In this research work, unfilled and mono-filled polytetrafluoroethylene (PTFE) materials were developed and characterised by physical, thermal, viscoelastic, mechanical, and wear analysis. The applied fillers were graphene, alumina (Al₂O₃), boehmite alumina (BA80), and hydrotalcite (MG70) in 0.25/1/4/8 and 16 wt % filler content. All samples were produced by room temperature pressing–free sintering method. All of the fillers were blended with PTFE by intensive dry mechanical stirring; the efficiency of the blending was analysed by Energy-dispersive X-ray spectroscopy (EDS) method. Compared to neat PTFE, graphene in 4/8/16 wt % improved the thermal conductivity by ~29%/~84%/~157%, respectively. All fillers increased the storage, shear and tensile modulus and decreased the ductility. PTFE with 4 wt % Al₂O₃ content reached the lowest wear rate; the reduction was more than two orders of magnitude compared to the neat PTFE.

In this research work, unfilled and monofilled polytetrafluoroethylene (PTFE) were investigated. The applied fillers were graphene, alumina (Al₂O₃), boehmite alumina (BA80) and hydrotalcite (MG70). Graphene and Al₂O₃ are already known in the literature as potential fillers of PTFE, while BA80 and MG70 are novel fillers in PTFE. Materials were produced by room temperature pressing—free sintering method with a maximum sintering temperature of 370 °C. The mass loss and decomposition analyses were carried out by thermogravimetric analysis (TGA) in two different ways. The first was a sensitivity analysis to gain a better view into the sintering process at 370 °C maximal temperature. The second was a heating from 50 °C up to 1000 °C for a full-scale decomposition analysis. BA80 is a suitable filler for PTFE, as most of its functional groups still existed after the sintering process. Both PTFE and Al₂O₃ had high thermal stability. However, when Al₂O₃ was incorporated in PTFE, a remarkable mass loss was observed during the sintering process, which indicated that the decomposition of PTFE was catalysed by the Al₂O₃ filler. The observed mass loss of the Al₂O₃-filled PTFE was increased, as the Al₂O₃ content or the applied dwelling time at a 370 °C sintering temperature increased.

The research focuses on slurry abrasion and erosion of martensitic steels used in the mining and agricultural industries. A traditionally constructed slurry pot tester with corundum abrasives in slurry form was used for wear characterisation. Wear testing was performed on each specimen for 180 h. Every 20 h, pauses were taken to characterise the specimen size, weight, hardness, and surface roughness. The worn zone’s damage progression was studied using optical microscopy. As the test period rose, the mass loss due to the wear, which was governed by the impact angle of the slurry flow, followed a linear pattern. The impact of specimen orientation on the wear rate was more pronounced than that of abrasive flow velocity. High-speed video recordings highlighted the varied contact conditions that caused the wear mechanism to shift from abrasion to slurry erosion. Slurry abrasion was seen at the bottom of the specimen as a result of pure sliding conditions, while pitting was observed at the top of the specimen as a result of fatigue from particle impact. Studies of 3D surfaces demonstrated a decrease in wear rate while transitioning from the abraded zone, which witnessed polishing and minor hardness, to the pitting zone. The wear performance of the materials was rated, with tempered martensitic steel coming out on top.