In the field of industrial wastewater treatment, membrane separation technology, as an emerging separation technology, compared with traditional separation technology such as precipitation, adsorption, and ion exchange, has advantages in separation efficiency, low energy consumption, low cost, simple operation, and no secondary pollution. The application has been expanding in recent years, but membrane fouling and other problems have seriously restricted the development of membrane technology. Natural cellulose is one of the most abundant resources in nature. In addition, nanocellulose has characteristics of high strength and specific surface area, surface activity groups, as well as being pollution-free and renewable, giving it a very wide development prospect in many fields, including membrane separation technology. This paper reviews the current status of nanocellulose filtration membrane, combs the widespread types of nanocellulose and its derivatives, and summarizes the current application of cellulose in membrane separation. In addition, for the purpose of nanocellulose filtration membrane in wastewater treatment, nanocellulose membranes are divided into two categories according to the role in filtration membrane: the application of nanocellulose as membrane matrix material and as a modified additive in composite membrane in wastewater treatment. Finally, the advantages and disadvantages of inorganic ceramic filtrations and nanocellulose filtrations are compared, and the application trend of nanocellulose in the filtration membrane direction is summarized and discussed.

Wood drying stress causes various drying defects, which result from the wood microstructure and the transfer of heat and mass during the drying. It is the fundamental way to solve the problem of defects to clarify the law and mechanism of wood stress and strain development during drying. In this paper, based on the defects of wood drying, the theory and experimental testing methods of drying stress and strain were summarized. Meanwhile, artificial neural networks (ANN) and their application in the wood drying field were also investigated. The traditional prong and slicing methods were used practically in the research and industry of wood drying, but the stress changes in-process cannot be trapped. The technologies of image analysis and near-infrared spectroscopy provide a new opportunity for the detection of drying stress and strain. Hence, future interest should be attached to the combination of the theory of heat and mass transfer and their coupling during drying with the theory of microscopic cell wall mechanics and macroscopic drying. A more complete image acquisition and analysis system should be developed to realize the real-time monitoring of drying strain and cracking, practically. A more feasible and reasonable prediction model of wood drying stress and strain should be established to achieve the accuracy of the prediction.

The modification of wood cell walls is based on the characteristics of the chemical composition and structure of the cell wall. Various physical and chemical modifications to these characteristics enhance the original properties of the cell wall and give additional functionality. Through complex modification, wood has also obtained the opportunity to become a multifunctional material. Scholars have paid more attention to the microscopic properties of the cell wall with continuous enrichment of modification methods and improvement of modification mechanisms. This article summarizes the methods of cell wall modification in recent years and proposes prospects for future development: (1) innovation of modifiers and combination with modification mechanism, as well as improvement of cell wall permeability; (2) the application directions of cell wall structures; and (3) the application of nano-technologies in cell wall modification. This review provides further ideas and technologies for wood modifications.

Wood is an environmentally friendly material, but some natural properties limit its wide application. To study the effect of a combination of heat treatment (HT) and wax impregnation (WI) on wood hygroscopicity, dimensional stability, and mechanical properties, samples of Pterocarpus macrocarpus Kurz wood were subjected to HT at a moderate temperature of 120 °C and a high temperature of 180 °C, for a 4 h duration. Subsequently, half of the 120 °C HT samples were treated with WI at 90 °C. The results showed that 180 °C HT and WI decreased the capacity of adsorption and liquid water uptake and swelled the wood significantly, while WI had the biggest reduction. The effect of 120 °C HT was significant only on decreasing the capacity of adsorption and the swelling of liquid water uptake. The bending strength (MOR) of wood decreased only after 180 °C HT, and 120 °C/4h HT and WI had no significant influence on MOR. The bending stiffness (MOE) increased significantly after 180 °C HT and WI, while 120 °C/4h HT had no significant influence on MOE. Therefore, the combination of moderate-temperature HT can act synergistically in the improvement of certain aspects of wood properties such as capacity of water adsorption and liquid water uptake. WI effectively improved wood hygroscopicity, dimensional stability, and mechanical properties.

Wood processing is a crucial step of wood utilization, but the adding of environmentally hazardous feedstocks and the use of unreasonable technology allow it to harm the environment and human health. Supercritical CO₂ (scCO₂) is a non-toxic, odorless, and safe solvent, which is widely used in studies and industrial production, but there is no review summarizing wood processing with scCO₂. The unique structure and chemical properties of wood combined with scCO₂ technology produce positive results. In this paper, wood processing with scCO₂ is summarized, including wood impregnation, wood drying, wood thermochemical conversion, and wood extraction. The green and efficient characteristics of wood processing with scCO₂ are explained in detail for researchers, engineers, and investors to provide a clean wood processing method. Further study is needed to reduce its energy consumption and commercialize it eventually.

Thermal modification (TM) improves the hydrophobicity, dimensional stability, and durability of wood, but TM commonly results in severe color change and mechanical strength loss as wood is treated at higher temperature. In this study, Pterocarpus macrocarpus Kurz wood was thermally modified at moderate temperature (150 °C) and higher temperature (200 °C), and subsequently TM wood at 150 °C was subjected to wax impregnation (WI), the effect of a combination of TM and WI on the hygroscopicity, dimensional stability, and mechanical properties, as well as the micro-structure of wood, were investigated and compared. The results showed that the mass loss of wood was slight at 150 °C TM, while it became severe at 200 °C TM conditions. TM conditions affected the amount of the subsequent wax impregnation; the equilibrium moisture content (EMC), water absorption ratio, and adsorption and absorption swelling of the 150 °C TM + WI group were lower than that of 200 °C TM, and presented the lowest value. Moderate temperature TM could improve the hydrophobicity and dimensional stability of wood, but WI played a key role in the improvement. TM decreased the modulus of rupture (MOR) of wood, while WI improved the MOR. TM increased the modulus of elasticity (MOE) of wood, but WI had little effect on MOE; Scanning electron microscope (SEM) observation showed that the wax was successfully impregnated into the wood interior, and presented an even distribution on the internal surfaces of wood cells; Fourier-transform infrared spectroscopy (FTIR) spectra verified the changes of –OH and C=O after TM and TM + WI, which contributed to decreasing hygroscopicity and improving the dimensional stability of the wood. Impregnated wax improved wood mechanical strength, but decreased the lightness, and deepened the color of wood. The combination of thermal modification at moderate temperature with subsequent wax impregnation is a practical approach for improving wood properties.