Polyaniline (PANI) and silver doped polyaniline (Ag/PANI) thin films were deposited on stainless steel substrates by a dip coating technique. To study the effect of doping concentration of Ag on the specific capacitance of PANI the concentration of Ag was varied from 0.3 to 1.2 weight percent. Fourier transform-infrared and Fourier transform-Raman spectroscopy, and energy dispersion X-ray techniques were used for the phase identification and determination of the doping content in the PANI films, respectively. The surface morphology of the films was examined by Field Emission Scanning Electron Microscopy, which revealed a nanofiber like structure for PANI and nanofibers with bright spots of Ag particles for the Ag/PANI films. There was decrease in the room temperature electrical resistivity of the Ag/PANI films of the order of 10² with increasing Ag concentration. The supercapacitive behavior of the electrodes was tested in a three electrode system using 1.0 M H₂SO₄ electrolyte. The specific capacitance increased from 285 F g⁻¹ (for PANI) to 512 F g⁻¹ for Ag/PANI at 0.9 weight percent doping of Ag, owing to the synergic effect of PANI and silver nanoparticles. This work demonstrates a simple strategy of improving the specific capacitance of polymer electrodes and may also be easily adopted for other dopants.

In this study, amorphous manganese oxide (MnO₂) nanostructured thin films were synthesized by a simple hydrothermal method. It is well known that the nanostructure plays a crucial role in energy storage applications. Herein, MnO₂ nanostructures ranging from plates to flakes were synthesized without the use of any hard or soft templates. The 4+ oxidation state of Mn was confirmed by X-ray photoelectron spectroscopy. The MnO₂ nanoflake structure has a specific surface area of 46 m²g⁻¹, which provides it with an excellent rate capability and an exactly rectangular cyclic voltammogram (CV) curve. The MnO₂ nanoflake electrode has a high specific capacitance of about 433 Fg⁻¹, an energy density of 60 Whkg⁻¹ at 0.5 mAcm⁻², and an excellent cyclic stability of 95% over 1000 CV cycles in 1 M aq. Na₂SO₄. Kinetics analysis of the charge storage in the nanoflake MnO₂ sample shows a 55.6% diffusion-controlled contribution and 44.4% capacitive-controlled contribution to the total current calculated at a scan rate of 100 mVs⁻¹ from the CV curve.

A ternary nanocomposite with poly (3,4 ethylene dioxythiophene:poly(styrene sulfonate) (PEDOT:PSS)-MnO₂ nanowires-graphene oxide (PMn-GO) was synthesized by using simple chemical route. The formation of the nanocomposite was analyzed by using X-ray diffraction and X-ray photoelectron spectroscopy. Field-emission scanning microscopy (FESEM) revealed the formation of MnO₂ nanowires and graphene oxide nanosheets. The highest specific capacitance (areal capacitance) of 841 Fg ⁻¹ (177 mFcm ⁻²) at 10 mVs ⁻¹ and energy density of 0.593 kWhkg ⁻¹ at 0.5 mA were observed for PMn-GO, indicating a constructive synergistic effect of PEDOT:PSS, MnO₂ nanowires and graphene oxide. The achieved promising electrochemical characteristics showed that this ternary nanocomposite is a good alternative as an electrode material for supercapacitor.

Quantum dot heterojunctions with type-II band alignment can efficiently separate photogenerated electron-hole pairs and, hence, are useful for solar cell studies. In this study, a quantum dot...

This work presents a synthesis of hierarchical manganese–iron-layered double hydroxide (MnFe-LDH) nanostructured electrodes using the hydrothermal synthesis route by varying the reaction time for electrochemical energy storage applications. The electrochemical behavior of the MnFe-LDH electrodes synthesized at different reaction times was analyzed in a three-electrode cell configuration using 2 M KOH electrolyte. The uniform and well-organized MnFe-LDH nanosheet electrode (MnFe-12h) showed the maximum areal capacitance of 2013 mFcm⁻² at a 5 mVs⁻¹ scan rate, and 1886 mFcm⁻² at a 25 mA applied current. Furthermore, the electrochemical behavior of MnFe-12h was examined by assembling an asymmetric cell device using activated carbon (AC) as a negative electrode and MnFe-12h as a positive electrode and it was tested in a wide voltage window range of 0.0 to 1.6 V. This asymmetric cell device achieved an appropriate energy density of 44.9 µW h cm⁻² (55.01 W h kg⁻¹), with a power density of 16 mW cm⁻² (5000 W kg⁻¹) at an applied current of 10 mA, and had a long-term cycling stability (93% capacitance retention after 5000 cycles) within the 1.6 V operating voltage window.