Herein, we analyzed the morphology of atmospheric plasma-sprayed (APS) coating on medical 316L stainless steel and its influence on the physical and electrochemical properties of implant application. Fivetypes of coatings were examined: hydroxyapatite (HAp), titanium (Ti), zirconium (Zr), Ti/HAp and Zr/HAp. The base properties of the coatings were analyzed via chemical and phase composition, surface topography, surface wettability and in particular the corrosion resistance in Ringer solution in immersed conditions and potentiodynamic test, and EIS analysis. APS coating of pure HAp on 316L stainless steel showed poor cohesive bonding to the substrate material, whereas the application of Ti and Zr interlayer prior to HAp deposition improved surface morphology and coating properties. The beneficial effect of Ti and Zr interlayer under HAp layer on binding was demonstrated. HAp containing coatings (HAp, Ti/HAp and Zr/HAp) show Ca/P ratio greater than 1.8, which may positively influence the differentiation of osteogenic cells and good adhesion to bones. Among the studied materials, the composite coatings with Zr or Zr/HAp showed favorable physicochemical properties and the highest corrosion resistance in Ringer solution.

Increasing demand for sustainable approaches to mining and raw material extraction, has prompted the need to explore advanced methods of surface modification for structural steels used in the extractive industry. The technology of powder plasma transferred arc welding (PPTAW), was used in this study as a surface modification technique to improve upon the abrasive wear resistance of structural steel grade EN S355. PPTAW process parameters, namely, plasma transferred arc (PTA) current and plasma gas flow rate (PGFR), were varied, and the effects of the variation were studied and used as criteria for selecting optimum conditions for further studies and parametric reproducibility. Two metal matrix composite (MMC) powders were used in the process, having compositions of Ni-Si-B+60 wt%WC (PG) and Ni-Cr-Si-B+45 wt%WC (PE). Microstructural observation under a scanning electron microscope (SEM) revealed a dendritic, multi-directional microstructure consisting of partially dissolved primary tungsten carbide particles and secondary tungsten carbide precipitates within the MMC solid solution. The hardness of the surface layers was higher than that of a reference AR400 steel by more than 263 HV. Final surface layers obtained from the MMC powders had abrasive wear resistance up to 5.7 times that of abrasion-resistant reference AR400 steel. Alloying the MMC matrix with chromium increased the hardness by 29.4%. Under the same process conditions, MMC powder with 60 wt% WC reinforcement had better abrasive wear resistance by up to 45.8% more than the MMC powder with 45 wt% WC.

The human body is an extremely aggressive environment in terms of corrosion. Titanium and its alloys are one of the most popular biomaterials used for implant applications due to biocompatibility. However, every element introduced into the body is treated as a foreign body. The human body’s immune response may, therefore, lead to implant rejection and the need for reoperation. For this purpose, it seems important to carry out surface modifications by applying coatings and inter alia by texturing to implants. The objective of this paper is to investigate the effect of surface treatment on the chosen properties of the pure titanium (Grade II) samples obtained by selective laser melting (SLM) processing. The samples were divided into five groups: Initial state (after polishing), after surface modification by the physical vapour deposition (PVD) method—CrN and TiN coatings were deposited on the surface of the tested material, and after laser texturing. The paper presents the results of the microscopic investigation, chemical and phase compositions, and physicochemical and electrochemical properties of the tested samples. Based on the results obtained it can be concluded that the hybrid surface modification shows significant effects on the properties of the pure titanium. The samples with the textured PVD-deposited TiN coatings were characterized by favorable physicochemical properties and were the highest performing in terms of pitting corrosion resistance.