Additive manufacturing (AM) or 3D printing of metals is gaining popularity due to its flexibility when fabricating parts with highly complex designs, as well as when simplifying manufacturing steps and optimizing process times. In this investigation, 17-4 PH stainless steel was additively manufactured using Laser Powder Bed Fusion (L-PBF), followed by functionalization through a DUPLEX treatment. This treatment involved a plasma-assisted nitriding process, followed by the deposition of an arc-PVD c-Al_0.7Cr_0.3N hard coating. The microstructural modifications resulting from plasma nitriding (such as the formation of Fe_2,3N and Fe₄N and the αN or expanded martensite phases) and the surface improvements with the c-Al_0.7Cr_0.3N coating on the 3D-printed 17-4 PH steel are evaluated in comparison to conventionally manufactured 17-4 PH steel. These microstructural characteristics are correlated with the mechanical response of the treated surfaces. As a result of the plasma nitriding process, the hardness of the 3D-printed 17-4 PH SS increased by approximately 260%. The wear, measured through dynamic and static scratch testing, was reduced by approximately 31%. This improvement was attributed to the modification of adhesive failure mechanisms, leading to a reduction in wear volume, improved coating adhesion, and enhanced scratch resistance.