Engineered, superparamagnetic, iron oxide nanoparticles (IONPs) have significant potential as platform materials for environmental sensing, imaging and remediation due to their unique size, physicochemical and magnetic properties. To this end, controlling the size and surface chemistry of the materials is crucial for such applications in the aqueous phase, and in particular, for porous matrixes with particle-surface interaction considerations. In this study, superparamagnetic, highly monodispersed 8 nm IONPs were synthesized and transferred into water as stable suspensions (remaining monodispersed) by way of an interfacial oleic acid bilayer surface. Once stabilized and characterized, particle–particle and model surface interactions (deposition and release) were quantitatively investigated and described systematically as a function of ionic strength (IS) and type with time-resolved dynamic light scattering (DLS), zeta potential, and real-time quartz crystal microbalance with dissipation monitoring (QCM-D) measurements. The critical coagulation concentration (CCC) for oleic acid bilayer coated iron oxide nanoparticles (OA-IONPs) were determined to be 710 mM for NaCl (matching DLVO predictions) and 10.6 mM for CaCl₂, respectively. For all conditions tested, surface deposition kinetics showed stronger, more favorable interactions between OA-IONPs and polystyrene surfaces compared to silica, which is hypothesized to be due to increased particle-surface hydrophobic interactions (when compared to silica surfaces).

Optimized engineered manganese ferrite (MnFe ₂ O ₄ ) nanocrystals, stabilized by tailorable organic acid bilayer structures, demonstrate ultra enhanced uranyl sorption capacities under environmental relevant aqueous conditions.

Herein, we describe engineered superparamagnetic iron oxide nanoparticles (IONPs) as platform materials for enhanced uranyl (UO₂²⁺) sorption and separation processes under environmentally relevant conditions. Specifically, monodispersed 8–25 nm iron oxide (magnetite, Fe₃O₄) nanoparticles with tailored organic acid bilayered coatings have been systematically evaluated and optimized to bind, and thus remove, uranium from water. The combined nonhydrolytic synthesis and bilayer phase transfer material preparation methods yield highly uniform and surface tailorable IONPs, which allow for direct evaluation of the size-dependent and coating-dependent sorption capacities of IONPs. Optimized materials demonstrate ultrahigh sorption capacities (>50% by wt/wt) at pH 5.6 for 8 nm oleic acid (OA) bilayer and sodium monododecyl phosphate (SDP) surface-stabilized IONPs. Synchrotron-based X-ray absorption spectroscopy shows that iron oxide core particle size and stabilizing surface functional group(s) substantially affect U(VI)-removal mechanisms, specifically the ratio of uptake via adsorption versus reduction to U(IV). Taken together, tunable size and surface functionality, high colloidal stability, and favorable affinity toward uranium provide distinct synergistic advantage(s) for the application of bilayered IONPs as part of the next-generation material-based uranium recovery, remediation, and sensing technologies.

Feasibility of osmotic backwashing for cleaning fouled membranes during forward osmosis (FO) process was investigated focusing on the mechanisms and factors involved. Alginate and humic acids were used as model organic foulants; and colloidal silica particles with different sizes were used as model inorganic particulate foulants. Results showed that noticeable flux recovery was achieved by osmotic backwashing through the instantaneous replacement of the draw solution with the dilute solution that has much less osmotic pressure than that of the feed solution. The switch of water flow direction through the membrane from feed-to-draw to draw-to-feed allows the effective detachment of foulants from the membrane surface. It was found that the efficiency of osmotic backwashing was affected by several factors including foulant type, membrane orientation and backwashing conditions (i.e. initial flux and duration). In addition, concentration polarization was found to play an important role in determining fouling behaviour, and thus, the osmotic backwashing efficiency.