This research was carried out to determinate the effect of the atmosphere processing conditions (air and argon) and two specific thermal treatments, on the properties of specimens made from the nickel-based alloy Hastelloy C-22 by plasma transferred arc (PTA). Firstly, the additive manufacturing parameters were optimized. Following, two walls were manufactured in air and argon respectively. Afterwards, a determinate number of specimens were cut out and evaluated. Regarding the comparison performed with the extracted specimens from both walls, three specimens of each wall were studied as-built samples. Furthermore, a commonly used heat treatment in Hastelloy, with two different cooling methods, was selected to carry out additional comparisons. In this respect, six additional specimens of each wall were selected to be heat treated to a temperature of 1120 °C for 20 min. After the heat treatment, three of them were cooled down by rapid air cooling (RAC), while the other three were cooled down by water quenching (WQ). In order to study the influence degree of the processing conditions, and how the thermal treatments could modify the final properties of the produced specimens, a detailed characterization was performed. X-ray diffraction and microstructural analyses revealed the phases-presence and the apparition of precipitates, varying the thermal treatment. Moreover, the results obtained after measuring mechanical and tribological properties showed slight changes caused by the variation of the processing atmosphere. The yield strength of the extracted specimens from the two walls achieved values closer to the standards ones in air 332.32 MPa (±21.36 MPa) and in argon 338.14 MPa (±9 MPa), both without thermal treatment. However, the effect of the cooling rate resulted as less beneficial, as expected, reducing the deformation properties of the specimens below 11%, independently of the air or argon manufacturing atmosphere and the cooling rate procedure.

In the last decade, titanium metal matrix composites (TMCs) have received considerable attention thanks to their interesting properties as a consequence of the clear interface between the matrix and the reinforcing phases formed. In this work, TMCs with 30 vol % of B₄C are consolidated by hot pressing. This technique is a powder metallurgy rapid process. Incorporation of the intermetallic to the matrix, 20 vol % (Ti-Al), is also evaluated. Here, the reinforcing phases formed by the reaction between the titanium matrix and the ceramic particles, as well as the intermetallic addition, promote substantial variations to the microstructure and to the properties of the fabricated composites. The influences of the starting materials and the consolidation temperature (900 °C and 1000 °C) are investigated. By X-ray diffraction, scanning and transmission electron microscopy analysis, the in-situ-formed phases in the matrix and the residual ceramic particles were studied. Furthermore, mechanical properties are studied through tensile and bending tests in addition to other properties, such as Young’s modulus, hardness, and densification of the composites. The results show the significant effect of temperature on the microstructure and on the mechanical properties from the same starting powder. Moreover, the Ti-Al addition causes variation in the interface between the reinforcement and the matrix, thereby affecting the behaviour of the TMCs produced at the same temperature.

This research is focused on the influence of processing temperature on titanium matrix composites reinforced through Ti, Al, and B₄C reactions. In order to investigate the effect of Ti-Al based intermetallic compounds on the properties of the composites, aluminum powder was incorporated into the starting materials. In this way, in situ Ti_xAl_y were expected to form as well as TiB and TiC. The specimens were fabricated by the powder metallurgy technique known as inductive hot pressing (iHP), using a temperature range between 900 °C and 1400 °C, at 40 MPa for 5 min. Raising the inductive hot pressing temperature may affect the microstructure and properties of the composites. Consequently, the variations of the reinforcing phases were investigated. X-ray diffraction, microstructural analysis, and mechanical properties (Young’s modulus and hardness) of the specimens were carried out to evaluate and determine the significant influence of the processing temperature on the behavior of the composites.

Plasma metal deposition (PMD) is an interesting additive technique whereby diverse materials can be employed to produce end parts with complex geometries. This study investigates not only the effects of the manufacturing conditions on the final properties of 316L stainless steel specimens by PMD, but it also affords an opportunity to study how secondary treatments could modify these properties. The tested processing condition was the atmosphere, either air or argon, with the other parameters having previously been optimized. Furthermore, two standard thermal treatments were conducted with the intention of broadening knowledge regarding how these secondary operations could cause changes in the microstructure and properties of 316L parts. To better appreciate and understand the variation of conditions affecting the behavior properties, a thorough characterization of the specimens was carried out. The results indicate that the presence of vermicular ferrite (δ) varied slightly as a consequence of the processing conditions, since it was less prone to appear in specimens manufactured in argon than in air. In this respect, their mechanical properties suffered variations; the higher the ferrite (δ) content, the higher the mechanical properties measured. The degree of influence of the thermal treatment was similar regardless of the processing conditions, which affected the properties based on the heating temperature.

This work focuses on the study of the microstructure, hardening, and stiffening effect caused by the secondary phases formed in titanium matrices. These secondary phases originated from reactions between the matrix and boron particles added in the starting mixtures of the composites. Not only was the composite composition studied as an influencing factor in the behaviour of the composites, but also different operational temperatures. Three volume percentages of boron content were tested (0.9 vol %, 2.5 vol %, and 5 vol % of amorphous boron). The manufacturing process used to produce the composites was inductive hot pressing, which operational temperatures were between 1000 and 1300 °C. Specimens showed optimal densification. Moreover, microstructural studies revealed the formation of TiB in various shapes and proportions. Mechanical testing confirmed that the secondary phases had a positive influence on properties of the composites. In general, adding boron particles increased the hardness and stiffness of the composites; however rising temperatures resulted in greater increases in stiffness than in hardness.

Arc-directed energy deposition using wire as feedstock is establishing itself as a 3D printing method capable of obtaining additively manufactured large structures. Contrasting results are reported in the literature about the effect of the deposition parameters on the quality of the deposited tracks, as it is highly dependent on the relationship and intercorrelations between the individual input parameters, which are generally deposition-technique-dependent. This study comprehensively analysed the effect of several deposition parameters and clarified their interactions in plasma metal deposition of Al alloys. It was found that, although no straightforward correlation between the individual input parameters investigated and the measured output deposition track’s quality aspects existed, the input current had the greatest effect, followed by the wire feed speed and its interaction with the input current. Moreover, the greatest effect of changing the shielding gas atmosphere, including the gas mixture, flow rate and plasma flow, was on the penetration depth, and fine-tuning the frequency/balance ratio and the preheating of the deposition substrates reduced the amount of porosity. This study demonstrates that well-deposited multi-layer walls made out of Al alloys can successfully be achieved via plasma metal deposition.