A radiative cooling device, based on a metamaterial able to mirror solar radiation and emit heat toward the universe by the transparency window of the atmosphere (8–13 µm), reaching and maintaining temperatures below ambient air, without any electricity input (passive), could have a significant impact on energy consumption of buildings and positive effects on the global warming prevention. A similar device is expected to properly work if exposed to the nocturnal sky, but during the daytime, its efficacy could be affected by its own heating under direct sunlight. In scientific literature, there are only few evidences of lab scale devices, acting as passive radiative cooling at daytime, and remaining few degrees below ambient air. This work describes the proof of concept of a daytime passive radiative cooler, entirely developed in ENEA labs, capable to reach well 12 °C under ambient temperature. In particular, the prototypal device is an acrylic box case, filled with noble gas, whose top face is a metamaterial deposited on a metal substrate covered with a transparent polymeric film. The metamaterial here tested, obtained by means of a semi-empirical approach, is a spectrally selective coating based on low cost materials, deposited as thin films by sputtering on the metallic substrate, that emits selectively in the 8–13 µm region, reflecting elsewhere UV_VIS_NIR_IR electromagnetic radiation. The prototype during the daytime sky could reach temperatures well beyond ambient temperature. However, the proof of concept experiment performed in a bright clear June day has evidenced some limitations. A critical analysis of the obtained experimental results has done, in order to individuate design revisions for the device and to identify future metamaterial improvements.

Indoor production of basil (Ocimum basilicum L.) is influenced by light spectrum, photosynthetic photon flux density (PPFD), and the photoperiod. To investigate the effects of different lighting on growth, chlorophyll content, and secondary metabolism, basil plants were grown from seedlings to fully expanded plants in microcosm devices under different light conditions: (a) white light at 250 and 380 μmol·m⁻²·s⁻¹ under 16/8 h light/dark and (b) white light at 380 μmol·m⁻²·s⁻¹ under 16/8 and 24/0 h light/dark. A higher yield was recorded under 380 μmol·m⁻²·s⁻¹ compared to 250 μmol·m⁻²·s⁻¹ (fresh and dry biomasses 260.6 ± 11.3 g vs. 144.9 ± 14.6 g and 34.1 ± 2.6 g vs. 13.2 ± 1.4 g, respectively), but not under longer photoperiods. No differences in plant height and chlorophyll content index were recorded, regardless of the PPFD level and photoperiod length. Almost the same volatile organic compounds (VOCs) were detected under the different lighting treatments, belonging to terpenes, aldehydes, alcohols, esters, and ketones. Linalool, eucalyptol, and eugenol were the main VOCs regardless of the lighting conditions. The multivariate data analysis showed a sharp separation of non-volatile metabolites in apical and middle leaves, but this was not related to different PPFD levels. Higher levels of sesquiterpenes and monoterpenes were detected in plants grown under 250 μmol·m⁻²·s⁻¹ and 380 μmol·m⁻²·s⁻¹, respectively. A low separation of non-volatile metabolites based on the photoperiod length and VOC overexpression under longer photoperiods were also highlighted.

In this work, tungsten nitrides sputtered at different powers supplied to a W target (300 W, 500 W, 700 W) and proposed for solar thermal applications as part of solar absorbers, as active and robust materials for capacity energy storage and as plasma-facing materials were annealed in vacuum at medium-high temperatures (470 °C, 580 °C) and characterized by means of X-ray diffraction (XRD), AFM, micro-Raman, FTIR, UV–VIS–-NIR, sheet, surficial energy and wetting angle measurements. From the overall set of analyses, some important modifications and differences between samples after annealing emerged (which will be useful for selecting them for specific applications) and have been correlated to sputtered W metallic clusters’ ability to adsorb, form complexes with and react with the strong N₂ triple bond under the various plasma conditions of a reactive sputtering process. In particular, the 300 W film of poor crystalline quality as deposited, after annealing released entrapped nitrogen and retained its W₂N structure up to a temperature of 580 °C. Despite there being no phase transition, there was an increase in sheet resistance, which is detrimental because the preservation of metallic character is an important requisite for the proposed applications. The 500 W film had a stable crystalline structure and a metallic character unmodified by increasing temperature. The 700 W film, whose structure as deposited was almost amorphous, underwent the most severe modification after annealing: crystallizing, disproportioning and giving rise to a composite and porous nature (W + WN_x) not ideal for spectrally selective coating applications, but useful for tailoring capacitive energy storage devices, or for catalysts for hydrogen evolution reactions (as an alternative to platinum) in alkaline water electrolysis.

In this study, a low-cost, scalable and robust process is proposed as an innovative method for coating solar mirrors with a self-cleaning, transparent in the full solar range and versatile material based on auxetic aluminum nitrides, previously obtained at the laboratory scale. This work presents the scaling-up of the fabrication process from the laboratory to prototypal scale and the preliminary results of outdoor self-cleaning solar mirror field tests in the demonstrative concentrating solar power (CSP) plant ENEASHIP located in Casaccia (Rome) ENEA Research Center. Prototypes with a size of 50 × 40 cm have shown stability in external conditions: no coating degradation occurred during the test campaign. Their washing restores the initial reflectance affected by soiling and the self-cleaning performance allows for the utilization of a reduced quantity of water for cleaning operations with respect to the uncoated glass of back surface mirrors. A similar self-cleaning AlN coating could be utilized on other solar components affected by soiling, such as the glass envelopes in heat-collecting elements, PV panels and other parts where a self-cleaning performance combined with an optical one is required.

Soiling severely reduces solar mirror performance, requiring dispendious water consumption for cleaning operations and causing an increase in the levelized cost of energy (LCOE). An emerging technology for facing this problem consists of developing transparent self-cleaning coatings, able to be washed with a small amount of water by virtue of the modulation of surficial wetting properties. Nevertheless, the beneficial effects of coatings decrease in the first year, and coated mirrors show even higher soiling than non-coated ones. Moreover, it is important that coating production processes are economically convenient, consistent with the intended reduction of overall costs. The aim of this work is the research and development of a cheap and scalable solution, compatible with mirror fabrication steps and, in such a sense, economically advantageous. It involves the substitution of the alumina last layer of solar mirrors with more hydrophobic, potentially auxetic aluminum compounds, such as nitrides. In particular, 2D inorganic aluminum nitride thin films doped with metals (such as aluminum and silver) and non-metals have been fabricated by means of reactive sputtering deposition and characterized for the purpose of studying their self-cleaning behavior, finding a trade-off between wetting properties, optical clarity, and stability.

Indoor farming of basil (Ocimum basilicum L.) under artificial lighting to support year-round produce demand is an area of increasing interest. Literature data indicate that diverse light regimes differently affect downstream metabolic pathways which influence basil growth, development and metabolism. In this study, basil was grown from seedlings to fully developed plants in a microcosm, an innovative device aimed at growing plants indoor as in natural conditions. Specifically, the effects of white (W) and blue-red (BR) light under a photosynthetic photon flux density of 255 μmol m⁻² s⁻¹ on plant growth, photochemistry, soluble nutrient concentration and secondary metabolism were investigated. Plants grew taller (41.8 ± 5.0 vs. 28.4 ± 2.5 cm) and produced greater biomass (150.3 ± 24.2/14.7 ± 2.0 g vs. 116.2 ± 28.3/12.3 ± 2.5 g fresh/dry biomass) under W light compared to BR light. The two lighting conditions differently influenced the soluble nutrient concentration and the translocation rate. No photosynthetic stress was observed under the two lighting regimes, but leaves grown under W light displayed higher levels of maximum quantum yield of PSII and electron transport rate. Sharp differences in metabolic patterns under the two lighting regimes were detected with higher concentrations of phenolic compounds under the BR light.