The USAF requirements for the durability and damage tolerance certification for additively manufactured (AM) aircraft structural parts, which are detailed in Structures Bulletin EZ-19-01, raise a number of new and, as yet, unanswered questions. The present paper attempts to address three questions: How to perform a fracture mechanics-based analysis of crack growth in an AM part so as to account for the residual stresses, how to perform a fracture mechanics-based durability analysis of a cold spray repair so as to account for both the induced residual stresses and the presence of multiple co-located cracks, and how to perform a fracture mechanics-based durability analysis of an AM part so as to account for the presence of multiple collocated surface braking cracks. In this context, the present paper reveals the potential of the Hartman–Schijve variant of the NASGRO crack growth equation to accurately predict the growth of each of the individual (collocated) cracks that arose in a cold spray-repaired specimen and in a specimen from a crack that nucleated and grew from a rough surface.

This paper summarises the findings of an investigation into the durability of cold spray repairs, also known as supersonic particle deposition or SPD repairs, to simulated corrosion damage in AA7075-T7351 aluminium alloy specimens. A feature of this paper is that it is the first to show how to perform the mandatory durability analysis of repaired corroded structures, where the corroded material is first removed by machining and then repaired using cold spray, in a fashion consistent with the requirements delineated in USAF Structures Bulletin EZ-19-01, MIL-STD-1530D, and the US Joint Services Structural Guidelines JSSG2006.

This paper presents an experimental study into the analysis required for the durability assessment of 7075 and 6061 cold spray repairs to military aircraft. To this end, it is first shown that provided the bulk stress in a 7075 cold spray coating can be kept beneath approximately 150 MPa, then the coating should not crack. A range of examples are presented in which the interface between the coating and the substrate only fails subsequent to crack growth in the substrate. We also show that failure of cold spray repaired/coated panels can also be due to the nucleation and growth of cracks in the substructure immediately adjacent to the coated/repaired region. As such, when performing a durability analysis for a cold spray repair, the growth of such small naturally occurring cracks, both at the interface and immediately adjacent to the ends of the coating, need to be accounted for.

Purpose: The purpose of this paper is to describe the results of a combined numerical and experimental study into the ability of supersonic particle deposition (SPD) to restore the load carrying capacity of rib stiffened wing planks with simulated stress corrosion cracking (SCC). Design/methodology/approach: In this context the experimental results reveal that SCC can result in a dramatic reduction in the load carrying capacity of the structure and catastrophic failure via cracking that tears the length of the structure through buckling. A combined numerical and experimental study then reveals how this reduction, in the load carrying capacity can be overcome by using SPD. Findings: This paper is the first to show that SPD can be used to restore the load carrying capacity of rib stiffened structures with SCC. It also shows that SPD repairs can be designed to have only a minimal effect on the local stiffness and hence on the load path. However, care should be taken to ensure that the design is such that premature failure of the SPD does not occur. Originality/value: This is the first paper to show that a thin layer of SPD deposited 7,075 aluminium alloy powder on either side of the SCC-simulated stiffener has the potential to restore the load carrying capability of a rib stiffened structure. As such it represents an important first step into establishing the potential for SPD to restore the buckling strength of rib stiffened wing panels containing SCC.