In this paper, self-healing microcapsules were prepared by using melamine–formaldehyde (MF) resin as the wall material and shellac as the core material repairing agent. In order to explore the effect of the four factors (i.e., the HLB value of emulsifier, the type of solvent, the mass ratio of shellac to rosin, and the rate of rotating) on the comprehensive performance of microcapsules, and orthogonal experiments with four factors and three levels were carried out. The results showed that the hydrophilic lipophilic balance (HLB) value of the emulsifier was the most important influencing factor. In order to further explore the relationship between the HLB value of the emulsifier and the morphology of the microcapsules and the coating rate as well as to further optimize the performance of the microcapsules, taking the HLB value of the emulsifier as the single factor variable, single-factor tests were carried out. The results showed that when the HLB value was 12.56, the microcapsules of melamine–formaldehyde resin-coated shellac–rosin mixture had a uniform distribution and high coating rate. In order to explore the self-healing properties of waterborne coatings with microcapsules, the microcapsules prepared by single-factor experiments were mixed into the waterborne coatings at mass ratios of 0%, 3.0%, 6.0%, 9.0%, 12.0%, and 15.0%. It showed that the elongation at break of the waterborne coating with the addition of 3.0% microcapsule at mass fraction was improved, and it had a higher repair rate. This study provides a new research idea for the optimization and characterization of the self-healing properties of waterborne coatings.

Microcapsules were prepared by in situ polymerization with urea formaldehyde resin as the wall material and Dulux waterborne acrylic acid as the core material. The effects of the core–wall ratio, water bath temperature and depositing time on the morphology, particle size, yield and encapsulation ratio of microcapsules were investigated by orthogonal experiment of three factors and two levels. The results showed that the core–wall ratio had the greatest influence on the performance of microcapsules. When the core–wall ratio was 0.58:1, the water bath temperature was 70 °C, and the depositing time was 5 d, the microcapsule performance was the best. With the increase in depositing time, the yield of microcapsule particles increased gradually, and the microcapsules appeared to show an adhesive phenomenon. However, the long-term depositing time did not lead to complete deposition and agglomeration of microcapsules. When 10.0% concentration of the waterborne acrylic microcapsules with 0.58:1 of core–wall ratio was added to the coatings, the mechanical and optical properties of the coatings did not decrease significantly, but the elongation at break increased significantly. Therefore, this study offers a new prospect for using waterborne acrylic microcapsules to improve the toughness of waterborne paint film which can be cured at room temperature on a wood surface.

In order to explore the applicability of the waterborne coating with self-repairing microcapsules based on the surface of wood boards and specify the optimal range of microcapsule content in the coating, three different kinds of shellac microcapsules (transparent shellac, purple shellac, and yellow shellac) were embedded in a waterborne acrylic coating at 0, 1.5 wt.%, 3.0 wt.%, 4.5 wt.%, 6.0 wt.%, and 7.5 wt.%. The Beli wood (Paraberlinia bifoliolata) boards were then covered with self-repairing coatings to investigate the self-repairing coating’s physical and chemical properties, aging resistance, and scratch repair abilities. The findings demonstrated that the chromatic difference and gloss of surface coatings on Beli wood boards were significantly influenced by the content of microcapsules. The optical characteristics and cold liquid resistance performance of the coating on Beli wood were enhanced when the microcapsule content was 3.0 wt.%. Additionally, the mechanical qualities of the coating with 3.0 wt.% transparent shellac microcapsules on Beli wood surface were better, with an H hardness, grade 2 adhesion, and 8 kg·cm of impact strength. The studies on scratch repairing and aging resistance indicated that microcapsules helped to slow down the coating’s damage and retard aging. After a microcrack appeared, the waterborne coating with microcapsules on Beli wood’s surface had the capacity to repair itself. After aging, the coating with 3.0 wt.% transparent shellac microcapsule on Beli wood boards had a better performance on the comprehensive properties, with a 28.9% light loss rate and a 6 kg·cm impact resistance. It also had a 25.0% repairing rate in scratch width after being damaged for 5 d. This study advances the development of self-healing waterborne coatings on the wood board with shellac microcapsules by examining the effects of shellac in various colors and shellac microcapsule content in waterborne coatings.

Microcapsules of melamine formaldehyde-coated shellac and waterborne coating were prepared by in situ polymerization at 400, 600, 800 and 1000 rpm. The microcapsules prepared at four different stirring rates were added into the waterborne primer at a concentration of 5.0%, 10.0%, 15.0%, 20.0% and 25.0%. The effects of microcapsules prepared at different stirring rates and the concentration of microcapsules added into the paint film on the optical, mechanical and liquid resistance properties of the paint film were investigated. The results showed that the comprehensive performance of Tilia europaea L. waterborne primer film was the best when the concentration of microcapsules obtained at 600 rpm was 5.0%. On this basis, the aging resistance and self-healing performance of waterborne primer film on Tilia europaea L. with the best comprehensive performance were explored to lay the foundation for optimizing the preparation process of self-healing coating.

Embedding melamine-formaldehyde (MF) resin-coated shellac microcapsules in waterborne coatings can extend the service longevity of waterborne coatings on a wood surface to a certain extent. Due to the content limitation of self-repairing microcapsules in waterborne coatings, the effective self-healing performance time is short. With the aim of improving the self-repairing properties of self-repairing coatings on the surface of a Microberlinla sp substrate, a more effective self-healing mechanism was achieved by impregnating the ebony wood substrate several times with an MF resin-coated transparent shellac-rosin microcapsule emulsion. After the impregnation of the ebony boards with microcapsules, a waterborne acrylic resin coating containing 3.0 wt.% transparent shellac microcapsules was applied to the surface of the wood boards. The influence of the number impregnations on the surface coating’s physical properties, chemical properties, and self-repairing properties was explored. The results showed that the hardness of the surface coating on the ebony boards changed little under different numbers of impregnations. With the increasing number of impregnations, the surface coatings’ adhesion and impact strength slowly increased, the chromatic difference value was increased, and the roughness first increased and then decreased. Impregnating ebony boards with the microcapsule emulsion contributes to enhancing the aging resistance and repair performance of surface coatings on the ebony boards. When the number of impregnations was eight, the width change rate of cracks on surface self-healing coatings was 28.4%, which suggested the best repair performance among all samples. By impregnating the wood substrate with the self-healing microcapsule emulsion, the effect of the interaction between microcapsules and wood on the self-repairing properties of the surface coating was studied, contributing to the theory for further improving the self-repairing properties of waterborne coatings on wood surfaces and promoting the application and development of self-healing microcapsules.

Three kinds of melamine-formaldehyde (MF) microcapsules, containing transparent shellac, purple shellac, and yellow shellac as core curing agents, were synthesized via in situ polymerization, and then were embedded into the water-based acrylic resin coatings according to the concentrations of 0, 3.0%, 6.0%, 9.0%, 12.0%, and 15.0%, respectively, to obtain waterborne films with different microcapsule contents. The color of different shellacs was relevant to the color parameters of the self-healing waterborne film. The content of microcapsules was negatively correlated with the chromatic aberration of the surface of waterborne films. When the content of microcapsules was 0–6.0%, the chromatic aberration of waterborne films was relatively low. The content of microcapsules and the color of the different shellacs would affect the light transmittance of waterborne films. Among all samples, the light transmittance of the waterborne film containing 3.0% transparent shellac microcapsules was the highest. The microcapsules with different colors of shellac in waterborne films had different self-repairing effects. When the content of microcapsules did not exceed 6.0%, the tensile repair rate of the waterborne film containing yellow shellac encapsulated microcapsules was the highest, at 47.19%. The scratch experiment illustrated that the scratch width of the waterborne coating with yellow shellac microcapsules decreased most significantly, and the width change rate was 73.0% after 5 days. The coating containing the 3.0% yellow shellac microcapsule has the best comprehensive performance on optical and self-healing properties. Exploring the influence of shellac resin’s color and the microcapsules’ content on the waterborne film provides technical references for the application of shellac in waterborne coatings and contribute to the further development of the preparation process of self-healing coatings.