The selection of dressing is crucial for the wound healing process. Traditional dressings protect against contamination and mechanical damage of an injured tissue. Alternatives for standard dressings are regenerating systems containing a polymer with an incorporated active compound. The aim of this research was to obtain a biodegradable wound dressing releasing propolis in a controlled manner throughout the healing process. Dressings were obtained by electrospinning a poly(lactide-co-glycolide) copolymer (PLGA) and propolis solution. The experiment consisted of in vitro drug release studies and in vivo macroscopic treatment evaluation. In in vitro studies released active compounds, the morphology of nonwovens, chemical composition changes of polymeric material during degradation process, weight loss and water absorption were determined. For in vivo research, four domestic pigs, were used. The 21-day experiment consisted of observation of healing third-degree burn wounds supplied with PLGA 85/15 nonwovens without active compound, with 5 wt % and 10 wt % of propolis, and wounds rinsed with NaCl. The in vitro experiment showed that controlling the molar ratio of lactidyl to glycolidyl units in the PLGA copolymer gives the opportunity to change the release profile of propolis from the nonwoven. The in vivo research showed that PLGA nonwovens with propolis may be a promising dressing material in the treatment of severe burn wounds.

Wound healing poses a serious therapeutic problem. Methods which accelerate tissue regeneration and minimize or eliminate complications are constantly being sought. This paper is aimed at evaluation of the potential use of biodegradable polymer nonwovens releasing propolis as wound healing dressings, based on the literature data. Propolis is honeybee product with antioxidant, antibacterial, antifungal, anticancer, anti-inflammatory, analgesic, and regenerative properties. Controlled release of this substance throughout the healing should promote healing process, reduce the risk of wound infection, and improve aesthetic effect. The use of biodegradable aliphatic polyesters and polyester carbonates as a propolis carrier eliminates the problem of local drug administration and dressing changes. Well-known degradation processes and kinetics of the active substance release allows the selection of the material composition appropriate to the therapy. The electrospinning method allows the production of nonwovens that protect the wound against mechanical damage. Moreover, this processing technique enables adjusting product properties by modifying the production parameters. It can be concluded that biodegradable polymer dressings, releasing a propolis, may find potential application in the treatment of complicated wounds, as they may increase the effectiveness of treatment, as well as improve the patient’s life quality.

Knowledge of degradation and impairment phenomena of (bio)degradable polymeric materials under operating conditions, and thus the selection of test procedures and prediction of their behavior designates the scope and capabilities as well as possible limitations of both: the preparation of the final product and its durability. The main novelty and objective of this research was to determine the degradation pathways during testing of polylactide and polylactide/polyhydroxyalkanoate materials made with three-dimensional printing and the development of a new strategy for the comprehensive characterization of such complex systems including behavior during waste disposal. Prototype objects were subjected to tests for damage evolution performed under simulating operating conditions. The reference samples and the tested items were characterized by gel permeation chromatography and differential scanning calorimetry to determine changes in material properties. The studies showed that: polyhydroxyalkanoate component during accelerated aging and degradation in environments rich in microorganisms accelerated the degradation of the material; paraffin accelerates polylactide degradation and slows degradation of polyhydroxyalkanoate-based material; under the influence of an environment rich in enzymes, paraffin contamination accelerates biodegradation; under the influence of natural conditions, paraffin contamination slowed degradation; the processing conditions, in particular the printing orientation of individual parts of the container, influenced the material properties in its various regions, affecting the rate of degradation of individual parts.

The use of (bio)degradable polymers, especially in medical applications, requires a proper understanding of their properties and behavior in various environments. Structural elements made of such polymers may be exposed to changing environmental conditions, which may cause defects. That is why it is so important to determine the effect of processing conditions on polymer properties and also their subsequent behavior during degradation. This paper presents original research on a specimen’s damage during 70 days of hydrolytic degradation. During a standard hydrolytic degradation study of polylactide and polylactide/polyhydroxyalkanoate dumbbell-shaped specimens obtained by 3D printing with two different processing build directions, exhibited unexpected shrinkage phenomena in the last degradation series, representing approximately 50% of the length of the specimens irrespective of the printing direction. Therefore, the continuation of previous ex-ante research of advanced polymer materials is presented to identify any possible defects before they arise and to minimize the potential failures of novel polymer products during their use and also during degradation. Studies on the impact of a specific processing method, i.e., processing parameters and conditions, on the properties expressed in molar mass and thermal properties changes of specimens obtained by three-dimensional printing from polyester-based filaments, and in particular on the occurrence of unexpected shrinkage phenomena after post-processing heat treatment, are presented.