally, detoxification fabrics are defined as fabrics that remove or inhibit the production of toxic compounds, especially chemical warfare agents such as nerve gas agents. They are usually prepared using a complicated and time-consuming method. This study suggests a facile treatment method for preparing detoxification fabrics against nerve gas agents using polyethyleneimine and microwave curing. The detoxification properties of polyethyleneimine and microwave-treated polypropylene nonwoven fabric were evaluated using diisopropylfluoro-phosphate, which is a nerve agent simulant. The treated polypropylene fabric decontaminated 53.6% of diisopropylfluorophosphate (DFP) in 2 h at 32 °C, and the half-life of DFP on the surface of the treated fabric was 122 min. The result indicates that the treated fabric can act as a basic organocatalyst for the DFP hydrolysis and has a shorter half-life owing to the large number of amine groups. Therefore, the facile treatment method has the potential for use in the preparation of detoxification fabrics.