The effects of the addition of 0.29 wt% Ce on the high-temperature mechanical properties of an Al–Cu–Li alloy were investigated. Ce addition contributes to T1 (Al₂CuLi) phase coarsening inhibition and Ce-containing intermetallic refinement which greatly improved the thermal stability and high-temperature deformation uniformity of this alloy. On the one hand, small Ce in solid solution and segregation at phase interface can effectively prevent the diffusion and convergence of the main element Cu on T1 phase during thermal exposure. Therefore, the thermal stability of Ce-containing alloy substantiality improves during thermal exposure at the medium-high-temperature stage (170 °C to 270 °C). On the other hand, the increment of the tensile elongation in Ce-containing alloy is much greater than that in Ce-free alloy at high temperatures tensile test, because the refined Al₈Cu₄Ce intermetallic phase with high-temperature stability are mainly located in the fracture area with plastic fracture characteristics. This work provides a new method for enhancing high-temperature mechanical properties of Al–Cu–Li alloy which could be used as a construction material for high-temperature structural components.

A self-polarized rGO/PVDF composite, engineered by water-induced polarization and micro-nano-composite, effectively reduces dye pollutants and yields H₂O₂ under mechanical force.

The effects of the addition of 0.29 wt % Ce on the recrystallization behavior of an Al–Cu–Li–0.13Zr (wt %) alloy during isothermal annealing were investigated. Ce addition greatly improved inhibition of recrystallization in this alloy compared with that in the Ce-free alloy. The texture of the Ce-containing alloy contained a large amount of β-fibers and fibrous unrecrystallized grain microstructures distributed along the rolling direction in the overall annealing process. The improved recrystallization resistance endowed by Ce addition can be attributed to the large number of small Al₈Cu₄Ce species formed on the grain boundary. These fine particles with high-temperature stability can exert a Zener pressure on the Al₃Zr dispersoid-free grain boundary. The yield strength of the Ce-containing alloy increased significantly, to 38 MPa, and the fracture toughness improved by 56.28% compared with those of the Ce-free alloy. This work provides a convenient and economical method for enhancing the overall performance of an Al–Cu–Li–Zr alloy via recrystallization inhibition by Ce addition.

Ultrasonic morphology modification of silver (Ag) nanowires and their applications in transparent film heaters for defogging in electric vehicles and surface-enhanced Raman scattering (SERS) detectors have been studied. With 10 min ultrasonic treatment of Ag nanowires, the electro-thermal conversion capability of Ag nanowire based transparent film heaters is efficiently improved (about 50% increase in temperature rise), which can be mainly attributed to the cross-section area reduction and the serious agglomerations of the ultrasonic modified Ag nanowire films. Furthermore, the bending or fracture caused by deformation of Ag nanowires after ultrasonic treatment provides more hot spots for SERS, and therefore lead to a significant SERS signal enhancement. This work not only greatly improves the performance of Ag nanowire based transparent film heaters and SERS detectors, but provides a new way for the functional modification of Ag nanowires.

An electricity-mediated plasmonic engineering was applied on a single Ag nanowire to engineer its tip for surface-enhanced Raman scattering (SERS). Under this constant photoelectric field treatment, a significant sharpening of the tip and reduction of the surface fluctuation was observed for the Ag nanowire tip via in situ atomic force microscopy. A significant SERS signal enhancement was thus obtained after the tip engineering. The relevant dynamic mechanisms of the tip engineering, including the light-induced plasmonic phase transition and electrostatic force driven flow on the Ag nanowire tip are discussed in detail. It is expected that this type of tip engineering will greatly enhance the signal of single metal nanowire SERS probes and provide new insights into fabrication technologies for metal nanostructures.

The Lithium sulfur (Li-S) battery has a great potential to replace lithium-ion batteries due to its high-energy density. However, the “shuttle effect” of polysulfide intermediates (Li₂S₈, Li₂S₆, Li₂S₄, etc.) from the cathode can lead to rapid capacity decay and low coulombic efficiency, thus limiting its further development. Anchoring polysulfide and inhibiting polysulfide migration in electrolytes is one of the focuses in Li-S battery. It is well known that polar metal oxides-manganese oxides (MnO₂) are normally used as an effective inhibitor for its polysulfide inhibiting properties. Considering the natural 1D tunnel structure, MnO₂ with three kinds of typical tunnel-type were screened to study the effects of the tunnel size on the adsorption capacity of polysulfide. We found that MnO₂ with larger tunnel sizes has stronger chemisorption capacity of polysulfide. It promotes the conversion of polysulfide, and corresponding cathode exhibits better cycle reliability and rate performance in the cell comparison tests. This work should point out a new strategy for the cathode design of advanced Li-S battery by controlling the tunnel size.