Wires of magnesium alloys possess a high potential, e.g., as filler materials, for joining applications but also for biodegradable applications, such as suture materials. While the typical process of producing wires is based on a wire drawing process, direct extrusion by using adjusted dies to deal with high degrees of deformation allows a one-step manufacturing of wires to some extent. In this work, the extrusion of wires with a thickness of 1 mm and even lower is shown feasible for pure magnesium and three Al-containing magnesium alloys (AZ31, AZ80, AZ91). The surface quality and the mechanical properties are improved with increasing Al content. It is shown that, despite the large difference in the degrees of deformation, the properties and their development are similar to those of extruded round bars. Wrapping tests were carried out as an exemplary more complex forming procedure, and the behavior is correlated to the microstructure and texture of the extruded wires.

The application of magnesium flat products is affected by the limited formability at room temperature and the anisotropy of the mechanical properties. The main reason for this is the underlying hexagonal crystal structure of magnesium and the development of strong crystallographic textures during massive forming processes with distinct alignment of basal planes. For an improvement in the properties of semi-finished products, the detailed knowledge of the influence of the manufacturing process on the microstructure and texture evolution of the flat products as a result of dynamic and static recrystallization is required. In this work, flat products made of conventional magnesium alloy AZ31 were manufactured by the rolling process as well as by direct extrusion, with variation in the process temperature. This allowed the development of a distinct variation in microstructures and textures of the flat products. The effects on mechanical properties and formability are highlighted and discussed in relation to the microstructure and texture. It is shown that both the process and the temperature have a major influence on texture and consequently on the material properties.