In this paper, we present the results of experimental tests and numerical calculations for parts of foundry mold devices made by selective laser melting (SLM). The main aim of this research was to compare the heat conduction efficiency of the conformal and the traditional channel arrangement. The infusion spreader with a conformal channel arrangement and the test material were made with an M2 Concept Laser Cusing machine using 1.2709 steel powder. Temperature changes in the spreaders were compared between conventional and conformal cooling channels using finite element method (FEM) calculations. The position of the so-called “thermal equilibrium isotherm” was determined for both sprue spreaders, which separate the area of the mold with a constant temperature from the zone of cyclic temperature changes. The components of the sprue spreaders in a stress state caused by temperature changes during the operation of the pressure machine were determined using the FEM model. It was found that the cooling system shortened the time of solidification and cooling of the alloy. Based on the analysis of the strength test results and the fracture surface of the samples, the relationship between heat treatment parameters and the strength, hardness, and elongation of the tested material was determined. The sprue spreaders were installed under a pressure machine and tested under production conditions. The use of a sprue spreader with a conformal cooling system shortened the time of a single cycle of the casting machine compared to the conventional solution.

This article presents the results of shape-dependent strength analyses in die-castings from traditional (straight-drilled) and conformal core-cooling moulds. Cores with a traditional cooling layout were made of H13 steel using machining, and the working sections of the conformal cores were made using the selective laser melting method (SLM). Two series of casts were produced in the same mould. For Series A, the mould was fitted with traditional cooling cores, and for Series B, the same mould was fitted with conformal ones. The cast specimens were subjected to two weeks of natural ageing. The strength testing of the casts determined the levels of the destructive forces. The destructive forces in the core-cooling impact zones were approximately 28% higher in the B samples than they were in the A samples. The impact of the alloy’s porosity, density, and microstructure on the strengths of the casts was demonstrated. The alloy densities in the central (broken-off) fragments of the casts from Series A were 2.6646 g/cm³; these were 2.6791 g/cm³ in the cases of casts from Series B. The values of the secondary dendrite arm space (SDAS) ranged from 6 to 13 μm in the analysed cross-section of the set of the A casts, and between 3 and 12 μm in the same zone of the set of the B casts. The results of the experimental determinations of the casts porosity levels and SDAS parameters were compared with the results of numerical simulations that were carried out in ProCAST software.

This paper presents the results of testing the mechanical properties of maraging steel 1.2709 that were obtained by the SLM method under uniaxial and triaxial states of stress. The triaxial state of stress was realised by making circumferential notches in the samples with different radii of rounding. The specimens were subjected to two types of heat treatment, which consisted of ageing at 490 °C and 540 °C for 8 h. The results of the tests that were conducted on the samples were considered as references and compared with the results of the strength tests that were conducted directly on the SLM-made core model. Differences were found between the results of these tests. Based on the experimental results, the relationship between the equivalent strain of the specimen in the bottom of notch ε_eq and triaxiality factor η was determined. Function ε_eq = f(η) was proposed as a criterion for the decrease in the plasticity of the material in the area of the pressure mould cooling channel. Using the FEM method, equivalent strain field ε_eq and triaxiality factor η were determined in the conformal channel cooled core model. Based on the proposed criterion of plasticity loss and the results of numerical calculations, it was shown that the values of equivalent strain ε_eq and triaxiality factor η in the core that was aged at 490 °C did not meet this criterion. On the other hand, the values of strain ε_eq and triaxiality factor η did not exceed the safety limit when ageing was carried out at 540 °C. The plasticity loss method presented in this paper assumes that the value of the triaxiality factor in the vicinity of the channel is influenced by the shape, cross-sectional dimensions and trajectory of the channel axis. Using the methodology proposed in this paper, it is possible to determine the value of allowable deformations in the cooling channel zone and to determine whether the heat treatment applied to the SLM steel does not cause an excessive reduction in the plastic properties.

• Theory and practice of environmental protection in the case of foundries in Europe and Asia • Experience resulting from the cooperation with the foundries in a few European countries, China and India • Phenomena and factors affecting the pollution of the natural environment and the implementation of measures aiming at the environmental protection. Every specialist dealing with foundry processes and their impact on environmental pollution must have encountered in their professional careers numerous situations in which the theory of environmental protection confronts the stark reality. The discrepancy between theory and practice can particularly be noticed in foundry engineering in developing countries where the contrasts between different countries and casting plants are extremely striking. The comparison of working conditions in European and Asian foundries provides a vast scope for further observations and analyses. Environmental protection seems not only a concern of manufacturers of castings, but also of their customers whose opinion exerts a significant influence on both the acceptability of working conditions and on the approach to environmental pollution adopted in metal casting industry. The article presents a number of examples of various outlooks on environmental issues in foundries manufacturing a wide range of cast steel and cast iron castings, where different technologies and production processes are applied.