Polyoxometalates (POMs) are polyatomic ions with closed three-dimensional frameworks. Their unique structure contains a large number of redox active sites, making them promising electrocatalysts for electrochemical energy conversion and storage applications. Thus, this paper presents an overview of the use of POMs as electrocatalysts for electrochemical energy conversion and storage devices, such as batteries, supercapacitors, fuel cells, or water electrolyzers. A discussion of the viability of these materials as alternatives to noble metal-based electrocatalysts is made. The current status of these materials to respond to the challenges of converting modern energy systems into more sustainable ones is also envisaged.

Bimetallic cobalt (Co)-based coatings were prepared by a facile, fast, and low-cost electroless deposition on a copper substrate (CoFe, CoMn, CoMo) and characterized by scanning electron microscopy with energy dispersive X-ray spectroscopy and X-ray diffraction analysis. Prepared coatings were thoroughly examined for hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) in alkaline solution (1 M potassium hydroxide, KOH) and their activity compared to that of Co and Ni coatings. All five coatings showed activity for both reactions, where CoMo and Co showed the highest activity for HER and OER, respectively. Namely, the highest HER current density was recorded at CoMo coating with low overpotential (61 mV) to reach a current density of 10 mA·cm⁻². The highest OER current density was recorded at Co coating with a low Tafel slope of 60 mV·dec⁻¹. Furthermore, these coatings proved to be stable under HER and OER polarization conditions.

The new 3D coordination polymer (CP) [Mn(L)(HCOO)]_n (Mn-CP) [L = 4-(pyridin-4-ylcarbamoyl)benzoate] was synthesised via a hydrothermal reaction using the pyridyl amide functionalized benzoic acid HL. It was characterized by elemental, FT-IR spectroscopy, single-crystal and powder X-ray diffraction (PXRD) analyses. Its structural features were disclosed by single-crystal X-ray diffraction analysis, which revealed a 3D structure with the monoclinic space group P21/c. Its performance as an electrocatalyst for oxygen reduction (ORR), oxygen evolution (OER), and hydrogen evolution (HER) reactions was tested in both acidic (0.5 M H₂SO₄) and alkaline (0.1 M KOH) media. A distinct reduction peak was observed at 0.53 V vs. RHE in 0.1 M KOH, which corresponds to the oxygen reduction, thus clearly demonstrating the material’s activity for the ORR. Tafel analysis revealed a Tafel slope of 101 mV dec⁻¹ with mixed kinetics of 2e⁻ and 4e⁻ pathways indicated by the Koutecky–Levich analysis. Conversely, the ORR peak was not present in 0.5 M H₂SO₄ indicating no activity of Mn-CP for this reaction in acidic media. In addition, Mn-CP demonstrated a noteworthy activity toward OER and HER in acidic media, in contrast to what was observed in 0.1 M KOH.

Molybdenum carbide (Mo₂C)-based electrocatalysts were prepared using two different carbon supports, commercial carbon nanotubes (CNTs) and synthesised carbon xerogel (CXG), to be studied from the point of view of both capacitive and electrocatalytic properties. Cation type (K⁺ or Na⁺) in the alkaline electrolyte solution did not affect the rate of formation of the electrical double layer at a low scan rate of 10 mV s⁻¹. Conversely, the different mobility of these cations through the electrolyte was found to be crucial for the rate of double-layer formation at higher scan rates. Molybdenum carbide supported on carbon xerogel (Mo₂C/CXG) showed ca. 3 times higher double-layer capacity amounting to 75 mF cm⁻² compared to molybdenum carbide supported on carbon nanotubes (Mo₂C/CNT) with a value of 23 mF cm⁻² due to having more than double the surface area size. The electrocatalytic properties of carbon-supported molybdenum carbides for the oxygen reduction reaction in alkaline media were evaluated using linear scan voltammetry with a rotating disk electrode. The studied materials demonstrated good electrocatalytic performance with Mo₂C/CXG delivering higher current densities at more positive onset and half-wave potential. The number of electrons exchanged during oxygen reduction reaction (ORR) was calculated to be 3, suggesting a combination of four- and two-electron mechanism.