In the present work, novel bicomponent polymeric hydrogels based on methacrylamide-modified gelatin (MAG) and 2-hydroxyethyl methacrylate (HEMA) have been prepared by cross-linking polymerization using photoinitiation. Five types of novel hydrogels have been prepared using different MAG/HEMA ratios between 1/0.5 and 1/10 w/w. Subsequently, porous scaffolds were obtained via a cryogenic treatment followed by freeze-drying. Physico-chemical measurements as well as in vitro degradation tests have been performed in order to correlate the material composition with the corresponding properties. Among the properties studied we have to mention the water uptake capacity, the rheological properties and the enzyme-mediated degradation behaviour. The results indicate that the HEMA content in the initial polymerization mixtures modulates the architecture of the porous scaffolds from straightforward, top-to-bottom oriented channels for hydrogels possessing the lowest HEMA content to a complex and dense internal porosity of the channels the case of higher HEMA loaded materials. While aiming at tissue engineering applications, it is important to notice that the covalently bound gelatin sequences significantly improve the biocompatibility of PHEMA based hydrogels.

Biocompatible methacrylamide-modified gelatin (GELMA) hydrogels with tuned characteristics, obtained through network-forming photopolymerization, have recently attracted increasing attention due to their wide range of possible applications such as drug release, tissue regeneration and generation of bioartificial implants. Due to the controlled number of CC bonds, GELMA may simultaneously act as macromonomer and crosslinker leading through polymerization to hydrogels with rationally designed performances. This study provides effortless one-pot synthesis of hybrid hydrogels based on covalently linked GELMA and polyacrylamide (PAA), using photo-induced network-forming polymerization. Conventional synthesis of similar hydrogels leads to interpenetrating gelatin and PAA networks, usually involving multistep crosslinking of the components and the use of toxic crosslinkers. Through the described one-pot chemistry, the synthetic water superabsorbent PAA with its well-recognized advantages can rationally benefit from the high biocompatibility and cell-adherence of GELMA in a simple covalent way. This work provides a correlation between the composition and the corresponding hydrogel properties (including swelling, pH influence, mechanical behaviour, ability to generate porous scaffolds, enzymatic degradation). The addition of PAA modulated the network density and the water affinity allowing the control of elasticity and degradability. Supplementary crosslinking of the synthetic component provided additional control over hydrophilicity. The capacity of such hydrogels to generate porous scaffolds was proved; interesting morphologies were developed only by varying the composition. In vitro cellular studies indicated that the presence of GELMA conferred controlled cell-affinity properties to the bicomponent hydrogels. Nevertheless, the drug release potential of such hydrogels was preliminarily investigated using sodium nafcillin. GELMA–PAA hydrogels may be useful for tissue regeneration due to effortless synthesis, compositional flexibility and variable properties.

Due to the reduced ability of most harmed tissues to self-regenerate, new strategies are being developed in order to promote self-repair assisted or not by biomaterials, among these tissue engineering (TE). Human adipose-derived mesenchymal stem cells (hASCs) currently represent a promising tool for tissue reconstruction, due to their low immunogenicity, high differentiation potential to multiple cell types and easy harvesting. Gelatin is a natural biocompatible polymer used for regenerative applications, while nanodiamond particles (NDs) are used as reinforcing nanomaterial that might modulate cell behavior, namely cell adhesion, viability, and proliferation. The development of electrospun microfibers loaded with NDs is expected to allow nanomechanical sensing due to local modifications of both nanostructure and stiffness. Two aqueous suspensions with 0.5 and 1% w/v NDs in gelatin from cold water fish skin (FG) were used to generate electrospun meshes. Advanced morpho- and micro-structural characterization revealed homogeneous microfibers. Nanoindentation tests confirmed the reinforcing effect of NDs. Biocompatibility assays showed an increased viability and proliferation profile of hASCs in contact with FG_NDs, correlated with very low cytotoxic effects of the materials. Moreover, hASCs developed an elongated cytoskeleton, suggesting that NDs addition to FG materials encouraged cell adhesion. This study showed the FG_NDs fibrous scaffolds potential for advanced TE applications.

This work proposes a simple method to obtain nanostructured hydrogels with improved mechanical characteristics and relevant antibacterial behavior for applications in articular cartilage regeneration and repair. Low amounts of silver-decorated carbon-nanotubes (Ag@CNTs) were used as reinforcing agents of the semi-interpenetrating polymer network, consisting of linear polyacrylamide (PAAm) embedded in a PAAm-methylene-bis-acrylamide (MBA) hydrogel. The rational design of the materials considered a specific purpose for each employed species: (1) the classical PAAm-MBA network provides the backbone of the materials; (2) the linear PAAm (i) aids the dispersion of the nanospecies, ensuring the systems’ homogeneity and (ii) enhances the mechanical properties of the materials with regard to resilience at repeated compressions and ultimate compression stress, as shown by the specific mechanical tests; and (3) the Ag@CNTs (i) reinforce the materials, making them more robust, and (ii) imprint antimicrobial characteristics on the obtained scaffolds. The tests also showed that the obtained materials are stable, exhibiting little degradation after 4 weeks of incubation in phosphate-buffered saline. Furthermore, as revealed by micro-computed tomography, the morphometric features of the scaffolds are adequate for applications in the field of articular tissue regeneration and repair.

Cartilage has limited regeneration potential. Thus, there is an imperative need to develop new strategies for cartilage tissue engineering (CTE) amenable for clinical use. Recent CTE approaches rely on optimal cell-scaffold interactions, which require a great deal of optimization. In this study we attempt to build a novel gelatin- (G-) alginate- (A-) polyacrylamide (PAA) 3D interpenetrating network (IPN) with superior performance in promoting chondrogenesis from human adipose-derived stem cells (hADSCs). We show that our G-A-PAA scaffold is capable of supporting hADSCs proliferation and survival, with no apparent cytotoxic effect. Moreover, we find that after exposure to prochondrogenic conditions a key transcription factor known to induce chondrogenesis, namely, Sox9, is highly expressed in our hADSCs/G-A-PAA bioconstruct, along with cartilage specific markers such as collagen type II, CEP68, and COMP extracellular matrix (ECM) components. These data suggest that our G-A-PAA structural properties and formulation might enable hADSCs conversion towards functional chondrocytes. We conclude that our novel G-A-PAA biomatrix is a good candidate for prospectivein vivoCTE applications.