Tin doped indium oxide (ITO) coatings fabricated onto D-shaped optical fibers are presented as the supporting medium for Lossy Mode Resonances (LMRs) generation. The characteristic geometry of ITO-coated D-shaped optical fibers enables to observe experimentally LMRs obtained with both TM and TE polarized light (LMR_TM and LMR_TE). This permits to obtain a maximum transmission decay of 36 dB with a LMR spectral width of 6.9 nm, improving that obtained in previous works, where the LMRs were a combination of an LMR_TM and an LMR_TE. Surrounding medium refractive index (SMRI) sensitivity characterization of LMR_TM has been performed obtaining a maximum sensitivity of 8742 nm/RIU in the range 1.365-1.38 refractive index units (RIU) which overcomes that of surface plasmon resonance-based optical fiber devices presented in recent works.

Nanocoated D-shaped optical fibers have been proven as effective sensors. Here, we show that the full width at half minimum (FWHM) of lossy mode resonance can be reduced by optimizing the nanocoating width, thickness and refractive index. As a counterpart, several resonances are observed in the optical spectrum for specific conditions. These resonances are caused by multiple modes guided in the nanocoating. By optimizing the width of the coating and the imaginary part of its refractive index, it is possible to isolate one of these resonances, which allows one to reduce the full width at half minimum of the device and, hence, to increase the figure of merit. Moreover, it is even possible to avoid the need of a polarizer by designing a device where the resonance bands for TE and TM polarization are centered at the same wavelength. This is interesting for the development of optical filters and sensors with a high figure of merit.

The measurement of chemical and biomedical parameters can take advantage of the features exclusively offered by optical fibre: passive nature, electromagnetic immunity and chemical stability are some of the most relevant ones. The small dimensions of the fibre generally require that the sensing material be loaded into a supporting matrix whose morphology is adjusted at a nanometric scale. Thanks to the advances in nanotechnology new deposition methods have been developed: they allow reagents from different chemical nature to be embedded into films with a thickness always below a few microns that also show a relevant aspect ratio to ensure a high transduction interface. This review reveals some of the main techniques that are currently been employed to develop this kind of sensors, describing in detail both the resulting supporting matrices as well as the sensing materials used. The main objective is to offer a general view of the state of the art to expose the main challenges and chances that this technology is facing currently.