Perovskite solar cells with the formula FA_1−xCs_xPbI₃, where FA is formamidinium, provide an attractive option for integrating high efficiency, durable stability and compatibility with scaled-up fabrication. Despite the incorporation of Cs cations, which could potentially enable a perfect perovskite lattice^1,2, the compositional inhomogeneity caused by A-site cation segregation is likely to be detrimental to the photovoltaic performance of the solar cells^3,4. Here we visualized the out-of-plane compositional inhomogeneity along the vertical direction across perovskite films and identified the underlying reasons for the inhomogeneity and its potential impact for devices. We devised a strategy using 1-(phenylsulfonyl)pyrrole to homogenize the distribution of cation composition in perovskite films. The resultant p–i–n devices yielded a certified steady-state photon-to-electron conversion efficiency of 25.2% and durable stability.

High-purity precursor materials are vital for high-efficiency perovskite solar cells (PSCs) to reduce defect density caused by impurities in perovskite. In this study, we present aqueous synthesized perovskite microcrystals as precursor materials for PSCs. Our approach enables kilogram-scale mass production and synthesizes formamidinium lead iodide (FAPbI ₃ ) microcrystals with up to 99.996% purity, with an average value of 99.994 ± 0.0015%, from inexpensive, low-purity raw materials. The reduction in calcium ions, which made up the largest impurity in the aqueous solution, led to the greatest reduction in carrier trap states, and its deliberate introduction was shown to decrease device performance. With these purified precursors, we achieved a power conversion efficiency (PCE) of 25.6% (25.3% certified) in inverted PSCs and retained 94% of the initial PCE after 1000 hours of continuous simulated solar illumination at 50°C.

Perovskite oxide BaSnO₃ with high electron mobility and a perovskite structure was first used as an electron-transporting layer in perovskite solar cells. After optimization, the resulting mp-BSO device can perform as well as the mp-TiO₂ one and even better.

The promising candidate La-BaSnO₃ provides a novel perspective on the application and investigation of doped materials in PSCs.