In the current study, solid-state additive manufacturing (SSAM) of two temper conditions AA2011 was successfully conducted using the friction stir deposition (FSD) process. The AA2011-T6 and AA2011-O consumable bars of 20 mm diameter were used as a feeding material against AA5083 substrate. The effect of the rotation rate and feeding speed of the consumable bars on the macrostructure, microstructure, and hardness of the friction stir deposited (FSD) materials were examined. The AA2011-T6 bars were deposited at a constant rotation rate of 1200 rpm and different feeding speeds of 3, 6, and 9 mm/min, whereas the AA2011-O bars were deposited at a constant rotation rate of 200 mm/min and varied feeding speeds of 1, 2, and 3 mm/min. The obtained microstructure was investigated using an optical microscope and scanning electron microscope equipped with EDS analysis to evaluate microstructural features. Hardness was also assessed as average values and maps. The results showed that this new technique succeeded in producing sound additive manufactured parts at all the applied processing parameters. The microstructures of the additive manufactured parts showed equiaxed refined grains compared to the coarse grain of the starting materials. The detected intermetallics in AA2011 alloy are mainly Al₂Cu and Al₇Cu₂Fe. The improvement in hardness of AA2011-O AMPs reached 163% of the starting material hardness at the applied feeding speed of 1 mm/min. The hardness mapping analysis reveals a homogeneous hardness profile along the building direction. Finally, it can be said that the temper conditions of the starting AA2011 materials govern the selection of the processing parameters in terms of rotation rate and feeding speed and affects the properties of the produced additive manufactured parts in terms of hardness and microstructural features.

In the current work, mild steel used in shipbuilding applications was friction-stir-welded (FSWed) with the aim of investigating the microstructure and mechanical properties of the FSWed joints. Mild steel of 5 mm thickness was friction-stir-welded at a constant tool rotation rate of 500 rpm and two different welding speeds of 20 mm/min and 50 mm/min and 3° tool tilt angle. The microstructure of the joints was investigated using optical and scanning electron microscopes. Additionally, the grain structure and crystallographic texture of the nugget (NG) zone of the FSWed joints was investigated using electron backscattering diffraction (EBSD). Furthermore, the mechanical properties were investigated using both tensile testing and hardness testing. The microstructure of the low-welding-speed joint was found to consist of fine-grain ferrite and bainite (acicular ferrite) with an average grain size of 3 µm, which indicates that the temperature experienced above A1, where a ferrite and austenite mixture is formed, and upon cooling, the austenite transformed into bainite. The joint produced using high welding speed resulted in a microstructure consisting mainly of polygonal ferrite and pearlite. This could be due to the temperature far below A1 experienced during FSW. In terms of joint efficiency expressed in terms of relative ultimate tensile, the stress of the joint to the base material was found to be around 92% for the low-speed joint and 83% for the high-welding-speed joint. A reduction in welding was attributed to the microstructure, as well as the microtunnel defect formed near the advancing side of the joint. The tensile strain was preserved at 18% for low welding speed and increased to 24% for the high welding speed. This can be attributed to the NG zone microstructural constituents. In terms of crystallographic texture, it is dominated by a simple shear texture, with increased intensity achieved by increasing the welding speed. In both joints, the hardness was found to be significantly increased in the NG zone of the joints, with a greater increase in the case of the low-welding-speed joint. This hardness increase is mainly attributed to the fine-grained structure formed after FSW.

The current research designed a statistical model for the bobbin tool friction stir processing (BT-FSP) of AA1050 aluminum alloy using the Response Surface Method (RSM). The analysis studied the influence of tool travel speeds of 100, 200, and 300 mm/min and different pin geometries (triangle, square, and cylindrical) at a constant tool rotation speed (RS) of 600 rpm on processing 8 mm thickness AA1050. The developed mathematical model optimizes the effect of the applied BT-FSP parameters on machine torque, processing zone (PZ) temperature, surface roughness, hardness values, and ultimate tensile strength (UTS). The experimental design is based on the Face Central Composite Design (FCCD), using linear and quadratic polynomial equations to develop the mathematical models. The results show that the proposed model adequately predicts the responses within the processing parameters, and the pin geometry is the most influential parameter during the BT-FSP of AA1050. The analysis of variance exhibit that the developed mathematical models can effectively predict the values of the machine torque, PZ temperature, surface roughness, hardness, and UTS with a confidence level of over 95% for the AA1050 BT-FSP. The optimization process shows that the optimum parameters to attain the highest mechanical properties in terms of hardness and tensile strength at the lowest surface roughness and machine torque are travel speed (TS) of 200 mm/min using cylindrical (Cy) pin geometry at the constant RS of 600 rpm. The PZ temperature of the processed specimens decreased with increasing TS at different pin geometries. Meanwhile, the surface roughness of the processed passes and machine torque increased with increasing the TS at different pin geometries. Increasing TS from 100 to 300 mm/min increases the hardness values of the processed materials using different pin geometries. The highest UTS of 79 MPa for the processed specimens was attained at the TS of 200 mm/min and RS of 600 rpm using the Cy pin geometry.

In the current investigation, additive friction stir-deposition (AFS-D) of as-cast hypoeutectic A356 Al alloy was conducted. The effect of feeding speeds of 3, 4, and 5 mm/min at a constant rotational speed of 1200 rpm on the macrostructure, microstructure, and hardness of the additive manufacturing parts (AMPs) was investigated. Various techniques (OM, SEM, and XRD) were used to evaluate grain microstructure, presence phases, and intermetallics for the as-cast material and the AMPs. The results showed that the friction stir deposition technique successfully produced sound additive manufactured parts at all the applied feeding speeds. The friction stir deposition process significantly improved the microstructure of the as-cast alloy by eliminating porosity and refining the dendritic α-Al grains, eutectic Si phase, and the primary Si plates in addition to intermetallic fragmentation. The mean values of the grain size of the produced AMPs at the feeding speeds of 3, 4, and 5 mm/min were 0.62 ± 0.1, 1.54 ± 0.2, and 2.40 ± 0.15 µm, respectively, compared to the grain size value of 30.85 ± 2 for the as-cast alloy. The AMPs exhibited higher hardness values than the as-cast A356 alloy. The as-cast A356 alloy showed highly scattered hardness values between 55 and 75.8 VHN. The AMP fabricated at a 3 mm/min feeding speed exhibited the maximum hardness values between 88 and 98.1 VHN.

Friction stir spot welding (FSSW) is one of the important variants of the friction stir welding (FSW) process. FSSW has been developed mainly for automotive applications where the different thickness sheets spot welding is essential. In the present work, different thin thickness sheets (1 mm and 2 mm) of AA6082-T6 were welded using FSSW at a constant dwell time of 3 s and different rotation speeds of 400, 600, 800, and 1000 rpm. The FSSW heat input was calculated, and the temperature cycle experience during the FSSW process was recorded. Both starting materials and produced FSSW joints were investigated by macro- and microstructural investigation, a hardness test, and a tensile shear test, and the fractured surfaces were examined using a scanning electron microscope (SEM). The macro examination showed that defect-free spot joints were produced at a wide range of rotation speeds (400–1000 rpm). The microstructural results in terms of grain refining of the stir zone (SZ) of the joints show good support for the mechanical properties of FSSW joints. It was found that the best welding condition was 600 rpm for achieving different thin sheet thicknesses spot joints with the SZ hardness of 95 ± 2 HV0.5 and a tensile shear load of 4300 ± 30 N.

This work investigates the feasibility of using friction stir welding (FSW) process as a groove filling welding technique to weld duplex stainless steel (DSS) that is extensively used by petroleum service companies and marine industries. For the FSW experiments, three different groove geometries without root gap were designed and machined in a DSS plates 6.5 mm thick. FSW were carried out to produce butt-joints at a constant tool rotation rate of 300 rpm, traverse welding speed of 25 mm/min, and tilt angle of 3^o using tungsten carbide (WC) tool. For comparison, the same DSS plates were welded using gas tungsten arc welding (GTAW). The produced joints were evaluated and characterized using radiographic inspection, optical microscopy, and hardness and tensile testing. Electron back scattering diffraction (EBSD) was used to examine the grain structure and phases before and after FSW. The initial results indicate that FSW were used successfully to weld DSS joints with different groove designs with defect-free joints produced using the 60° V-shape groove with a 2 mm root face without root gap. This friction stir welded (FSWed) joint was further investigated and compared with the GTAW joint. The FSWed joint microstructure mainly consists of α and γ with significant grain refining; the GTWA weld contains different austenitic-phase (γ) morphologies such as grain boundary austenite (GBA), intragranular austenite precipitates (IGA), and Widmanstätten austenite (WA) besides the ferrite phase (α) in the weld zone (WZ) due to the used high heat input and 2209 filler rod. The yield strength, ultimate tensile strength, and elongation of the FSWed joint are enhanced over the GTAW weldment by 21%, 41%, and 66% and over the BM by 65%, 33%, and 54%, respectively. EBSD investigation showed a significant grain refining after FSW with grain size average of 1.88 µm for austenite and 2.2 µm for ferrite.