This paper presents the results of laser welding of dissimilar joints, where low-carbon and stainless steels were welded inthe lap joint configuration. Performed welding of austenitic and ferritic-pearlitic steels included a sealed joint, where only partial penetration of lower material was obtained.The authors presented acomparative study of the joints under different configurations. The welding parameters for the assumed penetration were estimated via anumericalsimulation. Moreover, a stress–strain analysis was performed based on theestablished model. Numerical analysis showed significant differences in joint properties, therefore, further study was conducted. Investigation of the fusion mechanism in the obtained joints wascarried out using electron dispersive spectroscopy (EDS) and metallurgical analysis. The study of the lap joint under different configurations showed considerable dissimilarities in stress–strain distribution and relevant differences in the fusion zone structure. The results showed advantages of using stainless steel as the upper material of a microstructure, and uniform chemical element distribution and stress analysis is considered.

This article presents the results of research on the technology and peripheral properties of laser-welded micro-couplings. The aim of this research was to determine the characteristics of properly made joints and to indicate the range of optimal parameters of the welding process. Thin-walled AISI 316L steel pipes with diameters of 1.5 and 2 mm used in medical equipment were tested. The micro-welding process was carried out on a SISMA LM-D210 Nd:YAG laser. The research methods used were macroscopic and microscopic analyses of the samples, and assessment of the distribution of elements in the weld, the distribution of microhardness and the tear strength of the joint. As a result of the tests, the following welding parameters are recommended: a pulse energy of 2.05 J, pulse duration of 4 ms and frequency of 2 Hz, beam focusing to a diameter of 0.4 mm and a rotation speed of 0.157 rad/s. In addition, the tests show good joint properties with a strength of more than 75% of the thinner pipe, uniform distribution of alloying elements and a complex dendritic structure characteristic of pulse welding.

The article indicates the impact of the laser beam trajectory on the effect of interaction on material during the laser milling process, which is not often mentioned in scientific reports. The article presents the results of an experiment consisting in random cellular scanning method. For this purpose, an original system of random surface scanning was developed and tested. The processed area was divided into finite unit cells, which were once, randomly processed with a laser beam. The procedure was repeated for subsequent scanning processes. The article focuses on determining and comparing Ra and Sa roughness parameter values for random cellular scanning strategy during changes of number of processed layers. The micromachining process was performed using a laser device with UV picosecond pulses.