We experimentally investigated the effect of post-growth annealing on the morphological, structural, and electrophysical parameters of nanocrystalline ZnO films fabricated by pulsed laser deposition. The influence of post-growth annealing modes on the electroforming voltage and the resistive switching effect in ZnO nanocrystalline films is investigated. We demonstrated that nanocrystalline zinc oxide films, fabricated at certain regimes, show the electroforming-free resistive switching. It was shown, that the forming-free nanocrystalline ZnO film demonstrated a resistive switching effect and switched at a voltage 1.9 ± 0.2 V from 62.42 ± 6.47 (R_HRS) to 0.83 ± 0.06 kΩ (R_LRS). The influence of ZnO surface morphology on the resistive switching effect is experimentally investigated. It was shown, that the ZnO nanocrystalline film exhibits a stable resistive switching effect, which is weakly dependent on its nanoscale structure. The influence of technological parameters on the resistive switching effect in a forming-free ZnO nanocrystalline film is investigated. The results can be used for fabrication of new-generation micro- and nanoelectronics elements, including random resistive memory (ReRAM) elements for neuromorphic structures based on forming-free ZnO nanocrystalline films.

One of the significant limitations of the pulsed laser deposition method in the mass-production-technologies of micro- and nanoelectronic and molecular device electronic fabrication is the issue of ensuring deposition of films with uniform thickness on substrates with large diameter (more than 100 mm) since the area of the laser spot (1–5 mm²) on the surface of the ablated target is incommensurably smaller than the substrate area. This paper reports the methodology that allows to calculate the distribution profile of the film thickness over the surface substrate with a large diameter, taking into account the construction and technological parameters of the pulsed laser deposition equipment. Experimental verification of the proposed methodology showed that the discrepancy with the experiment does not exceed 8%. The modeling of various technological parameters influence on the thickness uniformity has been carried out. Based on the modeling results, recommendations and parameters are proposed for manufacturing uniform thickness films. The results allow for increasing the film thickness uniformity with the thickness distribution < 5% accounts for ~ 31% of 300 mm diameter substrate.

This article presents the results of experimental studies of the impact of electrode material and the effect of nanoscale film thickness on the resistive switching in forming-free nanocrystalline ZnO films grown by pulsed laser deposition. It was demonstrated that the nanocrystalline ZnO film with TiN, Pt, ZnO:In, and ZnO:Pd bottom electrodes exhibits a nonlinear bipolar effect of forming-free resistive switching. The sample with Pt showed the highest resistance values R_HRS and R_LRS and the highest value of U_set = 2.7 ± 0.4 V. The samples with the ZnO:In and ZnO:Pd bottom electrode showed the lowest U_set and U_res values. An increase in the number of laser pulses from 1000 to 5000 was shown to lead to an increase in the thickness of the nanocrystalline ZnO film from 7.2 ± 2.5 nm to 53.6 ± 18.3 nm. The dependence of electrophysical parameters (electron concentration, electron mobility, and resistivity) on the thickness of the forming-free nanocrystalline ZnO film for the TiN/ZnO/W structure was investigated. The endurance test and homogeneity test for TiN/ZnO/W structures were performed. The structure Al₂O₃/TiN/ZnO/W with a nanocrystalline ZnO thickness 41.2 ± 9.7 nm was shown to be preferable for the manufacture of ReRAM and memristive neuromorphic systems due to the highest value of R_HRS/R_LRS = 2307.8 ± 166.4 and low values of U_set = 1.9 ± 0.2 V and U_res = −1.3 ± 0.5 V. It was demonstrated that the use of the TiN top electrode in the Al₂O₃/TiN/ZnO memristor structure allowed for the reduction in U_set and Ures and the increase in the R_HRS/R_LRS ratio. The results obtained can be used in the manufacturing of resistive-switching nanoscale devices for neuromorphic computing based on the forming-free nanocrystalline ZnO oxide films.

The influence of the parameters of the deposition process on the stoichiometric composition and electrical and optical properties of ZnO films deposited by the ion-beam sputtering of a ZnO target is...

This paper reports the results of the influence of the energy of laser pulses during laser ablation on the morphology and electro-physical properties of LiNbO₃ nanocrystalline films. It is found that increasing laser pulse energy from 180 to 220 mJ results in the concentration of charge carriers in LiNbO₃ films decreasing from 8.6 × 10¹⁵ to 1.0 × 10¹³ cm⁻³, with the mobility of charge carriers increasing from 0.43 to 17.4 cm²/(V·s). In addition, experimental studies of sublayer material effects on the geometric parameters of carbon nanotubes (CNTs) are performed. It is found that the material of the lower electrode has a significant effect on the formation of CNTs. CNTs obtained at the same growth time on a sample with a Cr sublayer have a smaller diameter and a longer length compared to samples with a V sublayer. Based on the obtained results, the architecture of the energy nanogenerator is proposed. The current generated by the nanogenerator is 18 nA under mechanical stress of 600 nN. The obtained piezoelectric nanogenerator parameters are used to estimate the parameters of the hybrid-carbon-nanostructures-based piezoelectric energy converter. Obtained results are promising for the development of efficient energy converters for alternative energy devices based on lead-free ferroelectric films.