Asphalt binders have been modified with Crumb rubber (CR) as an effort to fulfil the demand for the development of eco-friendly and sustainable pavements. The objective of this study was to investigate the high temperature rheological behaviors and fatigue performance of crumb rubber modified asphalt (CRMA) binder activated using trans-polyoctenamer (TOR). Long-term and short-term aging tests were performed on samples by thin film oven test (TFOT) and pressure aging vessel (PAV). Rotational viscosity (RV), softening point, and dynamic shear rheometer (DSR) tests were conducted to characterize the rheological and physical performance. A linear amplitude sweep (LAS) test was employed to evaluate the fatigue performance. The results show that TOR-activated CRMA is more capable of hardening the matrix bitumen and improving its high-temperature viscoelastic properties after TFOT. The high temperature viscoelasticity is significantly better than styrene-butadiene-styrene block (SBS) modified asphalt (SBSMA) and CRMA. TOR-activated CRMA exhibits strong rutting resistance, but it is more likely to generate fatigue cracks under the violent advancement of complex modulus. Therefore, TOR active agent has a negative impact on the fatigue performance of CRMA. SBSMA exhibited superior fatigue resistance. The viscosity temperature index (VTS) of TOR-activated CRMA and CRMA was basically identical; the TOR did not significantly improve the temperature sensitivity of CRMA.

To obtain a crumb rubber asphalt mixture with excellent performance, this study combined trans-polyoctenamer rubber (TOR), crumb rubber, and other additives to establish a new type of crumb rubber (CRT). The objective of this study was to design and evaluate the road performance of the new type of crumb rubber asphalt mixture (CRTAM) with a skeleton dense texture through a dry process. First, the skeleton intrusion compact volume method was used to optimize the grading of coarse and fine aggregates, and the design of the CRTAM gradation was carried out through the same and unequal volume replacement grading method. Then, three types of road performance were analyzed: high-temperature stability, low-temperature crack resistance, and water stability. The results showed that 2% and 2.5% CRT met a low-temperature index with equal volume substitution, and the six gradations obtained by unequal volume replacement with 2% CRT complied with the requirements of a skeleton dense texture. When the substitution ratio was 1.5 and 0.5, the high-temperature performance was better. In addition, when the substitution ratio was 0.5, the flexural strain energy density was the highest and the low-temperature performance was the best. Including considerations of economic benefits, it is recommended that the CRT content be 2% and the substitution ratio be 0.5.

The dynamic stability of a rutting test does not optimally reflect the high-temperature stability of asphalt mixtures. In this study, a rutting test was performed over a long duration (4 h) at different temperatures (40, 50, 60, 70 °C) for three asphalt mixtures, namely, matrix AC-16, SMA-16, and modified AC-16 asphalt mixtures. Subsequently, the temperature rutting rate was obtained after considering the annual temperature conditions of Guangdong and Beijing in China. Because the conditions of the rutting test were different from that of the actual pavement, the rut depth was calculated using a modified temperature rutting rate. This modification considered four factors: wheel trace distribution, temperature, pavement thickness, and loading rate. The calculation of the temperature rutting rate considered the climatic conditions and utilized the rutting deformation data from hour 1–4 of the rutting tests, during which the asphalt mixture was in a stable creep period. Thus, the high-temperature stability of the asphalt mixture was reflected more scientifically by the temperature rutting rate than the dynamic stability. The high-temperature rut-resistance of the asphalt mixture was found to improve significantly after the introduction of two additives (anti-rutting agent and lignin fiber). The modified formula for rut depth can realistically predict the annual rutting depth for three asphalt mixtures in a one-way driving pavement.