The capability of some polymers, such as chitosan, to form low cost gels under mild conditions is of great application interest. Ionotropic gelation of chitosan has been used predominantly for the preparation of gel beads for biomedical application. Only in the last few years has the use of this method been extended to the fabrication of chitosan-based flat structures. Herein, after an initial analysis of the major applications of chitosan flat membranes and films and their usual methods of synthesis, the process of ionotropic gelation of chitosan and some recently proposed novel procedures for the synthesis of flat structures are presented.

Total phenolic compounds (TPC) and the chlorogenic acids content of potato by-product extracts of two hydro alcoholic solvents (methanol, ethanol) and two extraction methods (maceration and heating-assisted extraction) were studied. The content of TPC in the extracts was determined spectrometrically according to the Folin–Ciocalteu procedure and calculated as chlorogenic acid equivalents. Soluble phenolic acids, especially the chlorogenic acids, were performed by HPLC. The antioxidant activity of potato by-product extracts was determined by using the total oxygen radical absorbance capacity (ORAC) method. The highest content of TPC was found in raw and lyophilized red waters when using ethanol as a solvent around 57 mg/g fresh weight. Heating-assisted extraction enhances this quantitative increasing. At the given operating conditions, unpeeled potato samples exhibit a higher TPC than peeled ones, showing that TPC are accumulated in skin tissue. The greatest amount of chlorogenic acid (Caffeoyl-Quinic Acids, 3, 4, 5 CQA), mainly the 5-CQA (870 ± 39.66 µg/g WM for wet matter versus DM dry matter), was obtained in the pellets and lyophilized fresh peels (skin vs. flesh). In addition, the greatest amounts of chlorogenic acids were found when potato peels were extracted with methanol. Heating-assisted extraction improved the chlorogenic acid concentration of the potato peel extracts. The total ORAC amounts recorded in the different potato fractions varied between 1500 and 1650 µM TE/g. They were higher than those of some fruits, vegetables, nuts, cereals, and sweet potato cultivar. The good correlation coefficient found between TPC, chlorogenic acids determination, and the ORAC capacity indicates that the TPC can be used as a good indicator of the antioxidant capacity of potato by-products.

The curcumin degradation represents a significant limitation for its applications. The stability of free curcumin (FC) and immobilized curcumin in complex particles (ComPs) based on different polysaccharides was studied under the action of several factors. Ultraviolet-visible (UV-VIS) and Fourier-transform infrared (FTIR) spectroscopy proved the FC photodegradation and its role as a metal chelator: 82% of FC and between 26% and 39.79% of curcumin within the ComPs degraded after exposure for 28 days to natural light. The degradation half-life (t_1/2) decreases for FC when the pH increases, from 6.8 h at pH = 3 to 2.1 h at pH = 9. For curcumin extracted from ComPs, t_1/2 was constant (between 10 and 13 h) and depended on the sample’s composition. The total phenol (TPC) and total flavonoids (TFC) content values increased by 16% and 13%, respectively, for FC exposed to ultraviolet light at λ = 365 nm (UVA), whereas no significant change was observed for immobilized curcumin. Antioxidant activity expressed by IC₅₀ (µmoles/mL) for FC exposed to UVA decreased by 29%, but curcumin within ComPs was not affected by the UVA. The bovine serum albumin (BSA) adsorption efficiency on the ComPs surface depends on the pH value and the cross-linking degree. ComPs have a protective role for the immobilized curcumin.