Thermochromic microcapsules were prepared with a thermochromic compound as core material and urea formaldehyde as wall material. The molar ratio of urea and formaldehyde, the mass ratio of core material to wall material, the concentration of emulsifier, and rotating speed were selected to make a four-level and three-factor L₉(3⁴) orthogonal test. It was found that the molar ratio of urea and formaldehyde had the greatest influence on the coating rate of microcapsules. The effects of molar ratio of urea and formaldehyde on the discoloration temperature and coating rate of microcapsules were studied. When the molar ratio of urea to formaldehyde was 1:1.6, the core material: wall material ratio was 4:7, the concentration of emulsifier was 5.0%, and the rotating speed was 1600 rpm, the performance of the microcapsules was the best. When the microcapsule content was 20.0%, the color difference of the paint film was the largest, the gloss and hardness of the paint film decreased with increasing microcapsule content, and the impact resistance of the paint film first increased and then decreased with increasing microcapsule content. The adhesion of the paint film remained unchanged, and was grade 1. When the microcapsule content was 20.0%, the performance of the paint film was at its best. This provides a basis for the application of thermochromic coatings.

Wood surface treatment aims to improve or reduce the surface activity of wood by physical treatment, chemical treatment, biological activation treatment or other methods to achieve the purpose of surface modification. After wood surface modification, the paint film adhesion performance, gluing performance, surface wettability, surface free energy and surface visual properties would be affected. This article aims to explore the effects of different modification methods on the adhesion of wood coating films. Modification of the wood surface significantly improves the adhesion properties of the paint film, thereby extending the service life of the coating. Research showed that physical external force modification improved the hydrophilicity and wettability of wood by changing its surface structure and texture, thus enhancing the adhesion of the coating. Additionally, high-temperature heat treatment modification reduced the risk of coating cracking and peeling by eliminating stress and moisture within the wood. Chemical impregnation modification utilized the different properties of organic and inorganic substances to improve the stability and durability of wood. Organic impregnation effectively filled the wood cell wall and increased its density, while inorganic impregnation enhanced the adhesion of the coating by forming stable chemical bonds. Composite modification methods combined the advantages of the above technologies and significantly improved the comprehensive properties of wood through multiple modification treatments, showing superior adhesion and durability. Comprehensive analysis indicated that selecting the appropriate modification method was key for different wood types and application environments.

The modification experiment of waterborne coating was carried out by adding microcapsules. The wall material of the microcapsule was urea-formaldehyde resin and the core material of the microcapsule was epoxy resin. Core material can improve the toughness of the coating and prevent the cracking of the coating. The influences of different contents of microcapsules and the order of adding microcapsules in the coating process on the properties of gloss, color difference and toughness were studied. The results showed that the gloss of the waterborne coating decreased with the increase of microcapsule content. The color difference of coating increased first and then decreased, and when the microcapsule content was 8.0%, the color difference was the largest. The toughness of the coatings also increased first and then decreased. When the content of the microcapsule was 10.0%, the toughness of the coating was significantly enhanced. When the microcapsules with a content of 10.0% were added to the waterborne coating, under the same process, the coating gloss of microcapsules added to the primer was relatively high, and the coating gloss was the highest when the coating process was three-layer primer and two-layer topcoat. The microcapsule had little effect on the color difference of coating in different coating processes. When the coating process was three-layer primer and three-layer topcoat, the coating toughness was the best when microcapsules were added to the topcoats. This study provides a basis for industrial application of waterborne coatings to enhance their toughness.

Through the optimized preparation of tung oil microcapsules, five kinds of microcapsules containing different core material content were obtained to explore the influence of microcapsules on water-based paint film and the self-healing ability of microcapsules. The results showed that the microcapsules had good appearance, and the microcapsules were successfully prepared. The color difference in the paint film increased with the increase in microcapsule content, and the gloss decreased gradually. The mechanical test showed that adding microcapsules increased the toughness of the paint film to a certain extent, and the performance of the paint film was unchanged or better. The results showed that paint film with the core–wall ratio of 0.78:1 had the best performance and self-healing function when microcapsules were added.

In this paper, a thermochromic complex was prepared from crystal violet lactone (CVL), bisphenol A (BPA) and tetradecanol. The color-changing temperature of the color-changing compound was found to be 25 °C by orthogonal experiment. Microcapsules coated with a thermochromic compound were added into alkyd resin at different mass concentrations. With the increase in temperature and mass fraction of microcapsules in the coating, the color difference of the coating showed an upward trend. The highest variation in the coating’s color difference occurs when there were 10% microcapsules. When the mass fraction of microcapsules was 15.0~25.0%, there was little change to the gloss of the coating. With the increase in the mass fraction of the coating microcapsules, the hardness of the coating gradually increased. The hardness was at its best when the microcapsule concentration was 25%. When the microcapsule concentration was 20%, the impact resistance of the coating was at its best. The coating had good cold-liquid resistance to acetic acid, ethanol, and NaCl solutions, and there was basically no mark on the coating surface before and after the cold-liquid-resistance test. The addition of microcapsules did not change the chemical composition of the coating, and it improved the performance of the coating. When the microcapsule concentration was 10%, the overall performance of the coating was at its best, which laid the technical foundation for thermochromic coating on the metal surface.

A waterborne ultraviolet (UV)-curing coating was prepared on the surface of wood materials with modification of talcum powder and calcium carbonate (CaCO₃). When the waterborne UV-curing coatings on the surface of wood materials (WUVCW) was radiated for 1 min by UV (λ = 365 nm) and dried at 40 °C for 10 min, it showed good hardness, adhesion, and impact strength, with controlling the talcum content of 2.0% and CaCO₃ content of 1.0%, respectively. When the content of talcum powder was higher than 2%, the mechanical properties and gloss of the WUVCW decreased, and when the talcum powder of WUVCW increase to more than 5%, a matte surface appeared after curing. When CaCO₃ and talcum powder were present at the same time, the mechanical properties of WUVCW were better than those of only CaCO₃ or talcum powder.