Production of aerogels starts with solution chemistry and may end with supercritical carbon dioxide drying, which both require a specialized system. Here we present a complete aerogel production system that was developed and used in our laboratory over the last nine years. Our aim was to develop a supercritical dryer and a protocol, whereby the CO₂ pump can be left out, and the entire flow system is operated by the pressure of the CO₂ cylinder. Drying pressure and temperature are controlled by the combination of the filling and heating temperatures. A continuous-mode solvent exchange system has also been developed, in which the solvent consumption during the process can be reduced to one-third of the batch method. In the new medium temperature 1.5 L volume supercritical dryer, the temperature is set to a constant 80–82 °C, and the pressure can be in the 90–200 bar range, depending on the conditions. We have performed approximately 200 dryings thus far, and prepared a wide range of monolithic aerogels, from pristine silica aerogels to polysaccharides and collagen. In this paper, we have summarized not only the technical details, but also the work experiences, as well as advantages and disadvantages of the systems.

The imaging of non-conducting materials by scanning electron microscopy (SEM) is most often performed after depositing few nanometers thick conductive layers on the samples. It is shown in this work, that even a 5 nm thick sputtered gold layer can dramatically alter the morphology and the surface structure of many different types of aerogels. Silica, polyimide, polyamide, calcium-alginate and cellulose aerogels were imaged in their pristine forms and after gold sputtering utilizing low voltage scanning electron microscopy (LVSEM) in order to reduce charging effects. The morphological features seen in the SEM images of the pristine samples are in excellent agreement with the structural parameters of the aerogels measured by nitrogen adsorption-desorption porosimetry. In contrast, the morphologies of the sputter coated samples are significantly distorted and feature nanostructured gold. These findings point out that extra care should be taken in order to ensure that gold sputtering does not cause morphological artifacts. Otherwise, the application of low voltage scanning electron microscopy even yields high resolution images of pristine non-conducting aerogels.