Globally, the amounts of metal ore deposits have been declining, so the research directions investigating the extraction of metals from materials that are classified as waste are gaining more importance every year. High concentrations of Cu, Pb, Zn, and Fe were analyzed in the sludge sediment (Zlaté Hory, Czech Republic), which is a waste product of the mining industry. In the bioleaching process, bacterial cells have been established as being able to convert metals from solid to liquid phase. However, the most important parameters of bioleaching are particle size, pH, and pulp density, thus our research focused on their optimization. The acidophilic and mesophilic bacteria Acidithiobacillus ferrooxidans were applied due to the high Fe content in the sample. The recovery of metals in the leachate was determined by F-AAS and the residual metal concentrations in the waste fraction were analyzed by XRF. The grain size fractions <40 µm –200 µm were investigated. The atomic absorption spectrometry (AAS) results show that the highest Fe (76.48%), Cu (82.01%), and Pb (88.90%) recoveries were obtained at particle size of 71–100 μm. Zn was dissolved for all fractions above 90%. Experiments with different pH values were performed at a pH of 1.6–2.0. The highest dissolution rates of Zn, Fe, and Cu were achieved with a suspension pH of 1.8, where 98.73% of Zn, 85.42% of Fe, and 96.44% of Cu were recovered. Due to the high percentage dissolution of metals, experiments were performed under pilot conditions in a bioreactor at a pulp density of 2.5% and 4.2% (w/v). From an economic point of view, the leaching time of 28 days was evaluated as sufficient.

Large amounts of coal combustion products (as solid products of thermal power plants) with different chemical and physical properties cause serious environmental problems. Even though coal fly ash is a coal combustion product, it has a wide range of applications (e.g., in construction, metallurgy, chemical production, reclamation etc.). One of its potential uses is in zeolitization to obtain a higher added value of the product. The aim of this paper is to produce a material with sufficient textural properties used, for example, for environmental purposes (an adsorbent) and/or storage material. In practice, the coal fly ash (No. 1 and No. 2) from Czech power plants was firstly characterized in detail (X-ray diffraction (XRD), X-ray fluorescence (XRF), scanning electron microscopy with energy dispersive X-ray analysis (SEM-EDX), particle size measurement, and textural analysis), and then it was hydrothermally treated to synthetize zeolites. Different concentrations of NaOH, LiCl, Al₂O₃, and aqueous glass; different temperature effects (90–120 °C); and different process lengths (6–48 h) were studied. Furthermore, most of the experiments were supplemented with a crystallization phase that was run for 16 h at 50 °C. After qualitative product analysis (SEM-EDX, XRD, and textural analytics), quantitative XRD evaluation with an internal standard was used for zeolitization process evaluation. Sodalite (SOD), phillipsite (PHI), chabazite (CHA), faujasite-Na (FAU-Na), and faujasite-Ca (FAU-Ca) were obtained as the zeolite phases. The content of these zeolite phases ranged from 2.09 to 43.79%. The best conditions for the zeolite phase formation were as follows: 4 M NaOH, 4 mL 10% LiCl, liquid/solid ratio of 30:1, silica/alumina ratio change from 2:1 to 1:1, temperature of 120 °C, process time of 24 h, and a crystallization phase for 16 h at 50 °C.

Rapid regenerative medicine development requires new advanced biomaterials. Chitosan which is known of its unique properties like biocompability, biodegradability, bioactivity, antibacterial activity is a great candidate for scaffolds for cell culture. In this paper, a novel strategy for antioxidant aerogels obtainment method is presented. Biomaterials were synthesized under microwave-assisted conditions and modified with Tiliaplatyphyllos extract. Ready products were characterized over their physicochemical properties, morphology and biological properties including bioactivity and antimicrobial activity. Performed analyses confirmed obtainment of crosslinked biomaterial with advanced properties such as positive effect on cells proliferation and inhibition of Staphylococcus aureus growth.

Tissue engineering provides alternative solutions to traditional transplantation. In this study a novel strategy of chitosan scaffolds obtainment based on selective O-crosslinking using Aspartic acid and the addition of TiO₂ nanoparticles is presented. Prepared under microwave conditions biomaterials were of increased mechanical and thermal durability thanks to NPs presence comparing to pure chitosan. Moreover porous scaffolds maintained antimicrobial activity against S. Aureus and E. Coli. Biomaterials were susceptible to in vitro biodegradation and degradation. Hydrogels exhibited positive impact on proliferation activity of fibroblasts. Thus they may be applied as 3D scaffolds in tissue engineering focused on wound healing. GRAPHICAL ABSTRACT