Undoped as well as (Co, Mn) co-doped Zinc oxides have been effectively developed on glass substrates, taking advantage of the spray pyrolysis procedure. The X-ray diffraction XRD as well as X-ray photoelectron spectroscopy (XPS) measurements have recognized a pure hexagonal wurtzite form of ZnO, and no other collateral phases such as MnO₂ or CoO₂ have been observed as a result of doping. The calculated values of the texture coefficient (TC) were between 0.15 and 5.14, indicating a dominant orientation along the (002) plane. The crystallite size (D) varies with the (Co, Mn) contents. The dislocation density (δ) as well as the residual microstrains increased after Co and Mn doping. Furthermore, the surface morphology of the films has been affected significantly by the Co and Mn incorporation, as shown by the scanning electron microscopy (SEM) investigation. The study of the optical properties exhibits a red shift of the band gap energy (E_g) with the (Co, Mn) co-doping. The magnetic measurements have shown that the undoped and (Co, Mn) co-doped ZnO thin films displayed room-temperature ferromagnetism (RTFM).

Synthesis and characterization of undoped and samarium-doped CuO–SnO₂:F thin films using the spray pyrolysis technique are presented. The effect of the samarium doping level on the physical properties of these films was thoroughly analyzed. X-ray diffraction patterns proved the successful synthesis of pure CuO–SnO₂:F thin films, free from detectable impurities. The smallest crystallite size was observed in 6% Sm-doped CuO–SnO₂:F thin films. The 6% Sm-doped CuO–SnO₂films demonstrated an increasedsurface area of 40.6 m²/g, highlighting improved textural properties, which was further validated by XPS analysis.The bandgap energy was found to increase from 1.90 eV for undoped CuO–SnO₂:F to 2.52 eV for 4% Sm-doped CuO–SnO₂:F, before decreasing to 2.03 eV for 6% Sm-doped CuO–SnO2:F thin films. Photoluminescence spectra revealed various emission peaks, suggesting a quenching effect. A numerical simulation of a new solar cell based on FTO/ZnO/Sm–CuO–SnO₂:F/X/Mo was carried out using Silvaco Atlas software, where X represented the absorber layer CIGS, CdTe, and CZTS. The results showed that the solar cell with CIGS as the absorber layer achieved the highest efficiency of 15.98. Additionally, the thin films demonstrated strong photocatalytic performance, with 6% Sm-doped CuO–SnO₂:F showing 86% degradation of ampicillin after two hours. This comprehensive investigation provided valuable insights into the synthesis, properties, and potential applications of Sm-doped CuO–SnO₂ thin films, particularly for solar energy and pharmaceutical applications.