An aluminum/waterborne acrylic coating was developed by orthogonal experiments, and the gloss, emissivity, chromatic distortion, hardness, adhesion, impact resistance, and corrosion resistance of the coatings were examined. The results showed that the effect of drying time on the infrared emissivity of coatings was more significant than that of the Al powder concentration and nano-silica slurry. When the drying time was prolonged from 0.5 to 6.0 min, the gloss of the coating decreased slowly and the gloss remained low. The infrared emissivity first decreased and then increased. The infrared emissivity of coatings dried for 2.0 min was better. The L’ value gradually decreased and showed a small change of range. With the increasing of the drying time, the hardness of the coating gradually decreased and was the highest at 0.5–2.0 min. The drying time had no effect on the adhesion level. The impact resistance of the coating was better during the drying period of 1.0–3.0 min. The corrosion resistance of the coating was better at 2.0 min. When the drying time was 2.0 min, the waterborne coating showed the better comprehensive performance. This study provides new prospects in using low infrared emissive coatings for infrared stealth and compatibility with visible light.

The modification experiment of waterborne coating was carried out by adding microcapsules. The wall material of the microcapsule was urea-formaldehyde resin and the core material of the microcapsule was epoxy resin. Core material can improve the toughness of the coating and prevent the cracking of the coating. The influences of different contents of microcapsules and the order of adding microcapsules in the coating process on the properties of gloss, color difference and toughness were studied. The results showed that the gloss of the waterborne coating decreased with the increase of microcapsule content. The color difference of coating increased first and then decreased, and when the microcapsule content was 8.0%, the color difference was the largest. The toughness of the coatings also increased first and then decreased. When the content of the microcapsule was 10.0%, the toughness of the coating was significantly enhanced. When the microcapsules with a content of 10.0% were added to the waterborne coating, under the same process, the coating gloss of microcapsules added to the primer was relatively high, and the coating gloss was the highest when the coating process was three-layer primer and two-layer topcoat. The microcapsule had little effect on the color difference of coating in different coating processes. When the coating process was three-layer primer and three-layer topcoat, the coating toughness was the best when microcapsules were added to the topcoats. This study provides a basis for industrial application of waterborne coatings to enhance their toughness.

A two-step in situ polymerization method was utilized to fabricate urea formaldehyde (UF) resin-coated shellac resin microcapsules. The morphology and composition of microcapsules with different core-wall ratios were analyzed by scanning electron microscope (SEM) and infrared (IR) spectrum. The effects of different concentrations of microcapsules on gloss, color difference, hardness, adhesion, and impact resistance of waterborne paint films were studied. At the same time, the self-healing effect of the prepared microcapsules applied to waterborne paint film was discussed. The results revealed that the shellac resin microcapsules coated with UF resin were successfully prepared. At the 0.67:1 and 0.75:1 core-wall ratios, the color differences of the paint film with 0–20.0% (weight percent) microcapsules were small and the color was uniform. Under the condition of 60° incident angle and the same microcapsule concentration, a good gloss was obtained. When the concentration was 20.0%, the hardness of paint film reached the maximum value. The adhesion of paint film was better, which was not affected by microcapsule concentration. When the concentration was 5.0% and 10.0%, the microstructure of paint film was good. The paint film with a 10.0% concentration of the shellac resin microcapsules coated with UF resin had better self-healing performance and the comprehensive performance was better. This paper provides the basis for the industrial application of self-healing waterborne wood paint films.

This study chose organic thermochromic pigment powder and waterborne wood primer as the paint base, and Chinese fir board as the substrate to prepare thermochromic waterborne coatings with different concentrations of thermochromic pigment powder. The best concentration of thermochromic pigment powder for waterborne primer film on Chinese fir surface was explored. The experimental results showed that the color-changing property of the primer film was the best when the concentration of pigment powder in primer film was 5.0%–10%. There was a negative correlation between the gloss of the primer and the concentration of pigment powder. The gloss of the primer film was the highest when the concentration of pigment powder was 5%. When the concentration of pigment powder is 0%–20% and 25.0%–30%, the adhesion of the coating is grade 0 and grade 1, respectively. The resistance to the impact of primer film increased with the increase of concentration of pigment powder, but the resistance to the impact of primer film with 0%–30% of thermochromic pigment powder concentration was similar. Scanning electron microscopy showed that the higher the concentration of thermochromic pigment powder, the more particles and agglomeration. When the concentration of pigment powder was 5%, the distribution of particles was uniform and no agglomeration, and the microstructure of primer film was the best. Infrared spectroscopy showed that there was no difference in the composition of the paint film from 0% to 30%. The results showed that the comprehensive property of waterborne primer film on Chinese fir was better when the pigment concentration was 5%. Waterborne thermochromic primer film provides a potential application for the development of intelligent furniture in different temperature ranges.

Microcapsules with lac resin as the core material and urea-formaldehyde resin as the wall material were prepared by in situ polymerization, and then the lac resin microcapsules and fluorane microcapsules were added into a water-based primer or topcoat, respectively, to prepare water-based coatings with dual functions of thermochromic and self-repair. The effects of different methods of adding microcapsules on the optical properties, mechanical properties, self-repairing properties, and the aging resistance of water-based paint film were investigated, so as to prepare water-based paint film with the best discoloration and self-repairing functions. The results showed that the paint film with 10.0% fluorane microcapsules in the topcoat and 5.0% lac resin microcapsules in the primer had better comprehensive properties, and the paint film changed from yellow to colorless at 32 °C, with a color difference of 68.9, hardness of 3H, adhesion grade of 0, impact resistance of 13.0 kg∙cm, and elongation at break of 20.0%. The resistance of the paint film to NaCl, ethanol, and detergent was grade 2, with slight discontinuous marks, and the resistance to red ink was grade 3, with slight marks. The lac resin microcapsules have good aging resistance, which can enhance the aging resistance of the paint film with fluorane microcapsules. The gap width of the paint film was repaired by 2.1 µm, the self-repairing rate was 12.3%, and the paint film with lac resin microcapsules had a better crack inhibition effect. The results have provided a reference for multifunctional wood coatings.

An Al powder filler, nano silica slurry and KH560 were mixed with a prepared waterborne UV-curable coating, and the coating was optimized by an orthogonal experiment. Influences of the Al powder concentration on the gloss, infrared emissivity, brightness, mechanical properties, corrosion resistance and other related properties of the coating were further discussed. The results show that the influence of the Al powder concentration on the gloss was more significant, followed by the UV curing time and nano silica slurry concentration. After studying the key role of the concentration of the Al powder, we found that as the concentration of the Al powder is augmented from 10.0% to 25.0%, the gloss lessened from 19.1% to 8.5%. As the concentration of the Al powder was augmented from 10.0% to 40.0%, the infrared emissivity lessened from 0.649 to 0.083 and the brightness L’ value of the coating was step-by-step augmented and inclined to be stable; in addition, the coating’s mechanical properties reached an excellent level. The coating containing 25.0% Al powder had the best corrosion resistance, surface morphology and comprehensive properties, which can potentially be used for infrared stealth technology.