Clinical studies on the behavior of posterior translucent monolithic zirconia restorations are lacking. We assessed the clinical outcome and survival rate of posterior third-generation monolithic zirconia crowns over a 2-year period. A total of 24 patients, requiring 30 posterior full-contour restorations were selected. All abutments were scanned, and crowns were milled and cemented with a self-adhesive dual cure cement. Crowns were assessed using the California Dental Association’s criteria. Gingival status was assessed by evaluating the gingival index, plaque index, periodontal probing depth of the abutments and control teeth, and the margin index of the abutment teeth. Statistical analyses were performed using the Friedman and the Wilcoxon signed-rank tests. During the 2-year follow-up, no biological or mechanical complications were observed, and the survival and success rate was 100%. All restorations ranked as satisfactory throughout the follow-up period. The gingival index and plaque index were worse at the end of the 2-year follow-up. The margin index was stable during the 2 years of clinical service. No significant differences were recorded in periodontal parameters between crowns and control teeth. Third-generation monolithic zirconia could be a reliable alternative to posterior metal–ceramic and second-generation monolithic zirconia posterior crowns.

The purpose of this study was to investigate the effect of low-pressure plasma on the contact angle, shear bond strength (SBS), and the failure mode of zirconia ceramic. Zirconia specimens were divided into three groups according to the surface treatment methods as follows: sandblasting with aluminum oxide (ZR-C), sandblasting with aluminum oxide and oxygen plasma (ZR-CP), and argon plasma (ZR-P). The contact angle, SBS, and surface characteristics were tested after thermocycling. Data analysis was made using the Kruskal–Wallis test and one-way analysis of variance. Plasma treatment significantly reduced the contact angle (p < 0.001) with the lowest value for the Zr-P group. An increase in oxygen and a decrease in carbon was observed on the zirconia surface in both plasma groups. For the SBS, there were significant differences among the groups (p < 0.018), the Zr-CP group showing the highest bond strength. Mixed failures were the most frequent. Plasma treatment was effective in increasing the wettability, increasing the oxygen/carbon ratio without changing zirconia surface morphology. The sandblasting plus plasma with oxygen group exhibited the highest bond strength.

The introduction of new ceramic materials for dental restorations is currently a reality; however, little information is available on their surface treatment for the bonding process. Furthermore, surface treatment with plasma on ceramic materials has been recently introduced, although not many studies are available. The aim of this study was to evaluate the surface properties of a leucite-reinforced feldspar ceramic (LIC) and resin matrix ceramic (RMC) after low-pressure plasma treatment. From each material, 48 discs were prepared and subject to surface treatment. The LIC group was treated by hydrofluoric acid (HF) (LIC-HF), plasma with oxygen (LIC-O2), and plasma with argon (LIC-Ar). The RMC group was treated by sandblasting with alumina (RMC-SB), plasma with oxygen (RMC-O2), and plasma with argon (RMC-Ar). The groups whose surfaces were not subjected to treatment were considered as the control group. Surface wettability and roughness was analyzed. The results showed significant differences among the treatments for both ceramics regarding wettability and roughness. Plasma treatments increased the wettability and had a very low effect on the roughness. Plasma treatments achieved similar values for both surface properties in each ceramic group with no differences between both treatments. Plasma treatment seems to be a promising alternative for ceramic surface treatments since it increased the surface energy of the ceramics analyzed and hardly affects the roughness. Further studies are necessary to evaluate the effect of plasma treatment on the bond strength of ceramics.

Translucent monolithic zirconia restorations have recently introduced. The purpose of this study was to evaluate the clinical behavior and the survival rate of the posterior third-generation monolithic zirconia crowns (MZCs) during three years of clinical service. Twenty-four patients who needed thirty crowns were enrolled in this study. Digital impressions were made, and the crowns were milled and cemented with a resin cement. The crowns outcomes were assessed using the California Dental Association's (CDA) criteria. Gingival index (GI), plaque index (PI), and periodontal probing depth (PPD) for MZCs and contralateral natural teeth (control) were assessed. Margin index (MI) for MZCs was also assessed. Data analysis was conducted using the Wilcoxon signed-rank and the Friedman tests. The 3-year survival rate was 100%. All MZCs were rated as satisfactory throughout the follow-up period, and no biological or mechanical complications were observed. No differences were recorded when GI, PI and PPD at 3-year of follow-up were compared to baseline. No differences were recorded between crowned and control teeth. The MI remained stable throughout the study period. The third-generation monolithic zirconia appears to be a good treatment option for the rehabilitation of posterior single teeth.

The hydrolysis of the collagen matrix by metalloproteinases (MMPs) is one of the paradigms that currently arouses most interest due to its close relationship with a decrease in bond strength (BS) and consequent restoration failure. Chlorhexidine 2% has demonstrated its ability to inhibit MMPs’ activity in the permanent dentition, improving the duration of resin–dentine, but there are few studies on deciduous dentition and its possible repercussions. Aim: To determine the influence of 2% chlorhexidine digluconate (CHX) as a dentine pretreatment on the BS of three adhesive systems on primary molars. Methods: 128 primary extracted molars were assigned to eight groups at random. BS in vitro was recorded by micropush-out test, and analyzed by two-way ANOVA. Results: BS values oscillated from 15.01 MPa to 20.41 MPa. There was no statistically relevant variation between the BS total mean of those adhesive groups that had received CHX pretreatment versus those that did not. Adper Prompt L-Pop was the self-etching adhesive with the best BS. Adper Scotchbond 1XT was the total-etch adhesive with the best BS values. Conclusions: Application of 2% chlorhexidine for 60 s as dentine pretreatment did not affect the immediate BS of several adhesive systems used in primary dentition.

The immediate loading protocol has become increasingly popular due to the progressive growth in demand for a reduction in treatment times. The possibility of applying this protocol would depend on certain important factors. The application of the digital workflow mentioned in the protocol guarantees rapidity, precision, and esthetics. This report aims to describe a fully digital workflow using a dual scan impression technique to fabricate immediate fixed complete dentures (FCDs) for zygomatic and standard implants. A 58-year-old female patient requested treatment for her severely atrophic maxilla, and four unrehabilitated implants in the mandible. After proper diagnosis and planification, four zygomatic implants and two standard implants were placed. During the surgery, transmucosal abutments were placed on all implants. After suturing, the positions of the implants were recorded using a stereophotogrammetric technique, creating a standard tessellation (STL) file. In the lower arch, the second phase of the surgery was carried out: the transmucosal abutments were placed, and then the implant positions were recorded in the same way. The soft tissues were rescanned after suturing with an intraoral scanner (IOS), and all STL files were aligned to obtain the virtual final models. The pre-design after virtual modifications was aligned with the definitive models. The provisional prostheses were milled and placed after six hours after the surgery, and the definitive prostheses were placed six months after the surgery. The dual scan technique used obtained a precise fit for both the provisional and definitive FCDs. This technique might be an effective and reliable alternative for the fabrication of immediate and definitive screw-retained FCDs in a completely digital workflow. The time taken for scanning and fabrication was reduced, and the clinician’s and patient’s satisfaction were improved.