Polymer flocculants are used to promote solid–liquid separation processes in potable water and wastewater treatment. Recently, bio-based flocculants have received a lot of attention due to their superior advantages over conventional synthetic polymers or inorganic agents. Among natural polymers, polysaccharides show many benefits such as biodegradability, non-toxicity, ability to undergo different chemical modifications, and wide accessibility from renewable sources. The following article provides an overview of bio-based flocculants and their potential application in water treatment, which may be an indication to look for safer alternatives compared to synthetic polymers. Based on the recent literature, a new approach in searching for biopolymer flocculants sources, flocculation mechanisms, test methods, and factors affecting this process are presented. Particular attention is paid to flocculants based on starch, cellulose, chitosan, and their derivatives because they are low-cost and ecological materials, accepted in industrial practice. New trends in water treatment technology, including biosynthetic polymers, nanobioflocculants, and stimulant-responsive flocculants are also considered.

Materials based on natural high molecular compounds are particularly interesting for biomedical applications. It is known that the cross-linking agent used for preparation of biomacromolecule-based materials is as important as used biopolymer. Therefore, natural cross-linkers containing reactive carbonyl groups are of great interest especially for modifying properties of natural polysaccharides. One of the most popular cross-linking agents is glutaraldehyde. Nevertheless, the unreacted particles can be released from the cross-linked material and cause cytotoxic effects. This can be eliminated when using a cross-linker based e.g., on polysaccharides. This article describes quick and efficient synthesis of dialdehyde chitosan (DACS) and its application for the preparation of chitosan films. Materials obtained with different amount of DACS were fully characterized in terms of structure and surface morphology. Thermal and mechanical properties as well as hydrophilic character were also examined. The results obtained were compared with the materials obtained by cross-linking chitosan with low molecular weight glutaraldehyde and high molecular weight cross-linking agent based on polysaccharide–dialdehyde starch. Toxicity of all obtained materials was tested using the Microtox^® test. It has been shown that due to better mechanical, thermal and surface properties as well as lower toxicity, dialdehyde chitosan is a very promising crosslinking agent.

Magnetite nanoparticles (Fe₃O₄ NPs) coated by modified chitosan (m-CS) rich of amino groups and its mixture with poly[N-benzyl-2-(methacryloxy)-N,N-dimethylethanaminium bromide] (PQ) with various mass ratios were prepared by co-precipitation method. The thermal stability of magnetic materials has been investigated by thermogravimetric analysis (TG/DTG/DTA) in air and nitrogen atmosphere. It was found that magnetic NPs coated by polymer blend were characterized by lower thermal stability than protected only by alone CS or m-CS. Magnetite NPs enhance thermooxidative degradation of polymers, however, the stable surface layer, formed from polymer degradation products, efficiently protects the magnetite transformation at higher temperatures. The content of magnetite in obtained systems has been also determined from TG curves.

The blends based on poly(lactic acid), (PLA) and polyacrylates (1:1 weight ratio) have been prepared by photopolymerization of three different multifunctional acrylate monomers (pentaerythritol triacrylate, pentaerythritol tetraacrylate and dipentaerythritol pentaacrylate) in matrix of linear PLA. The structure of these systems has been studied by Atomic Force Microscopy (AFM), Differential Scanning Calorimetry (DSC) and X-ray Diffraction (XRD). It was found that the blends are highly crosslinked, rough, heterogeneous and some of them – semicrystalline. The effect of UV-irradiation on surface morphology of obtained mixtures was studied. The viscometry has been applied for measurements of changes of PLA molecular weight resulting of photodegradation. It was shown that blends are much more photostable than pure PLA.