During the investigations, functionalization of graphene oxide synthesized using modified Hummers’ method and its reduced form was performed. Mixtures of graphene oxide and reduced graphene oxide with pimelic acid and calcium hydroxide were prepared for functionalization. During the reaction, the molecules of pimelic acid were attached to the surface of graphene sheets. By forming links between the carboxylic groups of pimelic acid and graphene oxide, the durable connection was achieved. The functionalized graphene oxide and the reduced graphene oxide were used as additives in isotactic polypropylene crystallization. The influence of additives on crystallisation in non-isothermal conditions was examined using polarized optical microscopy and differential scanning calorimetry. The effect of the additives on the polypropylene structure was analysed using wide-angle X-ray scattering. For both functionalized compounds, the nucleating ability towards β-form of polypropylene was detected. Both additives showed the increase in the nucleation rate and promotion of growth of the β-form crystals. Nucleation efficiency similar to other nucleating agents used in the crystallization of the β-form of polypropylene was revealed.

Innovative geotextiles built from meandrically arranged thick ropes were produced. For the production of the geotextiles, the strips of woollen nonwoven were used. The segments of the geotextiles were installed on the bank of a drainage ditch. The behaviour of the geotextiles during 1 year was observed. It was demonstrated that the geotextiles installed in the ditch provide immediate protection of the bank. In the soil-covered wool, the process of slow biodegradation was initiated. Because of a low biodegradation rate at the end of the growing season, when the protective vegetation was not well developed, the geotextiles maintained their protective potential. In the following months, the biodegradation led to further destruction of wool fibres. During the biodegradation, the organic compounds rich in nitrogen were released into the soil. In spring, at the beginning of new growing season, the compounds acted as effective fertilizers, promoting the growth of protective vegetation. The vegetation growing on the bank provided an effective protection and took over the protective function of the geotextiles.

Graphene and its derivatives, such as graphene oxide (GO) or reduced graphene oxide (rGO), due to their properties, have been enjoying great interest for over two decades, particularly in the context of additive manufacturing (AM) applications in recent years. High-impact polystyrene (HIPS) is a polymer used in 3D printing technology due to its high dimensional stability, low cost, and ease of processing. However, the ongoing development of AM creates the need to produce modern feedstock materials with better properties and functionality. This can be achieved by introducing reduced graphene oxide into the polymer matrix. In this study, printable composite filaments were prepared and characterized in terms of morphology and thermal and mechanical properties. Among the obtained HIPS/rGO composites, the filament containing 0.5 wt% of reduced graphene oxide had the best mechanical properties. Its tensile strength increased from 19.84 to 22.45 MPa, for pure HIPS and HIPS-0.5, respectively. Furthermore, when using the HIPS-0.5 filament in the printing process, no clogging of the nozzle was observed, which may indicate good dispersion of the rGO in the polymer matrix.