Bimetallic cobalt (Co)-based coatings were prepared by a facile, fast, and low-cost electroless deposition on a copper substrate (CoFe, CoMn, CoMo) and characterized by scanning electron microscopy with energy dispersive X-ray spectroscopy and X-ray diffraction analysis. Prepared coatings were thoroughly examined for hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) in alkaline solution (1 M potassium hydroxide, KOH) and their activity compared to that of Co and Ni coatings. All five coatings showed activity for both reactions, where CoMo and Co showed the highest activity for HER and OER, respectively. Namely, the highest HER current density was recorded at CoMo coating with low overpotential (61 mV) to reach a current density of 10 mA·cm⁻². The highest OER current density was recorded at Co coating with a low Tafel slope of 60 mV·dec⁻¹. Furthermore, these coatings proved to be stable under HER and OER polarization conditions.

The production of high-purity hydrogen from hydrogen storage materials with further direct use of generated hydrogen in fuel cells is still a relevant research field. For this purpose, nickel-molybdenum-plated copper catalysts (NiMo/Cu), comprising between 1 and 20 wt.% molybdenum, as catalytic materials for hydrogen generation, were prepared using a low-cost, straightforward electroless metal deposition method by using citrate plating baths containing Ni²⁺–Mo⁶⁺ ions as a metal source and morpholine borane as a reducing agent. The catalytic activity of the prepared NiMo/Cu catalysts toward alkaline sodium borohydride (NaBH₄) hydrolysis increased with the increase in the content of molybdenum present in the catalysts. The hydrogen generation rate of 6.48 L min⁻¹ g_cat⁻¹ was achieved by employing NiMo/Cu comprising 20 wt.% at a temperature of 343 K and a calculated activation energy of 60.49 kJ mol⁻¹ with remarkable stability, retaining 94% of its initial catalytic activity for NaBH₄ hydrolysis following the completion of the fifth cycle. The synergetic effect between nickel and molybdenum, in addition to the formation of solid-state solutions between metals, promoted the hydrogen generation reaction.

Hydrogen production via water splitting is one of the latest low-cost green hydrogen production technologies. The challenge is to develop inexpensive and highly active catalysts. Herein, we present the preparation of electrocatalysts based on cobalt–phosphorus (Co-P) coatings with different P contents for hydrogen and oxygen evolution reactions (HER and OER). The Co-P coatings were deposited on the copper (Cu) surface using the economical and simple method of electroless metal deposition. The morphology, structure, and composition of the Co-P coatings deposited on the Cu surface were studied via scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX), while their activity for HER and OER in 1 M KOH was investigated using linear sweep voltammetry (LSV) and chrono-techniques. It was found that the catalyst activity for both HER and OER depends on the P content of the catalyst and varies based on the highest efficiency for each reaction. The Co-P coating with 11 wt% P exhibited the lowest overpotential value of 98.9 mV for the HER to obtain a current density of 10 mA cm⁻² compared to the Co-P coatings with 8, 5, 1.6, and 0.4 wt% P (107.6, 165.9, 218.2, and 253.9 mV, respectively). In contrast, the lowest OER overpotential (378 mV) was observed for the Co-P coating with 8 wt% P to obtain a current density of 10 mA cm⁻² as compared to the Co-P coatings with 5, 11, 1.6, and 0.4 wt% P (400, 413, 434, and 434 mV, respectively). These results suggest that the obtained catalysts are suitable for HER and OER in alkaline media.

Six cobalt gold (CoAu) electrodes were prepared by electroless deposition using different gold-containing solutions (acidic and weakly acidic) and different Au deposition times. Characterization of CoAu electrodes was done by scanning electron microscopy with energy-dispersive X-ray spectroscopy, N₂-sorption, and X-ray powder diffraction techniques. The possibility of using the prepared electrodes in environmental applications, i.e., for the electrochemical sensing of a trace amount of arsenic(III) in weakly alkaline media was assessed. Employing the CoAu electrode (prepared by immersing Co/Cu into 1 mM HAuCl₄ (pH 1.8) at 30 °C for 30 s) under optimized conditions (deposition potential −0.7 V and deposition time of 60 s), a low limit of detection of 2.16 ppb was obtained. Finally, this CoAu electrode showed activity for arsenic oxidation in the presence of Cu(II) as a model interferent as well as in real samples. Furthermore, the use of CoAu electrode as an anode in fuel cells, namely, direct borohydride – hydrogen peroxide fuel cells was also assessed. A peak power density of 191 mW cm⁻² was attained at 25 °C for DBHPFC with CoAu anode at a current density of 201 mA cm⁻² and cell voltage of 0.95 V, respectively. The peak power density further increased with the increase of the operating temperature to 55 °C.

Nickel boron (NiB) coatings were deposited onto copper using a nickelglycine (Ni-Gly) plating solution and morpholine borane (MB) as a reducing agent. It has been determined that using MB as a reducing agent in the Ni-Gly plating solution produces NiB coatings, which exhibit typical cauliflower-like textures. The deposition rate of the NiB coatings and their composition depend on the concentrations of the reducing agent (MB) and the ligand (Gly), in addition to the pH and temperature of the plating solution. The highest deposition rate (3.42 mg cm–2 h–1) of the NiB coating was obtained when the plating bath was operated at pH 5 and 60°C temperature. Using this method, NiB coatings containing 10–20 at.% of boron can be obtained.