Carbon nanotubes are highly versatile materials; new applications using them are continuously being developed. Special attention is being dedicated to the possible use of multiwall carbon nanotubes in biomaterials contacting with bone. This study describes the response of murine macrophage-like Raw 264.7 cells after two and six days of culture in contact with artificially generated particles from both, ultra-high molecular weight polyethylene polymer and the composite (multiwall carbon nanotubes and ultra-high molecular weight polyethylene). This novel composite has superior wear behavior, having thus the potential to reduce the number of revision knee arthroplasty surgeries required by wear failure of tibial articulating component and diminish particle-induced osteolysis. The results of an in vitro study of viability, and interleukin-6 and tumor necrosis factor-alpha production suggest good cytocompatibility, similar to that of conventional ultra-high molecular weight polyethylene.

Lightweight composite materials are the gold standard in aeronautical and aerospace applications due to their strength and low mass. To carry higher payloads and decrease launching costs, nanosatellites lightweight. Additionally, nanosatellites must also resist high thermal radiation loads while working in orbit. Polymer-based composite materials maintain low mass and added reinforcing ceramic fillers contributes to increasing radiation resistance, thus producing composites that meet both requirements. In this work, the effects of γ-alumina (Al2O3) and zinc oxide (ZnO) micro- and nanoparticles on the thermal properties and degradation kinetics of epoxy-based composites were investigated. The effective thermal conductivity improved up to 17.8 % for epoxy/γ-Al2O3 and 27.4 % for epoxy/ZnO. The effective thermal diffusivity values show a monotonic decreasing behavior as a function of the particle concentration for the epoxy/γ-Al2O3 composites; for the epoxy/ZnO composites, no correlation on the effective thermal diffusivity values with the ZnO-content was observed. Both oxide-based ceramic fillers increase the thermal stability of epoxy up to 250 °C; however, γ-Al2O3 decreased the maxima decomposition temperature of the epoxy matrix by 6°C. Zinc oxide did not affect the maxima decomposition temperature but decreased the activation energy of epoxy by ~ 45 %. These results provide a feasible manufacturing method for epoxy-based composite materials (i.e. nanosatellites) where efficient heat transfer, heat resistance, and low mass are required.