To evaluate the effects of industrial by-products materials on the performance of porous concrete for plant growth, this study investigated the physical, strength, and freeze/thaw resistances of porous concrete for plant growth, prepared by replacing cement with blast furnace slag powder at 60% by weight, and replacing natural stone aggregates with coarse blast furnace slag aggregates at rates of 0%, 20%, 40%, 60% and 100% by weight. In addition, the effects of adding natural jute fiber and styrene butadiene (SB) latex to these concrete mixtures were evaluated. The void ratio, compressive strength, and freeze/thaw resistance of the samples were measured. With increasing replacement rate of blast furnace aggregates, addition of latex, and mixing of natural jute fiber the void ratio of the concrete was increased. Compressive strength decreased as the replacement rate of blast-furnace slag aggregates increased. The compressive strength decreased after 100 freeze/thaw cycles, regardless of the replacement rate of blast furnace slag aggregates or of the addition of natural jute fiber and latex. The addition of natural jute fiber and latex decreased the compressive strength after 100 freeze/thaw cycles. The test results indicate that the control mixture satisfied the target compressive strength of 10 MPa and the target void ratio of 25% at replacement rates of 0% and 20% for blast furnace aggregates, and that the mixtures containing latex satisfied the criteria up to an aggregate replacement rate of 60%. However, the mixtures containing natural jute fiber did not satisfy these criteria. The relationship between void ratio and residual compressive strength after 100 freeze/thaw cycles indicates that the control mixture and the mixtures containing jute fiber at aggregate replacement rates of 20% and 40% satisfied the target void ratio of 25% and the target residual compressive strength of over 80% after 100 freeze/thaw cycles. The mixtures containing latex and aggregate replacement rates up to 60% satisfied the target void ratio and compressive strength.

The purpose of this study is to investigate porous vegetation concrete formed using the industrial by-products blast furnace slag powder and blast furnace slag aggregates. We investigated the void ratio, compressive strength, freeze–thaw resistance, plant growth and water purification properties using concretes containing these by-products, natural jute fiber and latex. The target performance was a compressive strength of ≥12 MPa, a void ratio of ≥25% and a residual compressive strength of ≥80% following 100 freeze–thaw cycles. Using these target performance metrics and test results for plant growth and water purification, an optimal mixing ratio was identified. The study characterized the physical and mechanical properties of the optimal mix, and found that the compressive strength decreased compared with the default mix, but that the void ratio and the freeze–thaw resistance increased. When latex was used, the compressive strength, void ratio and freeze–thaw resistance all improved, satisfying the target performance metrics. Vegetation growth tests showed that plant growth was more active when the blast furnace slag aggregate was used. Furthermore, the use of latex was also found to promote vegetation growth, which is attributed to the latex forming a film coating that suppresses leaching of toxic components from the cement. Water purification tests showed no so significant differences between different mixing ratios; however, a comparison of mixes with and without vegetation indicated improved water purification in terms of the total phosphorus content when vegetation had been allowed to grow.

Global optimization methods linked with simulation models are widely used for automated calibration and serve as useful tools for searching for cost-effective alternatives for environmental management. A genetic algorithm (GA) and shuffled complex evolution (SCE-UA) algorithm were linked with the Long-Term Hydrologic Impact Assessment (L-THIA) model, which employs the curve number (SCS-CN) method. The performance of the two optimization methods was compared by automatically calibrating L-THIA for monthly runoff from 10 watersheds in Indiana. The selected watershed areas ranged from 32.7 to 5844.1 km². The SCS-CN values and total five-day rainfall for adjustment were optimized, and the objective function used was the Nash-Sutcliffe value (NS value). The GA method rapidly reached the optimal space until the 10th generating population (generation), and after the 10th generation solutions increased dispersion around the optimal space, called a cross hair pattern, because of mutation rate increase. The number of looping executions influenced the performance of model calibration for the SCE-UA and GA method. The GA method performed better for the case of fewer loop executions than the SCE-UA method. For most watersheds, calibration performance using GA was better than for SCE-UA until the 50th generation when the number of model loop executions was around 5150 (one generation has 100 individuals). However, after the 50th generation of the GA method, the SCE-UA method performed better for calibrating monthly runoff compared to the GA method. Optimized SCS-CN values for primary land use types were nearly the same for the two methods, but those for minor land use types and total five-day rainfall for AMC adjustment were somewhat different because those parameters did not significantly influence calculation of the objective function. The GA method is recommended for cases when model simulation takes a long time and the model user does not have sufficient time for an optimization program to search for the best values of calibration parameters. For other cases, the SCE-UA program is recommended for automatic model calibration.

The purpose of this study was to evaluate the performance of porous vegetation concrete block made from blast furnace slag cement containing industrial by-products such as blast furnace slag aggregate and powder. The blocks were tested for void ratio, compressive strength and freeze-thaw resistance to determine the optimal mixing ratio for the porous vegetation block. An economic analysis of the mixing ratio showed that the economic efficiency increased when blast furnace slag aggregate and cement were used. Porous vegetation concrete blocks for river applications were designed and produced. Hydraulic safety, heavy metal elution and vegetation tests were completed after the blocks were applied in the field. The measured tractive force ranged between 7.0 kg/m² for fascine revetment (vegetation revetment) and 16.0 kg/m² for stone pitching (hard revetment), which ensured sufficient hydraulic stability in the field. Plant growth was measured after the porous vegetation concrete block was placed in the field. Seeds began to sprout one week after seeding; after six weeks, the plant length exceeded 300 mm. The average coverage ratio reached as high as 90% after six weeks of vegetation. These results clearly indicated that the porous vegetation concrete block was suitable for environmental restoration projects.

This study evaluated the effects of reinforcement fibers on the mechanical characteristics, chloride ion penetration properties and abrasion resistance of roller-compacted latex-modified fiber-reinforced rapid-hardening-cement concrete (RCLMFRRHCC) for use in the emergency repair of concrete pavements. The reinforcement fibers tested included macro synthetic fibers (a structural fiber) as well as PVA (polyvinyl alcohol) and natural Jute fibers (non-structural fibers). In the experiment, compressive strength, flexural strength, splitting tensile strength, chloride ion penetrating properties, abrasion resistance tests and impact resistance tests were performed. Test results were compared with traffic open standards of concrete for concrete pavement emergency repair. RCLMFRRHCC satisfied all traffic open standards for concrete emergency repair. Mixes with reinforcement fibers showed superior results to the mix without, in terms of compressive strength, flexural strength, splitting tensile strength, chloride ion penetration resistance, abrasion resistance and impact resistance. With regard to the reinforcement fibers, the compressive strength, flexural strength, splitting tensile strength, and impact resistance of the mix with macro synthetic fiber showed improved results as a structural fiber compared to mixes containing natural jute and PVA fibers, namely the non-structural fibers. However, using the reinforcement fiber type had little effect on chloride ion penetration resistance or abrasion resistance. Thus, the addition of reinforcement fibers was effective in improving the performance of RCLMFRRHCC. The use of macro synthetic fibers improved the mechanical characteristics of concrete.