The effects of the addition of 0.29 wt% Ce on the high-temperature mechanical properties of an Al–Cu–Li alloy were investigated. Ce addition contributes to T1 (Al₂CuLi) phase coarsening inhibition and Ce-containing intermetallic refinement which greatly improved the thermal stability and high-temperature deformation uniformity of this alloy. On the one hand, small Ce in solid solution and segregation at phase interface can effectively prevent the diffusion and convergence of the main element Cu on T1 phase during thermal exposure. Therefore, the thermal stability of Ce-containing alloy substantiality improves during thermal exposure at the medium-high-temperature stage (170 °C to 270 °C). On the other hand, the increment of the tensile elongation in Ce-containing alloy is much greater than that in Ce-free alloy at high temperatures tensile test, because the refined Al₈Cu₄Ce intermetallic phase with high-temperature stability are mainly located in the fracture area with plastic fracture characteristics. This work provides a new method for enhancing high-temperature mechanical properties of Al–Cu–Li alloy which could be used as a construction material for high-temperature structural components.

Ultrasonic morphology modification of silver (Ag) nanowires and their applications in transparent film heaters for defogging in electric vehicles and surface-enhanced Raman scattering (SERS) detectors have been studied. With 10 min ultrasonic treatment of Ag nanowires, the electro-thermal conversion capability of Ag nanowire based transparent film heaters is efficiently improved (about 50% increase in temperature rise), which can be mainly attributed to the cross-section area reduction and the serious agglomerations of the ultrasonic modified Ag nanowire films. Furthermore, the bending or fracture caused by deformation of Ag nanowires after ultrasonic treatment provides more hot spots for SERS, and therefore lead to a significant SERS signal enhancement. This work not only greatly improves the performance of Ag nanowire based transparent film heaters and SERS detectors, but provides a new way for the functional modification of Ag nanowires.

The corrosion resistance (exfoliation corrosion and inter-granular corrosion) and mechanical properties (strength and hardness) of a high-alloying Al-Zn-Mg-Cu-Zr alloy were improved by the synergistic effect of Ce addition and aging treatment. Ce addition promotes the morphology change of grain boundary precipitates from continuous form to discontinuous form at T6 temper. But the Cu content in grain boundary precipitates became much lower than that in Ce-free alloy, owing to a large amount of Cu being trapped in AlCuCe phase. Hence retrogression and re-aging (RRA) treatment were then adopted. The Cu content in grain boundary precipitates was improved, which can be attributed to the removal of Cu from solid solution during high temperature aging and its subsequent incorporation into grain boundary precipitates. In addition, the size and the distribution discontinuity of the grain boundary precipitates can be further increased and the main intra-grain phases of RRA alloy are still fine η′ phase similar to T6 temper. Therefore, the alloy at RRA temper obtains the optimal corrosion resistance without loss of high strength.

Highly ordered Ag particle-chains (AgPCs) have been obtained from Ag nanowires (AgNWs) by radio frequency (RF) plasma treatment. Such conversion is attributed to the fast nonequilibrium diffusion of Ag atoms (liquid-like behavior) on AgNWs surfaces through the plasma bombarding. Further, the formed AgPCs highly coincide with the predictions by Rayleigh instability. In contrast to heat treatment, AgPCs are formed rapidly, highly ordered and at temperature below 100 °C. Furthermore, aperiodicity and wire–wire welding instead of highly ordered particle-chains has been observed as the AgNWs are overlapped by plasma treatment. This work should provide a new perspective for metallic particle-chains fabrication.

Closed encounter Ag nanoshell pairs with remarkable improved plasmonic light enhancement in their gaps have been attracting much attention in the production of sensitivity SERS substrates. This work demonstrates the size effects of Ag nanoshell pairs on obtaining higher light intensity in their gaps. It is found that very complex light intensity changes occur in the gaps of Ag nanoshell pairs with their diameter enlargements ( nm). By the calculation of scattering efficiency and electric field vectors, the size-related light intensity changes in the gaps have been revealed and been concluded systematically. This work fills in the gaps of application of nanoshell pairs with larger sizes in SERS detectors and could guide the design of some other Ag nanoshell pair-based optical devices.