Inulin is a polysaccharide of fructose widely used in the food and pharmaceutical industry due to its physicochemical properties and technological applications. Inulin from jicama (Smallanthus sonchifolius) and cabuya (Agave americana) was obtained. The steps for inulin obtention were: raw material preparation, extraction and purification. The extraction conditions were determined using a random design with three levels of stirring speed (0, 130 and 300 rpm), and a 3² factorial experimental design with three levels of temperature (40, 60 and 80 °C) and solid:liquid ratio (1:2, 1:3 and 1:5 S:L). The results showed that the best extractions conditions for jicama were 130 rpm, 75 °C, 1:5 S:L and 25 min; while for cabuya were 80 °C, 300 rpm, 1:5 S-L and 100 min. The weight average molecular weight of inulin from jicama and cabuya were 5799.9 and 4659.75 g/mol, respectively. The identity of the obtained inulin from jicama and cabuya were confirmed by infrared (IR) and Raman spectroscopy. In addition, scanning electron microscopy, differential scanning calorimetry and thermogravimetry analyses were performed to characterize both inulins.

Thiosulfate leaching combined with ion-exchange resins is an innovative alternative for gold recovery. According to the properties of activated carbon, it could replace resins in the gold recovery process, improve efficiency, and reduce operating cost. In this research, the adsorption process of gold thiosulfate complex on thiol-modified activated carbon was studied. Thioglycolic acid (ATG) was impregnated in activated carbon, and its adsorption ability was tested with synthetic solutions of gold and sodium thiosulfate (Au 10 mg·L⁻¹, Na₂S₂O₃ 0.1 mol·L⁻¹, pH = 10.0). Carbon was characterized by infrared spectroscopy, SEM-EDS, PZC titration, hardness number measures, and proximal analysis. Synthetic solutions were also characterized by UV-vis spectroscopy and cyclic voltammetry. The percentage of volatile material increased from 10.0 to 13.9% due to the impregnation process of ATG. Infrared spectra show characteristic bands of C-H, S-H, and C-S bonds. In the adsorption tests, the ATG-impregnated carbon achieved 91% of gold recovery, while the same amount of ATG in the liquid phase stirred with unmodified activated carbon reached 90% of gold recovery. The 44.9% of gold recovered with activated carbon impregnated with ATG was eluted with sodium cyanide ([NaCN] = 0.2 mol·L⁻¹; [NaOH] = 0.25 mol·L⁻¹; [CH₃CH₂OH] = 30% V/V; pH = 12.0; t = 24 h). These results suggest the gold transferred from the thiosulfate complex to a new gold thiolate complex.