Organic-inorganic hybrid perovskite (OIHP) photodetectors that simultaneously achieve an ultrafast response and high sensitivity in the near-infrared (NIR) region are prerequisites for expanding current monitoring, imaging, and optical communication capbilities. Herein, we demonstrate photodetectors constructed by OIHP and an organic bulk heterojunction (BHJ) consisting of a low-bandgap nonfullerene and polymer, which achieve broadband response spectra up to 1 μm with a highest external quantum efficiency of approximately 54% at 850 nm, an ultrafast response speed of 5.6 ns and a linear dynamic range (LDR) of 191 dB. High sensitivity, ultrafast speed and a large LDR are preeminent prerequisites for the practical application of photodetectors. Encouragingly, due to the high-dynamic-range imaging capacity, high-quality visible-NIR actual imaging is achieved by employing the OIHP photodetectors. We believe that state-of-the-art OIHP photodetectors can accelerate the translation of solution-processed photodetector applications from the laboratory to the imaging market.

Although three-dimensional metal halide perovskite (ABX₃) single crystals are promising next-generation materials for radiation detection, state-of-the-art perovskite X-ray detectors include methylammonium as A-site cations, limiting the operational stability. Previous efforts to improve the stability using formamidinium–caesium-alloyed A-site cations usually sacrifice the detection performance because of high trap densities. Here we successfully solve this trade-off between stability and detection performance by synergistic composition engineering, where we include A-site alloys to decrease the trap density and B-site dopants to release the microstrain induced by A-site alloying. As such, we develop high-performance perovskite X-ray detectors with excellent stability. Our X-ray detectors exhibit high sensitivity of (2.6 ± 0.1) × 10⁴ μC Gy_air⁻¹ cm⁻² under 1 V cm⁻¹ and ultralow limit of detection of 7.09 nGy_air s⁻¹. In addition, they feature long-term operational stability over half a year and impressive thermal stability up to 125 °C. We further demonstrate the promise of our perovskite X-ray detectors for low-bias portable applications with high-quality X-ray imaging and monitoring prototypes.

Addition of the Ti₃C₂ into SnO₂ enhanced the power conversion efficiency due to the good conductivity of Ti₃C₂ nanosheets.