Centre of Isotopic and Geochemical Research based on the Analytical Department of Vinogradov Institute of Geochemistry SB RAS (Irkutsk) performs a wide range of analytical studies to solve mineralogical and petrological, geochemical, prospecting, ecological, paleoclimatic and applied problems. The studies are supported by the modern equipment for electron microprobe, X-ray diffraction, X-ray fluorescence, atomic emission and mass spectrometric (including isotope) analyses, as well as the necessary international certified reference materials (SRM) and a collection of SRM of the natural and technogenic composition of our production.

The crystal-chemical, vibrational, and optical properties of microporous aluminosilicate cancrinite have been investigated by combining electron probe microanalysis, single-crystal X-ray diffraction, infrared (IR) absorption, Raman, UV-Visible absorption, and electron spin resonance spectroscopy. The behavior of the peaks in the IR spectra was also studied during the dehydration of the sample. The analyzed sample has the following unit cell parameters (P6₃): a = 12.63189(14) Å, c = 5.13601(7) Å. The empirical formula, based on 12(Si + Al), is Na_6.47Ca_1.23K_0.01[Al_5.97Si_6.03O₂₄] (CO₃)_1.45(SO₄)_0.03Cl_0.01·2H₂O. The Al-Si framework of AB-type is formed by columns of based-shared “cancrinite” (CAN) cages, containing Na and H₂O positions located on the 3-fold axis, and channels with CO₃ groups, lying in two mutually exclusive and partially occupied positions in the center of the channel, and split Na/Ca cation sites. The revealed characteristics are somewhat different in comparison with the cancrinite structural features previously described in the literature. Studied crystals change color from grayish-pink to blue after X-ray irradiation (10⁴ Gy). The blue color of the irradiated cancrinite is caused by the formation (CO₃)^−● radicals in the crystals. Combining the results obtained using the selected methods will provide a better understanding of the relationships between the structural, chemical, and optical-physical properties of microporous aluminosilicates.

The results of an examination of vladimirivanovite, a new mineral of the sodalite group, found at the Tultui deposit in the Baikal region are discussed. The mineral occurs in the form of outer rims (0.01–3 mm thick) of lazurite, elongated segregations without faced crystals (0.2 to 3–4 mm in size; less frequently, 4 × 12–15 × 20 mm), and rare veinlets (up to 5 mm) hosted in calciphyre and marble. Vladimirivanovite is irregular and patchy dark blue. The mineral is brittle; on average, the microhardness VHN is 522–604, 575 kg/mm²; and the Mohs hardness is 5.0–5.5. The measured and calculated densities are 2.48(3) and 2.436 g/cm³, respectively. Vladimirivanovite is optically biaxial; 2V _meas = 63(±1)°, 2V _calc = 66.2°; the refractive indices are α = 1.502–1.507 (±0.002), N _m = 1.509–1.514 (±0.002), and N _g = 1.512–1.517 (±0.002). The chemical composition is as follows, wt %: 32.59 SiO₂, 27.39 Al₂O₃, 7.66 CaO, 17.74 Na₂O, 11.37 SO₃, 1.94 S, 0.12 Cl, and 1.0 H₂O; total is 99.62. The empirical formula calculated based on (Si + Al) = 12 with sulfide sulfur determined from the charge balance is Na_6.36Ca_1.52(Si_6.03Al_5.97)_Σ12O_23.99(SO₄)_1.58(S₃)_0.17(S₂)_0.08 · Cl_0.04 · 0.62H₂O; the idealized formula is Na₆Ca₂[Al₆Si₆O₂₄](SO₄,S₃,S₂,Cl)₂ · H₂O. The new mineral is orthorhombic, space group Pnaa; the unit-cell dimensions are a = 9.066, b = 12.851, c = 38.558 Å, V = 4492 ų, and Z = 6. The strongest reflections in the X-ray powder diffraction pattern (dÅ—I[hkl]) are: 6.61–5[015], 6.43–11[020, 006], 3.71–100[119, 133], 2.623–30[20.12, 240], 2.273–6[04.12], 2.141–14[159, 13.15], 1.783–9[06.12, 04.18], and 1.606–6[080, 00.24]. The crystal structure has been solved with a single crystal. The mineral was named in memoriam of Vladimir Georgievich Ivanov (1947–2002), Russian mineralogist and geochemist. The type material of the mineral is deposited at the Mineralogical Museum of St. Petersburg State University, St. Petersburg, Russia.