Materials based on natural high molecular compounds are particularly interesting for biomedical applications. It is known that the cross-linking agent used for preparation of biomacromolecule-based materials is as important as used biopolymer. Therefore, natural cross-linkers containing reactive carbonyl groups are of great interest especially for modifying properties of natural polysaccharides. One of the most popular cross-linking agents is glutaraldehyde. Nevertheless, the unreacted particles can be released from the cross-linked material and cause cytotoxic effects. This can be eliminated when using a cross-linker based e.g., on polysaccharides. This article describes quick and efficient synthesis of dialdehyde chitosan (DACS) and its application for the preparation of chitosan films. Materials obtained with different amount of DACS were fully characterized in terms of structure and surface morphology. Thermal and mechanical properties as well as hydrophilic character were also examined. The results obtained were compared with the materials obtained by cross-linking chitosan with low molecular weight glutaraldehyde and high molecular weight cross-linking agent based on polysaccharide–dialdehyde starch. Toxicity of all obtained materials was tested using the Microtox^® test. It has been shown that due to better mechanical, thermal and surface properties as well as lower toxicity, dialdehyde chitosan is a very promising crosslinking agent.

Magnetite nanoparticles (Fe₃O₄ NPs) coated by modified chitosan (m-CS) rich of amino groups and its mixture with poly[N-benzyl-2-(methacryloxy)-N,N-dimethylethanaminium bromide] (PQ) with various mass ratios were prepared by co-precipitation method. The thermal stability of magnetic materials has been investigated by thermogravimetric analysis (TG/DTG/DTA) in air and nitrogen atmosphere. It was found that magnetic NPs coated by polymer blend were characterized by lower thermal stability than protected only by alone CS or m-CS. Magnetite NPs enhance thermooxidative degradation of polymers, however, the stable surface layer, formed from polymer degradation products, efficiently protects the magnetite transformation at higher temperatures. The content of magnetite in obtained systems has been also determined from TG curves.

Three different novel chitosan derivatives for medical or biotechnological applications have been successfully obtained by chemical modification of reactive amino and hydroxyl groups in chitosan chain. The modification has led to incorporation of different amount (one to three) of long-distanced amino and imine groups into each repeating unit. These highly functionalized chitosan derivatives were used as a matrix for magnetite nanoparticles. The thermal stability of all obtained chitosan materials has been determined using thermogravimetric analysis in oxidative and inert atmosphere. Chitosan containing two side substituents behaves differently from the other two, which is caused by the significant water uptake. Magnetite causes decrease in thermal stability of studied chitosan derivatives. The highest stability is observed for the nanocomposite obtained from chitosan with three side groups. The changes in the structure of the magnetite core have been observed above 600 °C in nitrogen. Due to the different competitive reactions occurring in the modified chitosan, the proposed mechanism of thermal degradation is very complex.

In this study, thin chitosan-gelatin biofilms cross-linked with dialdehyde cellulose nanocrystals for dressing materials were received. Two types of dialdehyde cellulose nanocrystals from fiber (DNCL) and microcrystalline cellulose (DAMC) were obtained by periodate oxidation. An ATR-FTIR analysis confirmed the selective oxidation of cellulose nanocrystals with the creation of a carbonyl group at 1724 cm⁻¹. A higher degree of cross-linking was obtained in chitosan-gelatin biofilms with DNCL than with DAMC. An increasing amount of added cross-linkers resulted in a decrease in the apparent density value. The chitosan-gelatin biofilms cross-linked with DNCL exhibited a higher value of roughness parameters and antioxidant activity compared with materials cross-linked with DAMC. The cross-linking process improved the oxygen permeability and anti-inflammatory properties of both measurement series. Two samples cross-linked with DNCL achieved an ideal water vapor transition rate for wound dressings, CS-Gel with 10% and 15% addition of DNCL—8.60 and 9.60 mg/cm²/h, respectively. The swelling ability and interaction with human serum albumin (HSA) were improved for biofilms cross-linked with DAMC and DNCL. Significantly, the films cross-linked with DAMC were characterized by lower toxicity. These results confirmed that chitosan-gelatin biofilms cross-linked with DNCL and DAMC had improved properties for possible use in wound dressings.

In this study potato and corn starch were subjected to oxidation, using sodium periodate, to obtain dialdehyde starch (DAS) containing different amount of aldehyde groups. The obtained modified starch samples have been characterized with chemical analysis, scanning electron microscopy (SEM) and ATR-FTIR spectroscopy. Then, the samples were exposed to polychromatic UV radiation and the course of photochemical reaction has been monitored with ATR-FTIR spectroscopy. The surface properties of the native and dialdehyde starch before and after UV-irradiation have been determined by contact angle measurements and calculation of surface free energy. The crystallinity of the samples has been estimated with X-ray diffraction (XRD). It has been proved that the dialdehyded corn starch contained a higher amount of functional groups was more photostable than the oxidized potato starch. Sodium iodide(V), firmly bound to DAS macromolecules, has been found to have a significant effect on the photooxidative degradation of the tested systems. In addition, the mechanism of photoinduced reactions in the dialdehyde starch has been proposed.

This study focuses on obtaining and characterizing novel chitosan-based biomaterials containing cannabis oil to potentially promote wound healing. The primary active substance in cannabis oil is the non-psychoactive cannabidiol, which has many beneficial properties. In this study, three chitosan-based films containing different concentrations of cannabis oil were prepared. As the amount of oil increased, the obtained biomaterials became rougher as tested by atomic force microscopy. Such rough surfaces promote protein adsorption, confirmed by experiments assessing the interaction between human albumin with the obtained materials. Increased oil concentration also improved the films' mechanical parameters, swelling capacity, and hydrophilic properties, which were checked by the wetting angle measurement. On the other hand, higher oil content resulted in decreased water vapour permeability, which is essential in wound dressing. Furthermore, the prepared films were subjected to an acute toxicity test using a Microtox. Significantly, the film's increased cannabis oil content enhanced the antimicrobial effect against A. fischeri for films in direct contact with bacteria. More importantly, cell culture studies revealed that the obtained materials are biocompatible and, therefore, they might be potential candidates for application in wound dressing materials.