As a renewable biomass resource, biochar is new to modify or replace asphalt binder in pavement engineering. This paper focuses on the effect of biochar on the anti-aging performance of asphalt binder. The short- and long-term aging properties of biochar modified asphalt binder were investigated using dynamic shear rheometer (DSR) and bending beam rheometer (BBR) tests. The modification mechanism was investigated through the Fourier-transform infrared spectroscopy (FTIR) test. The aging tests and viscosity analysis showed that the softening point of biochar modified asphalt binder was higher than base asphalt binder, while the aging index and aging viscosity ratio were lower than base asphalt binder. After aging, the temperature sensitivity of biochar modified asphalt binder decreased and the high-temperature stability, reflected by dynamic shear modulus and resistance to rutting, improved. The BBR test after long-term aging showed that the anti-aging performance of biochar modified asphalt binder decreased with the decrease in temperature, and control of the biochar content could ensure good low-temperature performance of the modified asphalt binder after aging. FTIR spectra analysis showed that biochar in modified asphalt binder is physically blended with asphalt binder.

To obtain a crumb rubber asphalt mixture with excellent performance, this study combined trans-polyoctenamer rubber (TOR), crumb rubber, and other additives to establish a new type of crumb rubber (CRT). The objective of this study was to design and evaluate the road performance of the new type of crumb rubber asphalt mixture (CRTAM) with a skeleton dense texture through a dry process. First, the skeleton intrusion compact volume method was used to optimize the grading of coarse and fine aggregates, and the design of the CRTAM gradation was carried out through the same and unequal volume replacement grading method. Then, three types of road performance were analyzed: high-temperature stability, low-temperature crack resistance, and water stability. The results showed that 2% and 2.5% CRT met a low-temperature index with equal volume substitution, and the six gradations obtained by unequal volume replacement with 2% CRT complied with the requirements of a skeleton dense texture. When the substitution ratio was 1.5 and 0.5, the high-temperature performance was better. In addition, when the substitution ratio was 0.5, the flexural strain energy density was the highest and the low-temperature performance was the best. Including considerations of economic benefits, it is recommended that the CRT content be 2% and the substitution ratio be 0.5.

The dynamic stability of a rutting test does not optimally reflect the high-temperature stability of asphalt mixtures. In this study, a rutting test was performed over a long duration (4 h) at different temperatures (40, 50, 60, 70 °C) for three asphalt mixtures, namely, matrix AC-16, SMA-16, and modified AC-16 asphalt mixtures. Subsequently, the temperature rutting rate was obtained after considering the annual temperature conditions of Guangdong and Beijing in China. Because the conditions of the rutting test were different from that of the actual pavement, the rut depth was calculated using a modified temperature rutting rate. This modification considered four factors: wheel trace distribution, temperature, pavement thickness, and loading rate. The calculation of the temperature rutting rate considered the climatic conditions and utilized the rutting deformation data from hour 1–4 of the rutting tests, during which the asphalt mixture was in a stable creep period. Thus, the high-temperature stability of the asphalt mixture was reflected more scientifically by the temperature rutting rate than the dynamic stability. The high-temperature rut-resistance of the asphalt mixture was found to improve significantly after the introduction of two additives (anti-rutting agent and lignin fiber). The modified formula for rut depth can realistically predict the annual rutting depth for three asphalt mixtures in a one-way driving pavement.