Smart polymeric micelles (PMs) are of practical interest as nanocarriers for the encapsulation and controlled release of hydrophobic drugs. Two hydrophobic drugs, naturally-based curcumin (Cur) and synthetic 5-fluorouracil (5-FU), were loaded into the PMs formed by a well-defined pH-sensitive poly(2-vinyl pyridine)-b-poly(ethylene oxide) (P2VP₉₀-b-PEO₃₉₈) block copolymer. The influence of the drug loading on the micellar sizes was investigated by dynamic light scattering (DLS) and it appears that the size of the PMs increases from around 60 to 100 nm when Cur is loaded. On the contrary, the loading of the 5-FU has a smaller effect on the micellar sizes. This difference can be attributed to higher molar mass of Cur with respect to 5-FU but also to higher loading efficiency of Cur, 6.4%, compared to that of 5-FU, 5.8%. In vitro drug release was studied at pH 2, 6.8, and 7.4, and it was observed that the pH controls the release of both drugs. At pH 2, where the P2VP sequences from the “frozen-in” micellar core are protonated, the drug release efficiencies exceed 90%. Moreover, it was demonstrated, by in vitro assays, that these PMs are hemocompatible and biocompatible. Furthermore, the PMs protect the Cur against the photo-degradation, whereas the non-ionic PEO corona limits the adsorption of bovine serum albumin (BSA) protein on the surface. This study demonstrates that these pH-sensitive PMs are suitable for practical utilization as human-safe and smart, injectable drug delivery systems.

Two natural polymers, i.e., cellulose and water soluble pullulan, have been selectively oxidized employing the TEMPO-mediated protocol, to allow the introduction of C₆-OOH groups. Thereafter, the composite hydrogels of poly(vinyl alcohol) (PVA) and different content of the oxidized polysaccharides were prepared by the freezing/thawing method. The Fourier transform infrared spectroscopy (FTIR) has been used to discuss the degree of interaction between the hydrogels constituents into the physical network. The homogeneity of the prepared hydrogels as revealed by the SEM show an excellent distribution of the oxidized polysaccharides inside the PVA matrix. The samples exhibit self-healing features, since they quickly recover the initial structure after being subjected to a large deformation. The cell viability was performed for the selected hydrogels, all of them showing promising results. The samples are able to load L-arginine both by physical phenomena, such as diffusion, and also by chemical phenomena, when imine-type bonds are likely to be formed. The synergism between the two constituents, PVA and oxidized polysaccharides, into the physical network, propose these hydrogels for many other biomedical applications.

Magnolia spp. extracts are known for their use in traditional Korean, Chinese, and Japanese medicine in the treatment of gastrointestinal disorders, anxiety, and allergies. Among their main components with pharmacological activity, the most relevant are magnolol and honokiol, which also show antitumoral activity. The objectives of this work were to study some physicochemical properties of both substances and their stability under different conditions of temperature, pH, and oxidation. Additionally, liposomes of honokiol (the least stable compound) were formulated and characterized. Both compounds showed pH-dependent solubility, with different solubility–pH profiles. Magnolol showed a lower solubility than honokiol at acidic pH values, but a higher solubility at alkaline pH values. The partition coefficients were similar and relatively high for both compounds (log P_o/w ≈ 4.5), indicating their lipophilic nature. Honokiol was less stable than magnolol, mainly at neutral and basic pH values. To improve the poor stability of honokiol, it was suitably loaded in liposomes. The obtained liposomes were small in size (175 nm), homogeneous (polydispersity index = 0.17), highly negatively charged (−11 mV), and able to incorporate high amounts of honokiol (entrapment efficiency = 93.4%). The encapsulation of honokiol in liposomes increased its stability only at alkaline pH values.