The modification of wood cell walls is based on the characteristics of the chemical composition and structure of the cell wall. Various physical and chemical modifications to these characteristics enhance the original properties of the cell wall and give additional functionality. Through complex modification, wood has also obtained the opportunity to become a multifunctional material. Scholars have paid more attention to the microscopic properties of the cell wall with continuous enrichment of modification methods and improvement of modification mechanisms. This article summarizes the methods of cell wall modification in recent years and proposes prospects for future development: (1) innovation of modifiers and combination with modification mechanism, as well as improvement of cell wall permeability; (2) the application directions of cell wall structures; and (3) the application of nano-technologies in cell wall modification. This review provides further ideas and technologies for wood modifications.

Moisture transfer influences wood deformation and moisture content (MC) distribution during conventional drying of Eucalyptus urophylla wood. This study aims to investigate the effect of sample length (30, 100, and 200 mm) on moisture distribution and transfer in different directions and locations and on deformation of wood. The results showed that when the MC was above the fiber saturated point (FSP), the drying rate decreases exponentially with an increase of sample length; however, below the FSP, there was no obvious relationship between the drying rate and sample length and above the FSP, the moisture distribution was non-uniform along tangential, radial, and longitudinal directions and became even below the FSP, which was more significant in the middle location of wood. The greatest MC differences occurred between the surface and sub-central layers along the tangential and radial direction, which were between the end and sub-middle locations along the longitudinal direction. The effect of sample length on the MC distribution and MC differences along wood in the three directions depended on locations and the MC stage of wood; most of the free water and bound water transferred from the wood central to the ends along the longitudinal direction for three sets of samples. Bound water diffusion significantly slowed as the sample length exceeded 200 mm; sample length affects wood collapse and its recovery, but the drying rate has a lesser effect on collapse for samples with a length below 200 mm.

Wood is a green and renewable bio-based building material, but its hygroscopicity affects its dimensional stability, limiting its use in construction. Chemical modification can improve its properties, yet its effectiveness depends on wood permeability and traditional modifiers. This study first used a deep eutectic solvent (DES) to boost the permeability of North American alder wood. Then, methyl trimethoxysilane was impregnated under supercritical carbon dioxide (SCI), pressure (PI), vacuum (VI), and atmospheric pressure (AI) conditions. DES treatment damaged the cell structure, increasing wood permeability. Silane was deposited and polymerized in the cell lumen, chemically bonding with cell-wall components, filling walls and pits, and thickening walls. The VI group had the highest absolute density (0.59 g/cm³, +36.6%) and the lowest moisture absorption (4.4%, −33.3%). The AI group had the highest ASE (25%). The PI group showed the highest surface hardness (RL, 2592 N) and a water contact angle of 131.9°, much higher than natural wood. Overall, the VI group had the best performance. Silane reacts with cellulose, hemicellulose, and lignin in wood via hydrolysis and hydroxyl bonding, forming stable bonds that enhance the treated wood’s hydrophobicity, dimensional stability, and surface hardness.