Silica-gelatin hybrid aerogels of varying gelatin content (from 4 wt.% to 24 wt.%) can be conveniently impregnated with hydrophobic active agents (e.g. ibuprofen, ketoprofen) in supercritical CO₂ and used as drug delivery systems. Contrast variation neutron scattering (SANS) experiments show the molecular level hybridization of the silica and the gelatin components of the aerogel carriers. The active agents are amorphous, and homogeneously dispersed in these porous, hybrid matrices. Importantly, both fast and retarded drug release can be achieved with silica-gelatin hybrid aerogels, and the kinetics of drug release is governed by the gelatin content of the carrier. In this paper, for the first time, a molecular level explanation is given for the strong correlation between the composition and the functionality of a family of aerogel based drug delivery systems. Characterization of the wet aerogels by SANS and by NMR diffusiometry, cryoporometry and relaxometry revealed that the different hydration mechanisms of the aerogels are responsible for the broad spectrum of release kinetics. Low-gelatin (4-11 wt.%) aerogels retain their open-porous structure in water, thus rapid matrix erosion dictates fast drug release from these carriers. In contrast to this, wet aerogels of high gelatin content (18-24 wt.%) show well pronounced hydrogel-like characteristics, and a wide gradual transition zone forms in the solid-liquid interface. The extensive swelling of the high-gelatin hybrid backbone results in the collapse of the open porous structure, that limits mass transport towards the release medium, resulting in slower, diffusion controlled drug release. STATEMENT OF SIGNIFICANCE: Developing new drug delivery systems is a key aspect of pharmaceutical research. Supercritically dried mesoporous aerogels are ideal carriers for small molecular weight drugs due to their open porous structures and large specific surface areas. Hybrid silica-gelatin aerogels can display both fast and retarded drug release properties based on the gelatin contents of their backbones. The structural characterization of the aerogels by SANS and by NMR diffusiometry, cryoporometry and relaxometry revealed that the different hydration mechanisms of the hybrid backbones are responsible for the broad spectrum of release kinetics. The molecular level understanding of the functionality of these hybrid inorganic-biopolymer drug delivery systems facilitates the realization of quality-by-design in this research field.

Magnetic iron oxide-silica shell nanocomposites with different iron oxide/silica ratio were synthesized and structurally characterized by Fourier transform infrared (FT-IR) spectroscopy, X-ray diffraction (XRD), small-angle neutron scattering, magnetic and N₂-sorption studies. The composite that resulted with the best properties in terms of contact surface area and saturation of magnetization was selected for Pb²⁺ adsorption studies from aqueous media. The material presented good absorption capacity (maximum adsorption capacity 14.9 mg·g⁻¹) comparable with similar materials presented in literature. Its chemico-physical stability and adsorption capacity recommend the nanocomposite as a cheap adsorbent material for lead.

Mesoporous silica particles have been prepared with functionalized precursors, used either in situ co-condensation process or as post-synthesis grafting agents, in order to deliver surface functionalisation. Aminopropyl, mercaptopropyl, vinyl and hexyl organosilanes were used as funtionalized precursors, tetraethylorthosilicat as the base silica precursor material, hexadecyl-trimethylammonium bromide (CTAB) as directing agent and water-ethanol mixture as solvent, with ammonia catalyst. The aim was to explore the effect of various recipes on the structural properties of the composite materials. The samples’ microstructures have been evaluated using nitrogen sorption and small angle neutron scattering. Ordered mesoporous structures were obtained, for almost all synthesis conditions, after the solvent-extraction of the template agent. Only in one case, for the materials functionalized by mercaptopropyl groups in co-condensation route, disordered amorphous structure was obtained. All samples functionalized by post-grafting presented well-ordered structures mesoporous structures. The results have potential use for easy design of sorbent materials for drug loading or pollutant adsorption applications.