Silver nanoparticle-modified graphene oxide (Ag/GO) was reliably prepared by using sodium borohydride (NaBH₄) in the presence of citric acid capping agent via a simple wet chemistry method. This rapidly formed Ag/GO composite exhibited good dispersity in a solution containing hydrophilic polyacrylonitrile (PAN). Subsequent electrospinning of this precursor solution resulted in the successful formation of nanofibers without any notable defects. The Ag/GO-incorporated PAN nanofibers showed thinner fiber strands (544 ± 82 nm) compared to those of GO-PAN (688 ± 177 nm) and bare-PAN (656 ± 59 nm). Subsequent thermal treatment of nanofibers resulted in the preparation of thin membranes to possess the desired pore property and outstanding wettability. The Ag/GO-PAN nanofiber membrane also showed 30% higher water flux value (390 LMH) than that of bare-PAN (300 LMH) for possible microfiltration (MF) application. In addition, the resulting Ag/GO-PAN nanofiber membrane exhibited antibacterial activity against Escherichia coli (Gram-negative) and Staphylococcus aureus (Gram-positive). Furthermore, this composite membrane exhibited outstanding anti-fouling property compared to the GO-PAN nanofiber membrane in the wastewater treatment. Therefore, the simple modification strategy allows for the effective formation of Ag/GO composite as a filler that can be reliably incorporated into polymer nanofiber membranes to possess improved overall properties for wastewater treatment applications.

Exfoliated graphene oxide (GO) was reliably modified with a cetyltrimethylammonium chloride (CTAC) surfactant to greatly improve the dispersity of the GO in a polyacrylonitrile (PAN) polymer precursor solution. Subsequent electrospinning of the mixture readily resulted in the formation of GO–PAN composite nanofibers containing up to 30 wt % of GO as a filler without notable defects. The absence of common electrospinning problems associated with clogging and phase separation indicated the systematic and uniform integration of the GO within the PAN nanofibers beyond the typical limits. After thoroughly examining the formation and maximum loading efficiency of the modified GO in the PAN nanofibers, the resulting composite nanofibers were thermally treated to form membrane-type sheets. The wettability and pore properties of the composite membranes were notably improved with respect to the pristine PAN nanofiber membrane, possibly due to the reinforcing filler effect. In addition, the more GO loaded into the PAN nanofiber membranes, the higher the removal ability of the methylene blue (MB) and methyl red (MR) dyes in the aqueous system. The adsorption kinetics of a mixed dye solution were also monitored to understand how these MB and MR dyes interact differently with the composite nanofiber membranes. The simple surface modification of the fillers greatly facilitated the integration efficiency and improved the ability to control the overall physical properties of the nanofiber-based membranes, which highly impacted the removal performance of various dyes from water.

This work demonstrates the incorporation of gold nanoparticles (AuNPs) into crosslinker-free poly(N-isopropylacrylamide), PNIPAM, particles in situ and the examination of their structural and catalytic properties. The formation process of the AuNPs across the crosslinker-free PNIPAM particles are compared to that of crosslinked PNIPAM particles. Given the relatively larger free volume across the crosslinker-free polymer network, the AuNPs formed by the in situ reduction of gold ions are detectably larger and more polydisperse, but their overall integration efficiency is slightly inferior. The structural features and stability of these composite particles are also examined in basic and alcoholic solvent environments, where the crosslinker-free PNIPAM particles still offer comparable physicochemical properties to the crosslinked PNIPAM particles. Interestingly, the crosslinker-free composite particles as a colloidal catalyst display a higher reactivity toward the homocoupling of phenylboronic acid and reveal the importance of the polymer network density. As such, the capability to prepare composite particles in a controlled polymer network and reactive metal nanoparticles, as well as understanding the structure-dependent physicochemical properties, can allow for the development of highly practical catalytic systems.

This report describes the systematic incorporation of gold nanoparticles (AuNPs) onto mesoporous TiO₂ (MPT) particles without strong attractive forces to efficiently serve as reactive and recyclable catalysts in the homocoupling of arylboronic acid in green reaction conditions. Unlike using nonporous TiO₂ particles and conventional SiO₂ particles as supporting materials, the employment of MPT particles significantly improves the loading efficiency of AuNPs. The incorporated AuNPs are less than 10 nm in diameter, regardless of the amount of applied gold ions, and their surfaces, free from any modifiers, act as highly reactive catalytic sites to notably improve the yields in the homocoupling reaction. The overall physical properties of the AuNPs integrated onto the MPT particles are thoroughly examined as functions of the gold content, and their catalytic functions, including the rate of reaction, activation energy, and recyclability, are also evaluated. While the rate of reaction slightly increases with the improved loading efficiency of AuNPs, the apparent activation energies do not clearly show any correlation with the size or distribution of the AuNPs under our reaction conditions. Understanding the formation of these types of composite particles and their catalytic functions could lead to the development of highly practical, quasi-homogeneous catalysts in environmentally friendly reaction conditions.

Tungsten is the most effective eco-friendly material used for radiation shielding in hospitals. However, despite its commendable density and shielding performance, tungsten faces challenges in miscibility with other materials because of its elevated melting point and strength. In this study, to protect medical personnel against scattered rays, which are indirect X-rays, a lightweight material was prepared by mixing graphite oxide material, considering its thinness and flexibility. Tungsten particles were evenly dispersed in the polymer, and nanofibers were prepared using this blended polymer solution via electrospinning. Concurrently, the process technology was explored to craft a thin film sheet and obtain a lead-like shielding effect. A spinning solution was prepared by mixing Fe₃O₄-rGO (FerGO) and tungsten. At 60 kVp, 0.1 mm was measured as 0.097 mmPb, at 80 kVp, 0.2 mm was measured as 0.196 mmPb, and at 100 kVp, 0.3 mm was measured as 0.279 mmPb, showing similar shielding performance to lead. As density directly affects the shielding effect, graphene oxide played an important role in increasing the density of the material from 1.941 g/cm³ to 2.302 g/cm³. Thus, this study provides an effective process for producing thin film sheets equivalent to lead.

Gold nanoparticles (AuNPs) have been physically encapsulated into polymer particles to serve as highly reactive quasi-homogeneous catalysts in various types of chemical transformation reaction. Although diverse synthetic strategies have achieved great progress in designing catalytically active AuNPs, a major concern in most synthetic methods is the inevitable use of stabilizing or