Wheat straw is an easily affordable, cost-effective and natural source of antioxidants and cellulose, but its full potential is not yet utilized. In the present investigation, an auto-hydrolytic process was applied to recover both antioxidant phenolic compounds and cellulose from wheat straw. Two three-step acid/alkaline fractionation processes were applied differing for the first step: a conventional mild acid hydrolysis or an auto-hydrolysis. The liquors from the first step were analyzed for the recovery of antioxidants, while the final residues from the whole process were analyzed for cellulose yield and purity. The auto-hydrolysis process led to a higher yield in antioxidants but also in sugars (glucose and xylose) and sugar degradation products (5-HMF, 5-MF, furfural) than the acid hydrolysis process. The overall cellulose recovery (about 45% g/100 g_{cellulose wheat straw dm}) and purity was comparable in the two processes; therefore, the auto-hydrolysis-based process could be recommended as a potentially more environmentally friendly process to recover antioxidants and cellulose from wheat straw for different applications. Finally, a first study on the optimization of hydrolysis step was provided from the point of view of improving the cellulose yield, monitoring the sugars release during both the acid hydrolysis and the auto-hydrolysis process.

The thermal stability of four different commercial citrus peel extracts was tested and improved by an encapsulation process with β-cyclodextrins in a spray-dryer. All extracts after the encapsulation process maintained a good antioxidant capacity, with an apparent loss in total phenolic compounds of around 20–25%. In addition, all samples showed good antimicrobial activity (MIC 5–0.625 mg/mL) against Staphylococcus aureus, which was maintained after the encapsulation process (MIC 5–1.25 mg/mL). Based on the antioxidant and antimicrobial activity results, the best-encapsulated citrus extract was selected for incorporation into a polylactic acid/polyhydroxy butyrate (PLA/PHB) film. The latter was then produced on an industrial scale by cast extrusion and was found to be suitable for food contact as it showed overall migration values in different food simulants lower than the legislative limit of 10 mg of non-volatile substances per 1 dm² of surface area. The UHPLC-HRMS analysis, performed to evaluate the migration of the active compounds, revealed about 13.41% release in food simulant A and 11.02% in food simulant B. Antimicrobial analysis conducted directly on the film showed a growth inhibition activity towards Escherichia coli and Staphylococcus aureus equal to 30 and 60%, respectively.