The conventional cutting tools used for machining titanium alloys normally experience rapid tool wear, and it is generally difficult to achieve a cutting speed over 60 m/min. In this paper, a comprehensive study on improving the machining of Ti-6Al-4V alloy is presented, focusing on high-speed end milling at 100 m/min. Three different AlCrN PVD-coated cemented carbide tools were employed over cemented solid carbide endmills. The study aimed to understand the factors influencing tool performance and, particularly, the uncommon tool wear behavior characterized by chipping on the rake face. The research methodology involves a detailed investigation of coating properties, mechanical characteristics, surface defects, and tool edge geometries. Mechanical properties were measured to assess the resistance to plastic deformation and impact fatigue fracture resistance. Surface defects were meticulously observed, and tool edge geometries were evaluated through optical microscopies. These analyses uncover the key factors contributing to the best tool performance, notably the resistance to plastic deformation (H³/E² ratio), impact fatigue fracture resistance, and maintaining uniform tool edge geometries. The results of this study reveal that the moderate stress C3 coating outperformed the other two coatings, exhibiting a 1.5-times-longer tool life, a relatively stable cutting force curve, and favorable friction conditions in the cutting zone.

This work aimed to ascertain the corresponding influences of several PVD-coated cutting tools on the susceptibility of the machined surface of super duplex stainless steel (SDSS) to stress corrosion cracking. Coatings comprised of AlCrN, AlCrN/TiSiN, and AlTiN were applied to cemented carbide cutting tools using the PVD method; these were then used to turn the outer surface of the SDSS tube section. During the cutting process, the material presents the following combination of features: (i) a tendency for strain hardening, reflected in microstructural modifications and residual stresses of the machined surface and (ii) high temperatures in the cutting region, reducing the tool life. The goal of this work was to evaluate the surface integrity (work hardening and corrosion behaviour) of the SDSS obtained after the machining process (finish turning) with cemented carbide tools coated with three different PVD coatings.

The machining of austenitic stainless steel alloys is usually characterized by high levels of adhesion and built-up edge; therefore, improving tribological conditions is fundamental to obtaining higher tool life and better surface finish. In this work, three different Al_0.6Ti_0.4N coatings are compared, two deposited by Cathodic Arc Evaporation (CAE) and one with High-Power Impulse Magnetron Sputtering (HiPIMS). The effects of the micromechanical properties and the microstructure of the coatings were then studied and related to the machining performance. Both arc-deposited coatings (CAE 1 and 2) exhibited similar average tool life, 127 min and 128 min, respectively. Whereas the HiPIMS lasted for only 21.2 min, the HiPIMS-coated tool had a much shorter tool life (more than six times lower than both CAE coatings) due to the intense adhesion that occurred in the early stages of the tool life. This higher adhesion ultimately caused built-up edge and chipping of the tool. This was confirmed by the cutting forces and more deformation on the shear band and undersurface of the chips, which are related to higher levels of friction. The higher adhesion could be attributed to the columnar structure of the HiPIMS and the (111) main texture, which presents a higher surface energy when compared to the dominant (200) from both arc depositions. Studies focused on tribology are necessary to further understand this relationship. In terms of micromechanical properties, tools with the highest plasticity index performed better (CAE 2 = 0.544, CAE 1 = 0.532, and HiPIMS = 0.459). For interrupted cutting machining where adhesion is the main wear mechanism, a reserve of plasticity is beneficial to dissipate the energy generated during friction, even if this was related to lower hardness levels (CAE 2 = 26.6 GPa, CAE 1 = 29.9 GPa, and HiPIMS = 33.6 GPa), as the main wear mechanism was adhesive and not abrasive.

Hard coatings are a suitable solution for increasing the lifetime of tools and components employed in different industrial applications. Coatings of transition metal nitrides have great use for tribological applications due to due to their unique mechanical properties. Although widely employed, current deposition methods such as cathodic arc evaporation produce coatings with many defects, which in turn reduce the resistance to wear, especially under severe conditions. High Power Impulse Magnetron Sputtering is a novel physical vapor deposition technique that produces homogeneous coatings. In this study, CrN and CrAlN monolayer coatings were deposited on AISI 304 stainless steel substrates using HiPIMS. X-Ray Diffraction, Scanning Electron Microscopy, Atomic Force Microscopy were used to evaluate the microstructure, phase composition, morphology and chemical composition of the coating. Results showed that HiPIMS is a promising technique to deposit CrN and CrAlN homogeneous coatings with high hardness and good adhesion to the substrate.

Super duplex stainless steels (SDSSs) are widely utilized across industries owing to their remarkable mechanical properties and corrosion resistance. However, machining SDSS presents considerable challenges, particularly at high speeds. This study investigates the machinability of SDSS grade SAF 2507 (UNS S32750) under high-speed milling conditions using SiAlON insert tools. Comprehensive analysis of key machinability indicators, including chip compression ratio, chip analysis, shear angle, tool wear, and friction conditions, reveals that lower cutting speeds optimize machining performance, reducing cutting forces and improving chip formation. Finite element analysis (FEA) corroborates the efficacy of lower speeds and moderate feed rates. Furthermore, insights into friction dynamics at the tool–chip interface are offered, alongside strategies for enhancing SDSS machining. This study revealed the critical impact of cutting speed on cutting forces, with a significant reduction in forces at cutting speeds of 950 and 1350 m/min, but a substantial increase at 1750 m/min, particularly when tool wear is severe. Furthermore, the combination of 950 and 1350 m/min cutting speeds with a 0.2 mm/tooth feed rate led to smoother chip surfaces and decreased friction coefficients, thus enhancing machining efficiency. The presence of stick–slip phenomena at 1750 m/min indicated thermoplastic instability. Optimizing machining parameters for super duplex stainless steel necessitates balancing material removal rate and surface integrity, as the latter plays an important role in ensuring long-term performance and reliability in critical applications.