Five alumina-supported palladium catalysts have been prepared from a range of precursor compounds [palladium(II) nitrate, palladium(II) chloride, palladium(II) acetylacetonate, and tetraamminepalladium(II) tetraazidopalladate(II)] and at different metal loadings (1–7.3wt%). Collectively, this series of catalysts provides a range of metal particle sizes (1.2–8.5nm) that emphasize different morphological aspects of the palladium crystallites. The infrared spectra of chemisorbed CO applied under pulse-flow conditions reveal distinct groupings between metal crystallites dominated by low index planes and those that feature predominantly corner/edge atoms. Temperature-programmed infrared spectroscopy establishes that the linear CO band can be resolved into contributions from corner atoms and a combination of (111)∕(111) and (111)∕(100) particle edges. Propene hydrogenation has been used as a preliminary assessment of catalytic performance for the 1wt% loaded catalysts, with the relative inactivity of the catalyst prepared from palladium(II) chloride attributed to a diminished hydrogen supply due to decoration of edge sites by chlorine originating from the preparative process. It is anticipated that refinements linking the vibrational spectrum of a probe molecule with surface structure and accessible adsorption sites for such a versatile catalytic substrate provide a platform against which structure/reactivity relationships can be usefully developed.

Cobalt oxide Co3O4 has recently emerged as promising, noble metal-free catalyst for oxidation reactions but a better understanding of the active catalyst under working conditions is required for further development and potential commercialization. An operando approach has been applied, combining near ambient (atmospheric) pressure X-ray photoelectron spectroscopy (NAP-XPS), Fourier transform infrared spectroscopy (FTIR) or X-ray diffraction (XRD) with simultaneous catalytic tests of CO oxidation on Co3O4, enabling to monitor surface and bulk states under various reaction conditions (steady-state and dynamic conditions switching between CO and O2). Based on the surface-specific chemical information a complex network of different reaction pathways unfolded: Mars-van-Krevelen (MvK), CO dissociation followed by carbon oxidation, and formation of carbonates. A possible Langmuir–Hinshelwood (LH) pathway cannot be excluded because of the good activity when no oxygen vacancies were detected. The combined NAP-XPS/FTIR results are in line with a MvK mechanism above 100 oC, involving the Co3+/Co2+ redox couple and oxygen vacancy formation. Under steady state, the Co3O4 surface appeared oxidized and the amount of reduced Co2+ species at/near the surface remained low up to 200 °C. Only in pure CO, about 15% of surface reduction were detected, suggesting that the active sites are a minority species. The operando spectroscopic studies also revealed additional reaction pathways: CO dissociation followed by carbon reoxidation and carbonate formation and its decomposition. However, due to their thermal stability in various atmospheres, the carbonates are rather spectators and also CO dissociation seems a minor route. This study thus highlights the benefits of combining operando surface sensitive techniques to gain insight into catalytically active surfaces.

Metal-organic frameworks (MOFs) are commended as photocatalysts for H₂ evolution and CO₂ reduction as they combine light-harvesting and catalytic functions with excellent reactant adsorption capabilities. For dynamic processes in liquid phase, the accessibility of active sites becomes a critical parameter as reactant diffusion is limited by the inherently small micropores. Our strategy is to introduce additional mesopores by selectively removing one ligand in mixed-ligand MOFs via thermolysis. Here we report photoactive MOFs of the MIL-125-Ti family with two distinct mesopore architectures resembling either large cavities or branching fractures. The ligand removal is highly selective and follows a 2-step process tunable by temperature and time. The introduction of mesopores and the associated formation of new active sites have improved the HER rates of the MOFs by up to 500%. We envision that this strategy will allow the purposeful engineering of hierarchical MOFs and advance their applicability in environmental and energy technologies.

Any substantial move of energy sources from fossil fuels to renewable resources requires large scale storage of excess energy, for example via power to fuel processes. In this respect electrochemical reduction of CO2 may become very important, since it offers a method of sustainable CO production, which is a crucial prerequisite for synthesis of sustainable fuels. Carbon dioxide reduction in solid oxide electrolysis cells (SOECs) is particularly promising owing to the high operating temperature, which leads to both improved thermodynamics and fast kinetics. Additionally, compared to purely chemical CO formation on oxide catalysts, SOECs have the outstanding advantage that the catalytically active oxygen vacancies are continuously formed at the counter electrode, move to the working electrode where they reactivate the oxide surface without the need of a preceding chemical (e.g. by H2) or thermal reduction step. In the present work, the surface chemistry of (La,Sr)FeO3-δ and (La,Sr)CrO3-δ based perovskite-type electrodes was studied during electrochemical CO2 reduction by means of near ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) at SOEC operating temperatures. These measurements revealed the formation of a carbonate intermediate, which develops on the oxide surface only upon cathodic polarization (i.e. under sufficiently reducing conditions). The amount of these adsorbates increases with increasing oxygen vacancy concentration of the electrode material, thus suggesting vacant oxygen lattice sites as the predominant adsorption sites for carbon dioxide. The correlation of carbonate coverage and cathodic polarization indicates that an additional electron transfer is required to form the carbonate radical and thus to activate CO2 on the oxide surface. The results also suggest that acceptor doped oxides with high electron concentration and high oxygen vacancy concentration may be particularly suited for CO2 reduction. In contrast to water splitting, the CO2 electrolysis reaction was not significantly affected by metallic particles, which were exsolved from the perovskite electrodes upon cathodic polarization. Carbon formation on the electrode surface was only observed under very strong cathodic conditions and the carbon could be easily removed by retracting the applied voltage without damaging the electrode, which is particularly promising from an application point of view.